树脂卡环与Co-Cr卡环的脱位力及体外循环疲劳测试

目的:比较树脂卡环与Co-Cr卡环在循环疲劳测试中的脱位力及其衰减趋势。方法:制作树脂和Co-Cr卡环,在基牙0.25mm和0.50mm两种倒凹深度下,利用多功能生物力学测定仪进行循环疲劳测试,对比其脱位力大小及衰减情况,同时测试各卡环的形变距离。结果:卡环在循环疲劳测试后其脱位力都不同程度的下降,脱位力下降最明显的是Co-Cr卡环0.50mm倒凹组,达6.937N,最小的是树脂卡环0.25mm倒凹组,为0.050N;循环测试前后2种倒凹深度下Co-Cr卡环组脱位力差异显著,树脂卡环组脱位力差异无统计学意义;Co-Cr卡环组的形变距离大于树脂卡环组。结论:树脂卡环固位力较Co-Cr卡环小,但衰减缓慢、形变小。     

可摘局部义齿卡环疲劳性能测试方法及研究现状

牙列缺损是老年人的常见口腔疾病,会给患者的生活造成诸多不便,不仅影响患者的咀嚼、发音和口颌系统健康,也会对患者的心理健康和生活质量产生不同程度的负面影响.牙列缺损常见的修复方式有种植义齿、固定义齿和可摘局部义齿.目前,虽然选择种植义齿的患者日趋增多,然而仍有很多患者由于身体原因、经济原因等无法选择种植义齿修复.可摘局部...     

可摘局部义齿卡环疲劳的影响因素

研究卡环疲劳的影响因素对确保卡环功能的正常发挥以及延长卡环的使用寿命具有重要意义。本文从卡环的制作材料、组织结构、应力分布、形态、尺寸和使用环境等方面对卡环疲劳的影响因素作一综述。     

酸碱度对Vitallium与钴铬合金卡环疲劳强度影响的比较

目的:比较高钴铬钼合金(Vitallium 2000 plus,V)与钴铬合金(WBA,W)卡环臂在不同酸碱度下相同形变及循环次数时的疲劳衰减。方法:分别铸造V与W直型卡环臂20个,分别置于空气和pH值4.0、6.7和8.0的人工唾液中。用万能试验机进行0.8 mm变形的循环加载20000次,得到载荷-时间曲线算出试件的衰减百分数。扫描电镜观察表面。结果:W各组衰减均高于V,在空气中衰减最小,随实验组pH值增大试件衰减增大;V在pH=4组衰减最多。结论:使用Vitallium 2000 plus铸造可摘局部义齿的卡环可保持更长时间的初始修复效果。     

镍钛机用器械循环疲劳的研究进展

镍钛机用器械与不锈钢器械相比较具有更佳的柔韧性,应用于弯曲根管预备能取得更好的成形和清洁效果,缩短预备时间。但器械折断一直是有待解决的重要问题之一。器械折断的发生会增加根管治疗的难度,甚至导致治疗失败,而器械使用中的循环疲劳是器械折断的主要机制。影响镍钛机用器械循环疲劳的因素很多,包括器械自身因素和外部因素。本文对近年来镍钛机用器械循环疲劳的研究进展进行综述,重点讨论器械循环疲劳的影响因素。     

牙科陶瓷的动疲劳性能研究及循环疲劳寿命数值计算

目的 研究牙科陶瓷材料的力学性能并预测其在循环载荷作用下的寿命.方法 采用三点弯曲法对全瓷标准试件进行动疲劳实验.利用特征参数进一步计算材料在循环载荷下作用至断裂的循环次数理论值.结果 全瓷材料的三点弯曲强度、特征强度σ0和Weibull模数m分别为425.7、453.8 MPa和7.4;亚临界裂纹生长参数n、A和B分别为23.1、3.4×10-15和857.2.全瓷材料的抗折强度预测值10年内下降幅度达47%.数值计算结果显示,牙科陶瓷材料在0～200 N循环应力幅值作用下的疲劳寿命理论值为690 447次.结论 水环境和载荷速率对IPS e.max Press 标准试件的抗折强度值有影响.材料的抗折强度预测值随时间推移逐渐下降.数值计算结果可为体外实验提供校验依据,但需体外循环疲劳及有限元实验对修复体在口内服役的情况进行更精确模拟.     

