重组合同种异体皮质骨修复大段负重骨缺损的组织计量学研究

目的 :比较不同处理方式的深低温冷冻同种异体皮质骨修复兔大段负重骨缺损的组织计量学效果 ,为临床大段负重骨缺损的重建提供新方法。方法 :4 0只新西兰大白兔随机分为 5组 ,造成左侧股骨中上段缺损 2cm的模型 ,分别采用重组人骨形态发生蛋白 2 (rhBMP 2 )和Ⅰ型可吸收胶原海绵 (ACS)对各组移植骨进行处理 ,其中A组植入异体骨 +rhBMP 2 +ACS ,B组植入异体骨 +rhBMP 2 ,C组植入异体骨 +ACS ,D组单纯植入异体骨 ,E组植入自体骨。术后 1 2周处死动物 ,移植骨和宿主骨远、近结合部及移植骨中段分别取材 ,做不脱钙磨片 ,在荧光显微镜和普通光镜下测量新骨形成率、骨孔隙率、骨单位半径和哈佛氏管直径。结果 :A组在新骨形成率、骨孔隙率、骨单位半径和哈佛氏管直径等方面均优于B、C、D组 ,与E组相仿。结论 :同种异体皮质骨、rhBMP 2和ACS复合移植具有高效持续的骨诱导作用 ,能平衡骨吸收 /骨形成活动 ,移植骨愈合质量好 ,是修复大段负重骨缺损的好方法。     

自体富血小板-白细胞凝胶复合同种异体骨移植对大段骨缺损的干预效应

目的探讨自体富血小板-白细胞凝胶(PLRG)复合同种异体骨移植对大段骨缺损的干预效应。方法制备自体PLRG与大段同种异体脱钙骨(1.5 cm)后,取成年健康日本大耳白兔30只,制双侧桡骨中段1.5cm缺损,分A、B两组,每组15只30侧,A组缺损处嵌插植入同种异体骨段,其管腔内及两断端连接处用PLRG封闭;B组嵌插单纯植入异体脱钙骨段作为对照。移植12周时经放射学、组织学及组织形态计量学、生物化学和生物力学检测,评价骨缺损的重建修复效果。结果 (1)X线及骨密度计量分析显示,A组断端桥接良好,骨密度显著高于B组(P<0.05);(2)组织学观察发现,移植区A组新生骨形成和移植骨破骨细胞性骨吸收均较B组活跃,形态计量分析显示单个视野的成骨面积显著大于B组(P<0.05);(3)碱性磷酸酶活性检测显示,A组显著高于B组(P<0.05);(4)抗弯生物力学测试显示,A组破断载荷和破断能量均显著高于B组(P<0.05)。结论 PLRG可加速大段骨缺损再生修复,并促进大段同种异体骨骨重建。     

纳米羟基磷灰石复合重组人骨形态发生蛋白-2人工骨治疗骨缺损的研究

目的以纳米羟基磷灰石(Nano-HA)为载体支架,复合重组人骨形态发生蛋白-2(rhBMP-2)构建NanoHA复合rhBMP-2人工骨(Nano-HA/rhBMP-2复合人工骨),植入兔桡骨缺损,探讨Nano-HA/rhBMP-2复合人工骨局部成骨活性及修复兔桡骨骨缺损的能力,为临床骨缺损治疗提供理论依据。方法将36只成年的新西兰雄性大白兔随机分为Nano-HA/rhBMP-2复合人工骨组(A组)、Nano-HA人工骨组(B组)、空白组(C组)3组,每组12只,制作成桡骨为12mm的骨缺损模型。A组植入Nano-HA/rhBMP-2复合人工骨;B组植入Nano-HA人工骨,C组不植入任何材料。植入后于4、8、12周行大体观察、血清碱性磷酸酶(ALP)检测、X线摄片、组织学观察及生物力学检测。结果 1)与术前比较,3组ALP含量术后4周均明显升高(P<0.05),术后8周达最高峰(P<0.05),之后开始下降,在12周时ALP含量均较术前显著升高(P<0.05);3组术后4、8、12周ALP含量比较差异均有统计学意义(P<0.05)。2)X线片表现:术后12周A组植入材料完全降解,骨皮质连接完成,骨缺损完全修复;B组材料大部分降解,有大量骨密度影,有大量骨痂形成,骨髓腔基本再通,骨缺损大部分修复;C组骨折断端光滑硬化吸收,无骨质长入,骨髓腔封闭,形成骨不连。3组术后4、8、12周Lane-Sandhu X线骨形成评分A组>B组>C组,差异均有统计学意义(P<0.05)。3)组织学表现:术后12周A组材料完全降解,大量的板层骨形成,骨痂完成塑形,骨缺损修复;B组材料大部分降解及密质骨形成,有大量新生骨组织,骨缺损大部分修复;C组骨缺损断端大量的纤维组织形成,未见新骨形成,断端骨不连。3组术后4、8、12周Lane-Sandhu组织学骨形成评分A组>B组>C组,差异均有统计学意义(P<0.05)。4)三点抗弯生物力学检测A组标本术后4、8、12周均显著高于B组(P<0.05)。结论 Nano-HA/rhBMP-2复合人工骨比Nano-HA人工骨具有更强的成骨能力,明显缩短了骨缺损愈合时间。Nano-HA/rhBMP-2复合人工骨在修复长骨骨缺损方面具有潜在的临床价值,为临床骨缺损修复材料的选择提供了理论依据。     

