义齿基托修复材料表面粗糙度对变形链球菌粘附的影响

目的：观察义齿基托修复材料的表面粗糙度对变形链球菌粘附的影响,为正确处理义齿基托的表面提供参考。方法：常规制备钴铬合金标准试件8mm×8mm×1mm共40件,分为5组,每组8件,分别按照五种不同的打磨方法处理试件表面,使用手持式表面粗糙度仪测量每组试件的表面粗糙度,通过体外粘附实验观察变形链球菌在不同表面粗糙度试件上的粘附情况,进行Pearson相关性检验和单因素方差分析。结果：各组试件的表面粗糙度与变形链球菌粘附量之间有显著相关性（P〈O．01）,各组试件细菌粘附量之间的差异具有显著的统计学意义（P〈0．01）。结论：义齿基托修复材料表面粗糙度与细菌的粘附量呈正相关,提示制作义齿时应通过正确的方法减小义齿的表面粗糙度。     

几种常用口腔材料细菌粘附性能比较

目的：探讨5种口腔常用材料的抗细菌粘附性能。方法将自凝甲基丙烯酸甲酯基托树脂、Z250复合树脂、氧化锆陶瓷、纯钛和镍铬合金5种牙科常用修复材料,分别制备成3．0cm ×2．0cm ×0．2cm的板片试件,每组各5片。各组试件表面进行抛光处理,使试件表面粗糙度( Ra)值无显著性差异。实验菌株选用变形链球菌,用细菌悬浮液置试件表面,37℃培养48h,对粘附在材料表面的细菌再进行洗脱、培养、菌落计数,使用SPSSl7．0软件对试验结果进行统计分析。结果纯钛表面变形链球菌粘附量最低,依次为氧化锆陶瓷、Z250复合树脂、镍铬合金、自凝甲基丙烯酸甲酯基托树脂。结论不同口腔材料在同样粗糙度的条件下,抗细菌粘附性能存在差异,钛具有较好的抗细菌粘附性能。     

纯钛表面改性对细菌粘附的影响

目的：研究氮离子溅射和氮等离子浸没注入对纯钛表面细菌粘附能力的影响。方法：制作纯钛试件288件,各随机选出96件,分别采用氮离子溅射和氮等离子浸没注入对其表面改性,纯钛组为对照组,氮离子溅射组为实验1组,氮等离子浸没注入组为实验2组。在实验1、2组和对照组试件表面粘附血型链球菌、粘性放线菌、白色念珠菌和金黄色葡萄球菌,分别进行细菌体外粘附实验。用菌落形成单位计数法统计分析氮离子溅射和氮等离子浸没注入对各种细菌粘附量的影响。结果：在细菌粘附24h、48h、168h后,上述4种细菌在氮离子溅射组和氮等离子浸没注入组表面粘附量较对照组表面粘附量显著减少（P〈0.001）,其中4种细菌在氮等离子浸没注入组表面粘附量明显少于氮离子溅射组（P〈0.001）。结论：纯钛表面氮离子溅射和氮等离子浸没注入均可抑制细菌粘附,氮等离子浸没注入较氮离子溅射抑制细菌粘附效果更明显。     

常用可摘局部义齿支架材料表面微生物粘附的实验研究

［摘要］ 目的 研究变异链球菌和白色念珠菌对3种口腔常用金属材料的粘附性,为临床选择合适的材料提供理论依据。方法 选取最常用做可摘局部义齿支架材料的3种金属——钴铬合金、Vitallium 2000材料、纯钛,分别制成尺寸为20 mm×10 mm×2 mm的试件,每组各6个。将各组试件抛光,并保证各组间粗糙度无明显差异。选取变异链球菌和白色念珠菌作为实验菌株,制成菌悬液,分别放入试件进行48 h的粘附实验,取出试件后冲洗、震荡、培养,采用菌落形成计数法(CFU)测定微生物表面粘附量。结果 粘附48 h后,试件表面变异链球菌和白色念珠菌的粘附数量均为钴铬合金>纯钛>Vitallium 2000材料 (P＜0.05)。结论 Vitallium 2000材料与钴铬合金和纯钛相比,粘附微生物的数量最少,值得应用推广。     

