不同抛光方法对钴铬合金铸造义齿表面粗糙度及精度的影响

目的研究不同抛光方法对钴铬合金铸造义齿表面粗糙度及精度的影响。方法(1)制作30个30mm×10mm×1.5mm钴铬合金试件,选择1组作为对照组,其余各组分别用5种方法抛光光整技术、电解、打磨、打磨后再电解、打磨后再光整,测量其表面粗糙度;(2)铸造钴铬合金基托30个,选择1组作为对照组,其余各组用5种方法抛光,在相当于上颌第二磨牙远中部位切断义齿基托与标准模型,测量基托组织面与标准模型间5个部位的间隙。用SPSS13.0软件对数据进行方差分析。结果(1)抛光前,试件表面粗糙度值最大(Ra3.38μm),手工打磨后再光整组粗糙度值最小(Ra0.19μm)。除光整组、电解组试件之间的差别无统计学意义外(P>0.05),其余各组差别均有极显著统计学意义(P<0.01)。(2)各组试件的精度值在抛光前、后无统计学差异(P>0.05)。结论手工打磨后再进行光整的铸件表面粗糙度最低,光整抛光方法对上颌铸造基托的精度无影响。     

不同抛光方法对钴铬合金铸件表面质量及物理性能的影响

目的研究不同抛光方法对钴铬合金铸件表面质量及物理性能的影响。方法采用5种抛光方法抛光钴铬合金板试样,测量其表面粗糙度、硬度、弯曲强度、断裂强度和弹性模量,并对数据进行统计学分析。结果打磨后光整组试样表面粗糙度值最小(P<0.01);打磨后光整组试样的硬度较未抛光组要高(P<0.05);不同抛光方法抛光试样的弯曲强度,断裂强度与弹性模量无统计学差异。结论手工打磨后再进行光整的铸件表面粗糙度值最低,表面硬度增高;抛光方法对铸件物理性能无影响。     

5种抛光方法对钴铬烤瓷合金抗腐蚀性能的影响

目的 研究5种抛光方法对钴铬烤瓷合金抗腐蚀性能的影响.方法 制作30个钴铬烤瓷合金试样,随机分为5组,分别采用砂纸、金相布轮、橡皮轮、电解和化学方法进行抛光,测量试样的表面粗糙度.用浸泡实验检测试件在腐蚀液中浸泡后Co、Cr离子的析出量,并用扫描电镜观察试样浸泡前后的表面形貌.结果 电解抛光会破坏钴铬烤瓷合金试样,终止后续浸泡实验;化学抛光组表面粗糙度最大,为(0.35 ±0.09) μm,与其他组差异有统计学意义(P＜0.05).腐蚀液浸泡7d后,金相布轮抛光组试件Cr析出量最小,为(0.47 ±0.17) μg/cm2;化学抛光组试件Cr析出量最最多,为(2.34 ±0.76) μg/cm2,差异有统计学意义(P＜0.05).扫描电镜观察腐蚀液浸泡前的试件,金相布轮抛光和橡皮轮抛光可获得光滑表面,砂纸抛光和化学抛光后表面划痕明显;腐蚀液浸泡后各组表面划痕没有显著变化.结论 钴铬烤瓷合金采用金相布轮和橡皮轮抛光可获得较好的表面形貌和抗腐蚀性能,化学抛光对钴铬烤瓷合金表面形貌改善不大,其抗腐蚀性能最差.     

不同抛光方法对牙科钴铬合金离子析出影响研究

目的 比较不同抛光方法对钴铬合金离子析出的影响。方法 本研究于2013年3—8月在福建医科大学附属口腔医院进行。制作30个钴铬合金试样,随机分为5组,分别为砂纸抛光组、镜面抛光组、橡皮轮抛光组、电解抛光组和化学抛光组,每组6个试样。根据ISO 10271：2011标准采用浸泡实验检测试样Co、Cr离子的析出情况。检测腐蚀前的表面粗糙度和腐蚀前后表面形貌。结果 镜面抛光组Co、Cr析出量之和小于橡皮轮抛光组、电解抛光组和化学抛光组（P < 0.05）。化学抛光组表面粗糙度最大（P < 0.05）。化学抛光组Co、Cr析出量及其总和均大于砂纸抛光组、镜面抛光组、橡皮轮抛光组、电解抛光组（P < 0.05）。扫描电镜观察表明,砂纸抛光组、橡皮轮抛光组、化学抛光组表面有明显的腐蚀痕迹。结论 钴铬合金经镜面抛光可获得最好的表面形貌和抗腐蚀性能,化学抛光对钴铬合金表面形貌改善不大,其抗腐蚀性能最差。     