自体骨复合骨形态发生蛋白2和(或)血管内皮生长因子修复海水浸泡开放性骨缺损的实验研究

目的初步探讨骨形态发生蛋白2（BMP-2）和血管内皮生长因子（VEGF）单独及联合应用修复海水浸泡开放性骨缺损的疗效。方法将60只新西兰兔双侧桡骨中段制作1.5 cm骨缺损,海水浸泡3 h,随机分为A、B、C、D四组,每组15只兔。A组为对照组,植入自体髂骨;B、C、D三组为实验组,B组植入自体髂骨/可吸收胶原海绵（ACS）/BMP-2;C组植入自体髂骨/ACS/VEGF;D组植入自体髂骨/ACS/BMP-2/VEGF。分别于术后1、2、4、8及12周切取标本,每组每个时相点根据随机原则取6个标本,通过X线摄片、骨痂灰度值、组织形态学观察、免疫组织化学及环境扫描电镜观察各时相点骨缺损修复情况。结果①1、2周时,四组X线差异不明显,4、8、12周时B、C、D三组与A组的骨痂灰度值比较,差异有统计学意义（P〈0.05）;D组与B、C两组平均骨痂灰度值比较差异有统计学意义（P〈0.05）;B、C、两组平均骨痂灰度值比较差异无统计学意义（P〉0.05）。②免疫组织化学结果表明：骨缺损修复早期BMP-2、VEGF二者相互促进,联合应用具有协同效应。结论①BMP-2、VEGF单独应用均能促进海水浸泡兔桡骨开放性骨缺损的修复。②BMP-2和VEGF联合应用能显著促进海水浸泡开放性骨缺损修复,两者联合应用具有协同效应。     

BMP-2复合PLGA／磷酸三钙修复大段骨缺损的实验研究

目的研究骨形态发生蛋白-2（Bone Morphogenetic Protein,BMP-2）复合聚乳酸一乙醇酸共聚物（P01y-Laetide-CoGlycolic,PLGA）／磷酸三钙（Tricalcium Phosphate,TCP）修复羊大段桡骨缺损的能力。方法手术制成30mm绵羊尺、桡骨骨缺损模型,A组在桡骨缺损区植入BMP-2复合PLGA／磷酸三钙棒材,B组不植入任何材料。两组均以钢板固定桡骨缺损区。术后4、8、12、24周拍摄X片,24周时处死动物进行组织学观察。结果X线片检查示A组术后24周桡骨缺损处完全成骨修复,皮质骨与髓腔的轮廓清晰;B组无有效骨痂形成。组织学检查示A组术后24周时骨痂外层形成皮质骨,为较成熟的板层骨,与断端皮质骨完全融合,其中央可见大量骨髓组织,未见植人材料残留;B组缺损区可见大量纤维组织填充。结论BMP-2复合PLGA/磷酸三钙能很好的修复绵羊大段桡缺损,未来有望成为解决临床骨缺损的有效材料。     