微弧氧化纯钛表面对MC3 T3-E 1细胞胶原分泌及成骨基因表达的影响

目的：研究微弧氧化纯钛表面对MC3 T3-E 1细胞胶原分泌和成骨相关基因表达的影响。方法：纯钛圆片分为2个组：微弧氧化组（MAO）和抛光组（PT）,培养板表面（TC）作为对照组。用场发射扫描电镜（FESEM）观察试样表面形态,表面粗糙度仪测量其表面粗糙度。将细胞接种于3组材料表面体外培养,培养第12天用粘胶纤维红染色检测细胞胶原分泌,第16天RT-PCR检测细胞成骨相关基因表达。结果：纯钛表面经微弧氧化处理后形成一层多孔氧化层,表面粗糙度增加（P＜0．01）。细胞在MAO组试件表面的胶原分泌高于PT或TC组表面（P＜0．05）。细胞在MAO组试件表面OSX、COL-Iα1及OPN基因的表达均稍高于PT表面。结论：相比于纯钛抛光表面,微弧氧化纯钛表面更能促进MC3 T3-E 1细胞胶原分泌。     

不同粗糙度金铂合金和镍铬合金对种植体龈下优势菌粘附性的影响

目的 研究不同粗糙度冠修复材料对种植体龈下优势菌粘附性的影响。方法 选用两种常用冠修复合金材料:金铂合金和镍铬合金。将其制成两种不同粗糙度的试件粘固于种植纯钛板上,分别与4种龈下优势菌牙龈卟啉单胞菌(Porphyromanus gingivalis,Pg)、伴放线放线杆菌(Actinobacillus actinomycetemcomitans,Aa)、中间普氏菌(Prevotella intermedia,Pi)及具核梭杆菌(Fusobacterium nuclertum,Fn)共同厌氧孵育,采用菌落形成单位(colony-forming unit,CFU)计数法量化测定培养试件表面的细菌量,并进行统计学分析。同时扫描电镜观察各种菌在试件上的附着情况。结果 经两两比较,同种合金中粗糙度大的试件四种细菌附着量均大于粗糙度小的(P<0.01);同种粗糙度的试件,金铂合金与种植体钛上各种细菌粘附量均大于镍铬合金与种植钛上的附着量(P<0.01)。结论 在相同条件下,冠修复合金抛光度越高,细菌粘附量越小。体外培养镍铬合金上四种细菌的粘附均小于金铂合金。     

钴铬合金表面粗糙度对口内常见细菌黏附的影响

目的:观察并分析口腔常见菌种在不同表面粗糙度的钴铬合金修复体表面黏附和定植的数量,为临床制作良好的修复体和尽可能减少细菌在修复体表面附着和定植提供参考.方法:所有钴铬合金样本按不同步骤打磨抛光后,应用表面粗糙度仪MAHR M1测试其表面粗糙度,按不同粗糙度分为6组.将6组试件放入含有变形链球菌(Ua)、内氏放线菌(An)和牙龈卟啉单胞菌(Pg)的混合培养基中作厌氧培养,24h后分别定量检测各组试件表面黏附的细菌数量以及液体培养基中的细菌数量,将结果采用SPSS6.0软件包进行方差分析.结果:各组试件的表面粗糙度有显著差异(P<0.05).各组试件表面及液体培养基中均检测不到Pg,24h后,Ua和An在钴铬合金各组表面黏附定植的数量均有显著差异(P<0.05),细菌定植总数也有显著差异(P<0.05).结论:3种细菌混合培养时,Pg受到强烈的抑制.钴铬合金不同的表面粗糙度导致细菌黏附定植数量显著差异,粗糙度越大,细菌黏附量越多.临床应采用高度抛光的钴铬合金修复体,以尽量减少修复体表面的细菌黏附.     