钴铬合金表面粗糙度与细菌黏附

目的：了解临床用软质钴铬合金表面粗糙度与细菌黏附的关系。方法：用Talysurf/S5-CD型表面形貌仪测定六组软质钴铬合金试片表面粗糙度。采用体外黏附试验，了解变形链球菌在软质钴铬合金表面的黏附量受表面粗糙度影响的状况。结果：随着研磨和抛光程序的进行，钴铬合金表面粗糙度逐渐减低，其表面的细菌黏附量也不断减少。其中橡皮轮组和抛光膏组之间的表面粗糙度均值和细菌黏附量无显性差异，其余各组间表面粗糙度均值和细菌黏附量均有显性差异。结论：为减少菌斑附着，制作钴铬合金冠修复体后要重视磨光。     

3种义齿清洁剂对钴铬合金及纯钛耐腐蚀性的影响

目的:比较3种常用义齿清洁剂对铸造钴铬合金及纯钛耐腐蚀性的影响.方法:采用Tafel曲线电化学腐蚀测量法测出钴铬合金(CoCr)和纯钛(CP Ti)试件在不同义齿清洁剂中的自腐蚀电位(Ecorr),自腐蚀电流密度(Icorr),绘制出相应的极化曲线,应用扫描电子显微镜观察试件实验前后表面形貌的改变,并对实验结果进行双因素方差分析.结果:在不同义齿清洁剂中钴铬合金Ecorr大于纯钛,Icorr小于纯钛,差异有统计学意义(P＜0.05);钴铬合金在Protefix中的耐腐蚀性Ecorr最大,Icorr 最小,表面腐蚀坑较少;纯钛组在保丽净中Ecorr最大,Icorr较小,表面腐蚀坑较少.结论:在不同义齿清洁剂中钴铬合金耐腐蚀性优于纯钛;不同义齿清洁剂对钴铬合金和纯钛耐腐蚀性的影响有差异.     

铸造前纯钛和钴铬合金的耐腐蚀性研究

目的:探讨纯钛和新配方钴铬合金在体外的电化学腐蚀性.方法:应用Tafel曲线电化学腐蚀测量法,将纯钛合金和新配方钴铬合金浸泡在人工唾液和自来水中,温度室温,pH值为6.8,测量试件的腐蚀电位、腐蚀电流密度和极化电阻.应用扫描电镜(SEM)观察试件表面形态变化.结果:纯钛和钴铬合金在人工唾液和自来水中的腐蚀性均有显著差异(P<0.05),并且同种金属在人工唾液和自来水中的腐蚀性也存在显著差异(P<0.05).扫描电镜观察表明,纯钛金属表面的腐蚀痕迹比钴铬合金表面的腐蚀痕迹明显.结论:新配方钴铬合金比纯钛有较好的耐腐蚀性,而人工唾液比自来水对这两种金属的腐蚀性的影响更大.     

不同粒度石英对钴铬合金铸件表面粗糙度的影响

目的评价包埋料石英粒度对钴铬合金铸件表面粗糙度的影响。方法分别用石英的临界粒度为1-0.5mm、0.5-0.2mm、0.2-0.088mm、<0.088mm的包埋料与硅溶胶调拌包埋,检测气孔率、体积密度、耐压强度;并包埋铸造24个2.5cm×2.5cm×0.5cm的钴铬合金铸件(其中每种包埋料包埋铸造6个铸件),用粗糙度测量仪检测铸造出的钴铬合金铸件的表面粗糙度。结果随着包埋料中石英粒度逐渐变细,显气孔率逐渐增大,体积密度逐渐减小,4号试样显气孔率最大,体积密度最小;随着包埋料中石英粒度的减小,钴铬合金铸件表面粗糙度逐渐减小,4号铸件表面粗糙度降低更多。结论通过减小磷酸盐包埋料的石英粒度可提高钴铬合金铸件表面光洁度。     