带血供骨膜瓣包裹同种异体骨修复骨缺损的实验研究

目的探讨带血供骨膜瓣包裹去抗原异体骨修复骨缺损的效果。方法将兔的股骨经去抗原化后作为供体，制作带血供骨膜瓣色裹同种异体骨修复免大段骨缺损模型，实验设置对照组，即未用血管化骨膜瓣包裹移植物。分别在术后第4周、8周和16周分别行X线摄片，并对移植物及周围软组织、骨组织进行组织学观察（HE染色），对两组移植物骨形态发生蛋白（BMP）进行免疫组织化学染色。结果X线表现为实验组骨痂形成的速度快于对照组，骨痂形成的质和量优于对照组，组织学观察显示实验组骨质更新速度以及新生血管速度均快于对照组，BMP免疫组织化学染色显示在相同时期实验组的表达明显强于对照组。结论带血供骨膜瓣包裹异体骨修复骨缺损优于单纯异体骨移植，明显缩短骨缺损的修复时间。     

双基因rhBMP-4/VEGF121在治疗兔桡骨缺损中的作用

目的 研究双基因rhBMP-4/VEGF121混悬液在骨缺损修复中的作用.方法 新西兰成年兔20只,制作40侧桡骨中段15 mm骨缺损实验模型,随机分为A、B、C、D组.A组植入rhBMP-4+VEGF121+明胶海绵,B组植入rhBMP4+明胶海绵,C组植入VEGF121+明胶海绵,D组只植入明胶海绵.并于术后4、8、12周对骨缺损区进行大体、X线片、组织形态学观察,图像分析新生骨小梁的面积.结果 A组在12周内骨缺损完全修复,髓腔再通,且同时期内新生骨的数量和质量显著优于其他组;B、C组骨缺损为未完全成熟的板层骨修复,髓腔部分再通,B组骨愈合成熟度较C组佳;D组缺损主要由纤维结缔组织填充.结论 双基因rhBMP-4/VEGF121治疗骨缺损比单基因具有更好的促进骨修复再生能力.     

带血供骨膜瓣与同种异体脱钙骨联合修复大段骨缺损的实验研究

目的　探讨带血供骨膜瓣与同种异体脱钙骨联合修复大段骨缺损的效果。方法　以兔桡骨中段 15mm的大段骨缺损为模型 ,通过X线lane评分、组织学观察、电镜扫描 ,评价术后 4、8、12、16周时带血供骨膜瓣与同种异体脱钙骨联合修复骨缺损的效果。结果　带血供的骨膜瓣与同种异体脱钙骨联合修复效果明显好于单纯脱钙骨组 ,前者在Lane评分 (P <0 .0 5 )、组织学观察等方面均优于后者。结论　带血供骨膜瓣与同种异体脱钙骨联合修复大段骨缺损效果优于单纯脱钙骨。     

同种异体兔骨髓间充质干细胞复合纳米晶胶原基骨修复胫骨缺损的实验研究

目的探讨同种异体兔骨髓间充质干细胞（marrow mensenchymal stem cells，MSCs）与纳米晶胶原基骨（nano—hydroxyapatite／collagen，NHAC）修复材料构建的组织工程骨修复兔胫骨缺损的可行性。方法24只新西兰大白兔胫骨中段形成10mm长的骨缺损，右侧骨缺损处植入组织工程骨作为实验组，左侧骨缺损处植入单纯NHAC作为对照组。术后3、6、9、12wk分批处死动物，行一般情况、缺损区大体观察、X线、组织学染色分析等指标检测，行统计学分析，比较各组修复骨缺损的效果。结果24只新西兰大白兔均进入结果分析。①术后一般情况：各组兔术后恢复及进食均正常，伤口无炎症反应，愈合良好。②大体观察：实验组术后6wk骨缺损部分修复，9、12wk骨缺损完全修复，3、6、9、12wk骨缺损修复情况明显好于对照组。③X线：实验组缺损区术后3wk可见有骨痂生长，9wk骨缺损基本修复，对照组术后12wk缺损区基本修复，各观察时间点实验组骨缺损修复情况明显好于对照组。④组织学染色：实验组缺损区新生类骨样组织、编织骨和板状骨出现的时间较对照组早，并且不经软骨介导即可直接成骨，而对照组以“爬行替代”方式修复骨缺损。结论同种异体兔MSCs复合NHAC修复骨缺损的能力较单纯NHAC强且迅速，能够对大段骨缺损进行快速有效的修复。     