不同表面处理对纯钛的耐腐蚀性研究

目的：研究不同表面处理方式对纯钛耐腐蚀性的影响。方法：制作纯钛试件36件,分别进行机械抛光和电解抛光后,浸泡于不同氟浓度(0%、0.05%、0.2%)人工唾液中,(37.0±1.0)℃浸泡4周,测量浸泡前后表面粗糙度并观察表面形貌。结果：浸泡前后电解抛光组表面粗糙度均小于机械抛光组,差异有统计学意义(P<0.01);浸泡后纯钛表面粗糙度随氟浓度升高而增加。无氟存在时浸泡前后两组差异无统计学意义(P>0.05),加入氟后均与前组差异有统计学意义(P<0.01),电解抛光组与机械抛光组组间比较差异均有统计学意义(P<0.01)。显微镜下观察其表面形貌与粗糙度值结果一致。结论：电解抛光方式的耐腐蚀性优于机械抛光;氟离子对纯钛具有腐蚀性;高氟制品对纯钛的耐腐蚀性影响较大,选用纯钛修复体的患者,建议电解抛光后戴入口内。     

贵金属合金及粗糙度对种植体龈下优势菌黏附性的影响

目的:观察2种合金及其粗糙度对种植体龈下优势菌黏附性的影响.方法:选用2种常用冠修复合金材料:金铂合金和金钯合金.将其制成2种不同粗糙度的试件,粘固于种植纯钛板上,分别与4种龈下优势菌Pg、Aa、Pi及Fn共同厌氧孵育,采用菌落形成单位(CFU)计数法量化测定培养试件表面的细菌黏附量.应用SPSS13.0软件包,对试件表面粗糙度的测量值及试件上黏附的菌落数进行统计学分析,同时在扫描电镜下观察各种菌在试件上的附着情况.结果:同种合金中.粗糙度大的试件4种细菌附着量均大于粗糙度小者(P＜0.01);同种粗糙度的试件,金铂合金与种植体钛上各种细菌黏附量均大于金钯合金与种植钛上的附着量(P＜0.01).结论:金钯合金对细菌黏附的影响比金铂合金大,同种合金粗糙度大者.细菌黏附量多.     

变形链球菌黏附对2种不同抛光方式的纯钛、钛合金表面腐蚀的影响

目的:研究在厌氧环境下变形链球菌粘附对2种抛光方式的纯钛及钛合金表面腐蚀的影响.方法:将牙科用纯钛、钛合金材料制备成30mm×8mm×1mm板片,各32片,分为2组,分别进行机械抛光和电化学抛光.再将每组试件随机分为空白对照组、培养基对照组、3个月实验组和6个月实验组.将试件放入各组对应的试管,置于95%N2、5%CO2、37℃环境中,细菌每周传代1次,试件按各组预定时间取出,消毒灭菌.以表面轮廓仪测试各组试件表面粗糙度变化,扫描电镜观察各组试件表面形态变化,采用SPSS11.0软件包对结果进行方差分析.结果:纯钛实验组较对照组粗糙度无显著差异(P>0.05),钛合金实验组较对照组粗糙度有显著差异(P<0.05).同种材料2种抛光方式下的实验组和对照组粗糙度变化无显著差异.扫描电镜下可见纯钛及钛合金试件表面存在腐蚀.纯钛表面腐蚀孔较钛合金少.结论:变形链球菌黏附对纯钛、钛合金表面产生腐蚀,单纯机械抛光和电化学抛光对变形链球菌腐蚀作用的影响无显著差异.     

牙科陶瓷表面粗糙度与细菌粘附的实验研究

目的　比较陶瓷抛光和陶瓷上釉后表面粗糙度的差异及变形链球菌在其表面的粘附能力。方法　制作陶瓷样本 30个。A组陶瓷用金刚石抛光膏打磨抛光 ,B组陶瓷上釉 ,C组陶瓷用2 4 0 #Al2 O3 磨头磨平。用轮廓仪测量各组陶瓷样本的表面粗糙度。将各组样本置于变形链球菌悬浮液中 ,37℃培养 1h。图像分析仪计算变形链球菌在各样本表面的粘附面积比。结果　A、B、C组陶瓷的表面粗糙度分别为 (0 1987± 0 0 5 7) μm、(0 1990± 0 0 91) μm及 (0 4 2 6 0± 0 174 ) μm。变形链球菌在A、B、C 3组陶瓷表面的粘附面积比分别为 (15 92± 4 37) %、(16 39± 6 31) %、(41 4 8± 12 1) %。经统计学分析 ,A、B组陶瓷组间表面粗糙度及细菌粘附面积比差异无显著性 (P >0 0 5 ) ,C组陶瓷与其他各组样本表面粗糙度及细菌粘附面积比差异有高度显著性 (P <0 0 1)。结论　陶瓷上釉和抛光表面能达到同样光滑 ,细菌在其表面的粘附量亦基本相同。粗糙陶瓷表面比光滑陶瓷表面更容易粘附口腔细菌     