人工唾液和氟化物对钴铬合金卡环疲劳强度及粗糙度影响的研究

目的:探讨人工唾液和氟化物对钴铬合金卡环疲劳强度及粗糙度的影响.方法:用成品卡环蜡型制作钴铬合金卡环60个,分为6组,分别在空气中、人工唾液和氟化物中进行测试,初始载荷强度和疲劳失效前的载荷循环次数被自动记录;疲劳裂纹和表面形貌进行扫描电镜分析.用精密粗糙度测量仪检测各组表面粗糙度.结果:钴铬合金卡环在不同测试条件下的...     

铸造纯钛抛光方法的研究

目的 探讨不同抛光方法对纯钛铸件表面的抛光效果。方法 常规制作铸造纯钛试件35个,随机分为7组,除1个对照组外,其余6组分别用不同方法进行抛光处理。观察试件表面形貌,并测定表面粗糙度（Ra值）,计算抛光前后的减重率（Wt%）及单位面积损失的厚度（H）,比较各种抛光方法的抛光效果。结果 用氧化铝和氧化铬抛光膏抛光纯钛铸件可取得良好效果;铸件酸洗后进行电解抛光,表面粗糙度有一定改善。结论 氧化铝和氧化铬抛光膏可用于铸钛表面的机械抛光,电解抛光有一定效果,但电解工艺仍需改进。     

不同磨光方法对弹性义齿基托表面粗糙度影响的实验研究

目的:研究不同磨光处理对弹性义齿基托表面粗糙度的影响,为临床选择合适的磨光方法提供参考。方法:常规制作弹性基托试件90个,随机分为3组,分别采用硅橡胶磨头(1#-3#),金刚砂磨头(001#、002#),砂纸卷(500目、1000目、1500目)粗磨,采用布轮沾水,布轮沾抛光蜡,布轮沾抛光蜡和亮托抛光浆细磨抛光,利用表面粗糙度检查仪测定其粗糙度,扫描电镜观察磨光后的表面形貌,然后对检测结果进行统计学分析。结果:表面粗糙度检查仪检测:不同粗磨方法样本组的表面粗糙度(Ra值)的平均值比较:砂纸组<硅橡胶磨头组<金刚砂组,统计学上存在显著性差异(P<0.001);各组抛光方法表面粗糙度(Ra值)的平均值比较:布轮沾抛光膏和亮托抛光浆组<布轮沾抛光膏组<布轮沾水组,统计学上存在显著性差异(P<0.001)。扫描电镜观察:经金刚砂粗磨,试件表面粗糙,划痕较多,较深;经硅橡胶磨头粗磨,试件表面较光滑,划痕较浅;经1500目砂纸粗磨,试件表面最光滑,划痕最浅。经布轮沾水抛光,试件表面粗糙,划痕较多,较深;经布轮沾抛光蜡抛光,试件表面较光滑,划痕较浅;经布轮沾抛光蜡和亮托抛光浆抛光,试件表面最平滑。结论:经砂纸;硅橡胶磨头;金刚砂处理弹性义齿试件,获得不同的表面粗糙度,经1500目砂纸和硅橡胶磨头处理的试件表面平滑。经布轮沾抛光蜡,布轮沾亮托抛光浆抛光弹性义齿试件表面,表面粗糙度得到显著降低,试件表面平滑。弹性义齿试件不同的粗磨和抛光方法之间存在交互作用,经1500目砂纸粗磨和布轮沾抛光蜡和亮托抛光浆处理后,可以获得较低的粗糙度值,试件表面最平滑。     

Effect of Different Finishing and Polishing Agents on the Surface Roughness of Cast Pure Titanium