组织工程化磷酸钙骨水泥修复兔股骨远端骨缺损的评价

背景：磷酸钙骨水泥是一种良好的骨移植替代材料,具有优异的组织相容性和骨引导性能。但是骨诱导性能不佳限制了其广泛应用。本研究目的是评价具有骨诱导活性的组织工程化磷酸钙骨水泥修复骨缺损的效果,并观察了种子细胞在体内的增殖、分化和转归情况。 方法：通过将微囊化rhBMP-2基因修饰的骨髓间充质干细胞种植入磷酸钙骨水泥中来制备组织工程化磷酸钙骨水泥。rhBMP-2基因修饰的骨髓间充质干细胞可以共表达绿色荧光蛋白（GFP）与重组人骨形态发生蛋白-2（rhBMP-2）。制备兔双侧股骨髁骨缺损模型,将组织工程化磷酸钙骨水泥随机植入一侧骨缺损中,单纯磷酸钙骨水泥植入对侧骨缺损中,做自身对照。12w后取材,进行X线片检查、组织形态学观察、骨计量学评价和种子细胞体内示踪观察。 结果：X线片显示两种骨水泥对骨缺损填充良好,组织工程化磷酸钙骨水泥吸收速度和新骨形成速度较快。组织学观察与骨计量学评价结果示组织工程化磷酸钙骨水泥被分解成无数个小块,可以看到活动动性骨吸收和骨重建现象,单纯骨水泥组中残余骨水泥面积相对较大。体内示踪结果显示,术后12w组织工程化磷酸钙骨水泥组中仍有大量的细胞同时表达GFP和rhBMP-2,这些细胞不仅分布于髓腔中,也分布于骨表面。 结论：组织工程化磷酸骨水泥可以有效地修复骨缺损,同种异体移植种子细胞可以在体内存活并分化。     

Osteogenic potential of the human bone morphogenetic protein 2 gene activated nanobone putty

Background Nanobone putty is an injectable and bioresorbable bone substitute. The neutral-pH putty resembles hard bone tissue, does not contain polymers or plasticizers, and is self-setting and nearly isothermic, properties which are helpful for the adhesion, proliferation, and function of bone cells. The aim of this study was to investigate the osteogenic potential of human bone morphogenetic protein 2 （hBMP2） gene activated nanobone putty in inducing ectopic bone formation, and the effects of the hBMP2 gene activated nanobone putty on repairing bone defects.
Methods Twenty four Kunming mice were randomly divided into two groups. The nanobone putty ＋ hBMP2 plasmid was injected into the right thigh muscle pouches of the mice （experiment side）. The nanobone putty ＋ blank plasmid or nanobone putty was injected into the left thigh muscle pouches of the group 1 （control side 1） or group 2 （control side 2）, respectively. The effects of ectopic bone formation were evaluated by radiography, histology, and molecular biology analysis at 2 and 4 weeks after operation. Bilateral 15 mm radial defects were made in forty-eight rabbits. These rabbits were randomly divided into three groups： Group A, nanobone putty ＋ hBMP2 plasmid; Group B, putty ＋ blank plasmid; Group C, nanobone putty only. Six rabbits with left radial defects served as blank controls. The effect of bone repairing was evaluated by radiography, histology, molecular biology, and biomechanical analysis at 4, 8, and 12 weeks after operation.
Results The tissue from the experimental side of the mice expressed hBMP2. Obvious cartilage and island-distributed immature bone formation in implants of the experiment side were observed at 2 weeks after operation, and massive mature bone observed at 4 weeks. No bone formation was observed in the control side of the mice. The ALP activity in the experiment side of the mice was higher than that in the control side. The tissue of Group A rabbits expressed hBMP2 protein and higher ALP level. The ne     

重组合异体冻干骨修复兔桡骨节段性骨缺损

目的 :研究碱性成纤维细胞生长因子 (bFGF)和透明质酸凝胶 (HAG)复合异体冷冻干燥骨修复兔桡骨缺损的能力 ,并探讨它们的作用机制。方法 :于 36只新西兰大白兔两侧桡骨干处造成 15mm缺损 ,采用 3种不同的治疗方法 :A组 ,植入bFGF ,HAG与冻干骨的复合物 ;B组 ,植入吸附bFGF的冻干骨 ;C组 ,单纯植入冻干骨作为对照。在术后不同时间进行放射学、组织学和核素扫描检查 ,并测定钙含量。结果 :A组在术后不同时间的骨代谢活性 ,新骨生成量和钙含量均高于B组 ,B组高于C组 (P <0 .0 5或P <0 .0 1)。A组和B组缺损分别于术后 8周和 10周完全愈合。结论 :bFGF作为一种骨生长因子 ,促进新骨生成 ;HAG作为缓释载体 ,提高bFGF的效能 ,三者结合可有效修复骨缺损     