等离子渗氮表面处理对纯钛材料细菌黏附能力的影响

目的：研究等离子渗氮对钛表面的组织结构、性能及对变形链球菌黏附的影响。方法：将相同规格的钛片60片经逐级抛光后随机分成抛光组和等离子渗氮表面处理组。测量所有试件表面的粗糙度值,并采用扫描电镜、Axiovert 25CA光学图像分析仪及GDA750对钛表面渗镀层的表面形貌情况进行分析;将材料接种于变形链球菌悬液1h,在荧光显微镜下计数黏附细菌的数量。结果：等离子渗氮表面处理仅使纯钛表面粗糙度略微增加,并均在0.2μm以下;扫描电镜显示,等离子渗氮表面处理后材料表面的原始划痕消失;GDS检测分析结果表明,等离子渗氮表面处理后,表面主要由氮化钛化合物组成。经渗氮处理后,纯钛黏附细菌的量显著减少。结论：纯钛经等离子渗氮表面处理后形成了稳定的改性层,且能减少细菌的黏附。     

Effect of surface roughness of porcelain on adhesion of bacteria and their synthesizing glucans

STATEMENT OF PROBLEM: In some instances of porcelain restoration, refinishing is inevitable. In terms of plaque accumulation on porcelain, refinishing could be a substitute method for glazing. PURPOSE: This study compared the amount of adhesion of plaque components (bacterial cells and glucans) on porcelain disks with various degrees of surface roughness to assess the effects of surface roughness on the amount of plaque accumulation. MATERIAL AND METHODS: Radiolabeled cell suspensions were incubated with porcelain disks for 3, 8, and 24 hours at 37 degrees C, and the amounts of adhered cells and glucans were measured by using a liquid scintillation method. RESULTS: The amount of cells and glucans adhered on porcelain increased with incubation time. The surface roughness value and the amount of plaque adhesion decreased with the increase in polishing level. However, the greatest amount of plaque was adhered on glazed surfaces, although their surfaces were smoother than the surfaces polished with 120- or 600-grit abrasive papers. CONCLUSION: With the exception of glazed surfaces, a positive correlation between surface roughness and the amount of plaque accumulation was observed. Repolishing with a diamond paste would not induce problems of plaque accumulation, compared with an intact glazed surface.     

Comparison of castability and surface roughness of commercially pure titanium and cobalt-chromium denture frameworks.

STATEMENT OF PROBLEM: Titanium is a biocompatible material, but it is not widely used in clinical dentistry for conventional removable denture frameworks. Little research exists on its applicability. PURPOSE: This study compared the casting accuracy and roughness of titanium and cobalt-chromium denture frameworks. MATERIAL AND METHODS: Twenty Kennedy Class II, Division 1 removable partial denture frameworks were fabricated with commercially pure titanium (n = 10) and a cobalt-chromium alloy (n = 10). The casting accuracy of each framework was determined by visual, radiographic, and microscopic methods. The roughness of each polished framework surface was analyzed with atomic force microscopy. RESULTS: The clinical fit, porosities, and microporosities of both types of metal frameworks were qualitatively similar. The surface roughness of polished pure titanium and cobalt-chromium frameworks was 104.43 +/- 69.24 nm and 133.91 +/- 40.92 nm, respectively. This difference was not statistically significant (P >.05). CONCLUSION: The clinical fit, porosity, and surface roughness of the titanium and cobalt-chromium frameworks fabricated for this study were comparable.     