PURPOSE: The aim of this study was to evaluate the effect of finishing and polishing agents on surface roughness of cast commercially pure titanium using scanning electron microscope (SEM) analysis. MATERIALS AND METHODS: A standardized square steel die measuring 10 x 10 mm with a thickness of 2 mm was machine cut. An impression of this die was used to create wax patterns for casting. Sixty specimens were cast in commercially pure titanium. These were divided into three groups (A, B, and C) of 20 specimens each. Group A specimens were polished with black, brown, and green rubber discs followed by green polishing compound with buff. Group B specimens were polished with black, brown, and green rubber cones, buffed with yellow polishing cake designed for gold alloy. Group C specimens were polished with silicium carbide cones and buffed with orange polishing cake. Surface roughness of the test specimens was measured in microns with a perthometer. Data were analyzed with ANOVA and Tukey's honest significant difference (HSD) multiple comparison tests among the different groups. Qualitative analysis was done by SEM photomicrographs. RESULTS: Surface roughness values R(a) for Groups A, B, and C were 0.68 microm, 0.78 microm, and 0.27 microm, respectively. SEM photomicrographs and the statistical analysis revealed that the finishing and polishing were better with Group C test specimens with lower surface roughness values compared with groups A and B. Tests showed that Group C was statistically smoother (p< or = 0.01). CONCLUSION: Within the limitations of this study, surface roughness was less on cast CpTi specimens that were finished and polished from the cutters designed specifically for titanium.     

氟化物控释装置对钛合金表面粗糙度影响的初步研究

目的:研究氟化物控释装置防龋对钛合金表面粗糙度的影响。方法:成品钛基台样本24个,随机均分4组。A、B、C组分别在加入2粒氟化物控释装置的20mL人工唾液中浸泡5、10、25d,D组在20mL人工唾液中浸泡25d作为空白对照。用干涉显微镜测量各组样本的表面粗糙度。结果:A、B、C组样本的表面粗糙度分别为(0.302±0.025)μm、(0.311±0.035)μm、(0.330±0.039)μm,D组的表面粗糙度为(0.292±0.030)μm。经统计学分析,空白对照组样本与其他各组样本表面粗糙度无显著性差异(P>0.05),A、B、C组样本两两之间亦无显著性差异(P>0.05)。结论:应用氟化物控释装置对钛合金表面无显著影响,表面粗糙度不随时间变化而变化。     

纯钛表面酸碱处理及生物矿化的初步研究

目的:探讨不同的酸、碱处理条件下纯钛表面生物矿化沉积磷灰石层的差异。方法:对商用纯钛分别采用磨光处理、酸处理、酸碱处理或酸碱及热处理,然后放入模拟体液(SBF)中矿化处理7天;采用SEM观察试样表面的形貌,采用XRD分析试样表面沉积层的相组成。结果:经酸碱处理后纯钛形成微粗糙表面,随着碱液浓度的升高和采用热处理,试样表面的粗糙度增加且更均匀;经碱液处理的试样矿化后其表面出现磷灰石沉积层;而未处理组未发现磷灰石沉积层;XRD图谱分析发现矿化表面沉积物为HCA,钙磷比为1.37。结论:碱液处理有利于磷灰石层的形成,而改变碱液浓度和是否采用热处理对磷灰石沉积能力有影响。     

不同邻面抛光方法对牙釉质表面粗糙度及表面形貌的影响

目的：评价4种邻面抛光方法对邻面釉质表面粗糙度及显微形貌的影响,为邻面抛光方法的选择提供依据。方法：选择21颗离体牙前磨牙,沿颊舌面中线纵剖后获得邻面釉质试件42枚,再用自凝塑料包埋,暴露邻面釉质,用浮石粉抛光,并超声清洗。将42个试样均分为6组,分别作如下处理：A组空白对照,不做处理;B组：阴性对照,采用标准金刚砂车针切磨触点及其周围釉质,切磨后不抛光;其余4组为实验组,经标准金刚砂车针切磨后分别采用以下方法抛光：C组：极细粒度金刚砂车针抛光;D组：裂钻抛光;E组：矽粒子抛光;F组：彩虹抛光条抛光。之后用粗糙度仪测定釉面粗糙度,并进行扫描电镜观察。结果：标准金刚砂车针切磨后粗糙度大幅度增加（P〈0.05）,釉质表面发生明显条形凹陷性缺损;经4种方法抛光后,釉质表面粗糙度均有显著下降（P〈0.05）,显微形貌均较阴性组光滑,其中矽粒子抛光组可达到较空白对照组更为光滑的表面。结论：实验涉及的4种不同邻面抛光方法均有助于降低釉质切磨区域的表面粗糙度,但抛光效果存在差异;采用矽粒子抛光可完全抵消牙体预备时旋转器械对邻牙邻面的切磨作用,获得最为光滑的釉质表面。     