重组人骨形成蛋白-2促进兔下颌牵张成骨的实验研究

目的：研究重组人骨形成蛋白-2（recombinant human bone morphogenetic protein-2,rhBMP-2）对兔下颌牵张成骨的作用。方法：建立兔下颌双侧牵张成骨动物模型．于下颌右侧骨断端间植入含有rhBMP-2的可吸收胶原海绵（absorbable collagen sponge,ACS）,左侧单纯应用ACS作为对照。分别于固定期第3、5周末处死动物。取标本行X线及组织学观察。结果：应用rhBMP-2侧新骨形成的速度以及骨小梁的密度均高于对照。结论：局部应用rhBMP-2能够提高牵张区新骨形成的速度和质量．对下颌牵张成骨具有促进作用。     

不同浓度一氧化氮对冻干移植骨修复骨缺损影响的实验研究

目的　比较深低温冷冻干燥骨和亚硝基化牛血清蛋白的复合物与单独应用深低温冷冻干燥骨在修复大段骨缺损中的效果 ,探讨NO在异体组织移植中的作用。方法　采用新西兰大耳白兔桡骨中段切除 1.5cm骨干和骨膜的实验动物模型 ,同时制备能在体内持续缓慢释放一氧化氮的亚硝基化牛血清蛋白 ,将 4 8只兔随机分成 3组。A组 :低浓度亚硝基化牛血清蛋白与深低温冷冻干燥骨的复合物 (低浓度NO冻干骨组 ) ;B组 :高浓度亚硝基化牛血清蛋白与深低温冷冻干燥骨的复合物 (高浓度NO冻干骨组 ) ;C组 :深低温冷冻干燥骨 (单纯冻干骨组 )。分别在术后3、6、9及 12周对上述 3组的骨缺损模型进行X线片、组织学检查及钙含量测定。并在 12周处死动物前 ,测量动物体内NO的含量。结果 (1)低浓度NO冻干骨组修复骨缺损的效果明显好于单纯冻干骨组 (P <0 .0 5 )和高浓度NO冻干骨组 (P <0 .0 1) ,术后第 12周缺损区完全性修复 ,骨髓腔再通 ;单纯冻干骨组修复骨缺损的效果优于高浓度NO冻干骨组 (P <0 .0 5 )。 (2 ) 12周时高浓度NO冻干骨组的NO含量高于单纯冻干骨组 (P <0 .0 1)和低浓度NO冻干骨组 (P <0 .0 5 ) ,低浓度NO冻干骨组的NO含量高于单纯冻干骨组 (P <0 .0 5 )。结论　在修复骨缺损的过程中 ,低浓度NO能促进骨愈合 ,而高浓度N     

Reconstruction of orbital defect in rabbits with composite of calcium phosphate cement and recombinant human bone morphogenetic protein-2

PURPOSE Calcium phosphate cement (CPC) is a biocompatible and osteoconductive bone substitute, and recombinant human bone morphogenetic protein-2 (rhBMP-2) has strong osteoinductibility, therefore we developed a composite bone substitute with CPC and rhBMP-2 and evaluate its reconstruction effect in rabbit orbital defect. METHODS Thirty-six rabbits were randomly divided into two groups and a 5mm×5mm×2mm bone defect in the infraorbital rim was induced by surgery in each orbit (72 orbits in all). The orbital defects were treated with pure CPC or composite of CPC and rhBMP-2. The osteogenesis ability of different bone substitute was evaluated by gross observation, histological examination, histomorphometrical evaluation, compressive load-to-failure testing, and scanning electron microscope (SEM). RESULTS Gross observation showed that both bone substitutes were safe and effective for reconstruction of orbital defect. However, histological examination, histomorphometrical evaluation and SEM showed that CPC/rhBMP-2 group had faster speed in new bone formation and degradation of substitute material than CPC group. Compressive load-to-failure testing showed that CPC/rhBMP-2 group had stronger compressive strength than CPC group at every stage with significant difference (P<0.05). CONCLUSIONS Composite of CPC/rhBMP-2 is an ideal bioactive material for repairing orbital defect, with good osteoconductibility and osteoinductibility.     