不同复合树脂修复体表面粗糙度与菌斑黏附关系的研究

目的：研究复合树脂修复体表面粗糙度的不同对其表面细菌黏附程度的影响。方法：对3种不同复合树脂材料进行表面处理,使每一种材料相同地形成3种粗糙度。将不同粗糙度级的试件与口腔变形链球菌于体外培养,测定细菌黏附量。结果：随着粗糙度的降低,各树脂试件的菌斑黏附量均有明显下降;同一粗糙度实验组z350纳米树脂的菌斑黏附量较少。结论：表面粗糙度对细菌黏附有重要影响,即表面越粗糙,菌斑形成越多。相同处理条件下,Z350纳米树脂的菌斑黏附量少。     

The effect of polishing on surface roughness of tissue conditioners

PURPOSE: Surface roughness can affect microbial colonization of long-term denture liners, alloys, and denture acrylic. The purpose of the present study was to examine the effect of finishing and polishing procedures on surface roughness of 4 temporary resilient denture liners (tissue conditioners). MATERIALS AND METHODS: Mean surface roughness was measured for 4 materials (Lynal, Visco-gel, Coe-Soft, and Functional Impression Tissue Toner [FITT]) finished in 4 ways: unfinished (control); polished; reduced, unpolished; and reduced, polished. Samples were allowed to polymerize at 37 degrees C for 24 hours, and the surface roughness was measured using a Mitutoyo Surftest 212. RESULTS: Mean surface roughness ranged from 1.8 +/- 0.8 microns for polished Lynal to 7.8 +/- 1.1 microns for reduced, unpolished FITT. All polished samples were smoother than unpolished samples (including controls), whether or not the samples were reduced with a bur. CONCLUSION: Polished samples of tissue conditioning material had lower mean surface roughness measurements than control or reduced, unpolished samples at the 95% level of confidence. There was no difference in mean surface roughness measurements of control samples and unpolished samples reduced with a bur at the 95% level of confidence. Mean surface roughness differed significantly between the materials tested.     

两种抛光方法对纯钛和钴铬合金粗糙度的影响

目的：研究两种抛光方法对纯钛和钴铬合金表面粗糙度的影响。方法：将纯钛和钴铬合金各分为3组,除一个对照组外,其余两组分别进行机械法和化学法抛光。记录试件抛光后的减重率（wt%）,测量表面粗糙度Ra值,并用扫描电镜（SEM）观察试件表面形态变化。结果：同种金属经过不同抛光处理后,减重率和表面粗糙度Ra值都有显著差异（P〈0.01）,且纯钛和钴铬合金分别经过同种抛光处理后,减重率和表面粗糙度也均有显著差异（P〈0.01）。扫描电镜观察表明,化学抛光后钴铬合金表面更加光滑,均匀一致。结论：与纯钛相比,钴铬合金更容易抛光,且化学法比机械法更易于获得良好的金属表面。     

振荡培养条件下氧化锆陶瓷和钛合金表面粗糙度与细菌黏附的比较

目的：振荡培养条件下比较氧化锆陶瓷和钛合金抛光后表面粗糙度的差异及变形链球菌在其表面的黏附能力。方法：制作氧化锆陶瓷和钛合金样本各6个。A组氧化锆陶瓷用EVE专用抛光轮高度抛光,B组钛合金原始铸件依次用粗砂纸、水砂纸（依次为200目、600目、800目、1000目、1200目、1500目、2000目）逐级磨光,再用抛光轮抛光。用表面粗糙度检测仪测量各组样本的表面粗糙度。将两组样本置于变形链球菌悬浮液中,37℃振荡培养条件下培养1h。荧光显微镜下计数黏附变形链球茵的数量,并通过扫描电子显微镜观察各样本的表面形貌。结果：A、B两组的表面粗糙度分别为（0．0548±0．027）μm、（0．0483±0．006）μm。变形链球菌在A、B两组样本表面的黏附数分别为4．2222±1．019、8．5417±2．208。经统计学分析,A、B两组表面粗糙度差异无显著性（P〉0．05）,A组与B组样本变形链球菌黏附数差异有显著性（P〈0．05）。扫描电镜显示,氧化锆陶瓷抛光组试件表面散在少量细小孔隙,而钛合金抛光组试件表面未见少量细小空隙,但有较多裂隙和凹陷。结论：氧化锆陶瓷和钛合金抛光后表面能达到同样光滑,但钛合金表面比氧化锆陶瓷表面更容易黏附变形链球茵。