纳米渗氮类金刚石碳膜的耐磨性研究

目的:研究纯钛铸件镀制纳米渗氮类金刚石碳膜(N-DLC)在体外球磨实验及刷洗实验中粗糙度、表面形貌变化,为临床应用类金刚石碳膜提供理论依据.方法:铸造纯钛试件30片,分别镀制N-DLC、TiN薄膜以及空白对照后进行球磨实验和牙刷刷洗实验,通过测量摩擦系数及磨痕深度等综合评价其耐磨性,并在扫描电镜下观察表面形貌.结果:3组试件中,N-DLC镀膜的粗糙度增加值、反射率下降值最小(P＜0.01),空白对照组的变化最大(P＜0.01),TiN的变化值略小于N-DLC镀膜(P＜0.05).扫描电镜观察空白对照表面刷痕明显,TiN和N-DLC镀膜表面未见明显刷痕,仅见有加工处理残留的细小痕迹.结论:与其他表面改性方法相比,N-DLC镀膜的表面形态受磨耗试验影响最小.     

微弧氧化技术用于纯钛表面改性的研究

目的 研究微弧氧化技术(microarc oxidation,MAO)用于纯钛种植体表面改性的可行性.方法 20枚TA2纯钛片,其中15枚用MAO进行表面处理作为实验组,另5枚不做表面处理作为对照组.测试纯钛表面微弧氧化膜的理化性能.扫描电镜观察L929细胞在两组纯钛片表面培养24 h后的生长情况.结果 纯钛表面微弧氧化膜的平均厚度为32.7 μm,表面存在大量直径3～20 μm的蜂窝状孔隙,纯钛微弧氧化膜中富含钙、磷成分,并且出现羟基磷灰石结晶.平均膜基结合强度为8.29 Mpa. L929细胞在经MAO处理的纯钛表面的生长情况优于未经MAO处理的纯钛.结论 MAO可改善纯钛的表面性能,提高生物相容性.     

纯钛铸件化学抛光的实验研究

目的:探讨纯钛铸件的化学抛光效果。方法:3组板状铸件(15mm×15 mm×1.4 mm)分别给予以下3种处理:A组铸件喷砂后不做其它处理;B组铸件喷砂后常规手工研磨;C组铸件喷砂后化学抛光。测试B、C两组铸件的减重率(-wt％),各处理组铸件的表面粗糙度(Ra值)和表面氧化膜厚度。结果:肉眼观察经化学抛光的纯钛铸件表面呈镜面状。化学抛光组的减重率高于手工研磨组,Ra值小于手工研磨组(P<0.05)。其表面存在约8μm厚的氧化膜,且均匀一致。结论:纯钛铸件化学抛光效果良好,具有临床推广价值。     

不同钛表面对血管内皮细胞早期粘附与增殖活性的影响

目的:观察血管内皮细胞在两种纯钛表面(光滑表面和粗糙表面)上的粘附情况.方法:医用纯钛片预备成光滑表面和粗糙表面两组,将猪血管内皮细胞接种于两组钛片表面,分别培养24、48和72 h后,通过吖啶橙染色和MTT活性测定,观察细胞在两种不同表面上的粘附和增殖活性.结果:荧光显微镜显示两组钛片上的内皮细胞均随着培养时间延长而增多,24 h时粗糙表面钛片上粘附的内皮细胞明显多于光滑表面组,而且细胞形态伸展好、成梭形.MTT结果显示粗糙表面组24 h和48 h的0D490值显著高于光滑表面组,而在培养72 h时,两组间没有统计学差异.结论:纯钛经双酸蚀处理形成的粗糙表面较其光滑表面更有利于血管内皮细胞的早期粘附,并促进其增殖.