组织工程化骨修复兔桡骨缺损的实验研究

目的:探讨骨髓间充质干细胞复合脱钙骨基质和骨形成蛋白修复兔桡骨缺损的效果。方法:体外分离、培养骨髓间充质干细胞,复合于脱钙骨基质,以骨形成蛋白进行成骨化诱导。日本大耳白兔45只,随机分为3组,A组:骨髓间充质干细胞+脱钙骨基质+骨形成蛋白;B组:脱钙骨基质+骨形成蛋白;C组:空白组。行兔15 mm桡骨缺损修复。术后12周取桡骨标本,大体观察并手法评估3组桡骨缺损修复情况,组织学及生物力学测定植入材料融合情况。结果:术后12周,大体可见A组基本骨性愈合,融合组织质地硬,形态不规整;B组见少量骨痂形成,尚有部分缺损未愈合。C组骨缺损处见肉芽组织充填,未见骨痂形成。组织学观察Masson染色示A组大量软骨形成,靠近连接处可见新生骨小梁形成且处于成骨活跃期,软骨与骨组织之间过渡自然。B组可见部分新生骨小梁形成,材料骨小梁变细较少,断裂明显。C组未见新生骨小梁形成。生物力学测定A组的最大载荷、抗压强度和弹性模量分别为(87.8±9.8)N、(8.4±0.9)MPa及(187.5±8.2)GPa,均低于健侧组([112.3±11.2)N、(9.5±0.2)MPa及(210.5±15.9)GPa],且组间比较有统计学差异(P<0.05)。结论:骨髓间充质干细胞复合脱钙骨基质和骨形成蛋白修复兔桡骨缺损,优于应用脱钙骨基质和骨形成蛋白,早期生物力学强度低于正常骨组织。     

Reconstruction of orbital defect in rabbits with composite of calcium phosphate cement and recombinant human bone morphogenetic protein-2

Background Calcium phosphate cement （CPC） is a biocompatible and osteoconductive bone substitute, and recombinant human bone morphogenetic protein-2 （rhBMP-2） has strong osteoinductibility, therefore we developed a composite bone substitute with CPC and rhBMP-2 and evaluate its reconstruction effect in rabbit orbital defect.Methods Thirty-six rabbits were randomly divided into two groups and a 5 mmx5 mmx2 mm bone defect in the infraorbital rim was induced by surgery in each orbit （72 orbits in all）. The orbital defects were treated with pure CPC or composite of CPC and rhBMP-2. The osteogenesis ability of different bone substitute was evaluated by gross observation, histological examination, histomorphometrical evaluation, compressive load-to-failure testing, and scanning electron microscope （SEM）.Results Gross observation showed that both bone substitutes were safe and effective for reconstruction of orbital defect. However, histological examination, histomorphometrical evaluation and SEM showed that CPC/rhBMP-2 group had faster speed in new bone formation and degradation of substitute material than CPC group. Compressive load-to-failure testing showed that CPC/rhBMP-2 group had stronger compressive strength than CPC group at every stage with significant difference （P ＜0.05）.Conclusion Composite of CPC/rhBMP-2 is an ideal bioactive material for repairing orbital defect, with good osteoconductibility and osteoinductibility.     

异体脱钙骨基质复合bBMP修复兔桡骨骨缺损

目的：探讨异体脱钙骨基质复合BMP修复节段性骨缺损的能力。方法：64只新西兰大白兔采用桡骨15mm节段性骨缺损模型，随机分为4组，A组植入异体脱钙骨基质(Demineralized Bone Matrix,DBM)与牛骨形态发生蛋白(Bovine Bone Morphogentic Protein,bBMP)复合材料，B组植入异体DBIM，C组植入异体骨粒，D组为空白对照组。术后4、8、12、16w，进行放射学检查、病理组织学检查和计算机图像分析新生骨面积。结果：异体DBM与bBMP复合材料组骨生成、新骨面积和骨连接情况明显优于异体DBM组、异体骨粒组和空白对照组。结论：异体DBM复合BMP材料通过骨诱导和骨传导两种方式修复骨缺损，是一种较为理想、具有高效成骨活性的植骨材料。