卡环作用于烤瓷冠的固位力衰减及冠磨损研究

目的研究钴铬合金、纯钛卡环在烤瓷冠的最大脱位力变化趋势和实验前后烤瓷冠表面特定区域的磨损。方法制作模拟下颌第一磨牙外形的镍铬烤瓷冠,其上制作钴铬合金卡环和纯钛卡环。卡环就位后采用万能力学测试仪进行1500次反复摘戴实验,每摘戴20次后测试一次峰值,比较卡环与烤瓷冠脱位力的衰减情况并采用回归拟合的方法进行统计。扫描电子显微镜观察,比较实验前后烤瓷冠定点区域的磨损情况。结果纯钛卡环固位力在520次循环内呈线性衰减。其后趋于稳定,均值9．00N。钴铬合金卡环固位力没有衰减,均值9．36N。二者差别有统计学意义。纯钛卡环在烤瓷冠表面造成的磨损比钴铬合金卡环组轻。结论综合考虑固位力衰减和冠表面磨损情况,烤瓷冠表面适宜采用纯钛卡环。     

树脂卡环固位力和形变的体外研究

目的研究树脂卡环固位力和形变的大小。方法整体铸造前磨牙和磨牙试件各40个,倒凹计测定出0.25 mm和0.50 mm的倒凹。根据基牙类型和倒凹深度,将试件分为4组：0.25 mm倒凹前磨牙组、0.50 mm倒凹前磨牙组、0.25 mm倒凹磨牙组、0.50 mm倒凹磨牙组,每组20个试件。每组试件分别制作树脂三臂卡和Co-Cr合金三臂卡各10个。将卡环戴入相应的基牙并浸泡于去离子水中,测定在0、720、1 440、2 160、2 880、3 600、4 320次连续取出和戴入循环周期时卡环的固位力,并记录0和4 320次循环周期时卡环固位臂卡环尖和抗力臂卡环尖之间的距离。结果1）树脂卡环的平均固位力为1.69 N,低于Co-Cr卡环的平均固位力5.87 N（P<0.01）。在其他因素相同的情况下,树脂卡环的固位力小于Co-Cr卡环的固位力（P<0.01）,磨牙卡环的固位力小于前磨牙卡环的固位力（P<0.01）,0.25 mm倒凹卡环的固位力小于0.50 mm倒凹卡环的固位力（P<0.01）。随着循环次数的增加,Co-Cr卡环的固位力显著降低（P<0.01）,而树脂卡环的固位力无显著变化（P＞0.05）。2）4 320次循环周期后,Co-Cr卡环的固位臂卡环尖和抗力臂卡环尖之间的距离显著增加（P<0.05）,而树脂卡环的固位臂卡环尖和抗力臂卡环尖之间的距离无显著变化（P＞0.05）。结论树脂卡环的固位力和形变均明显低于铸造卡环。     

疲劳试验对两种口腔树脂的黏接耐久性研究

目的 评价两种口腔黏接性树脂 Super-Bond C ＆ B(SB)和 Panvia 21(PV)的黏接耐久性。方法 双臂牵张试验检测SB和 PV的 Mode Ⅰ破坏韧性,研究疲劳试验的影响。结果 SB的破坏韧性值(Gmax)与振动次数N的对数成近似直线的关系;而PV的Gmax分散度大,观察不到明显的趋势。结论 SB的破坏韧性值经疲劳试验后,有下降趋势,而PV的变化趋势不显著。Gmax可作为SB的损伤容许值,在需控制义齿疲劳寿命的修复设计中是有效的。     

人工唾液和乳酸对钛合金卡环疲劳强度影响的研究

目的:探讨人工唾液和乳酸对钛合金卡环疲劳强度的影响.方法:用成品卡环蜡型制作钛合金卡环15个,分为3组,分别在空气中、人工唾液和乳酸溶液中进行测试,初始载荷强度和疲劳失效前的载荷循环次数被自动记录.疲劳裂纹进行扫描电镜分析.结果:钛合金卡环在不同测试条件下的初始载荷强度无差异(P＞0.05).在空气中的循环次数最高,在乳酸溶液中的循环次数最低.SPSS软件分析表明3组之间的疲劳强度有显著性差异(P＜0.01).结论:结果表明人工唾液和乳酸溶液均使钛合金卡环的疲劳强度下降.     

树脂卡环的临床应用效果观察

目的：观察树脂卡环的临床应用效果。方法：76例94个树脂卡环临床使用6至45个月后，对卡环固位力、易折性、支持稳定性、美观性、牙菌斑检测和对基牙及牙周组织的影响等情况进行追踪观察。结果：树脂卡环固位良好；具有美观的特点，可按基牙颜色进行比色；能提供一定的支持稳定作用；并具有良好的生物相容性，对基牙及牙周围组织无损伤。结论：树脂卡环是一种美观适用可以推广的可局部义齿固位体，尤其是在前牙上使用效果更佳。     

���ȶԴ��ѿ���ƣ��ǿ��Ӱ����о�

目的 研究酸碱度对纯钛铸造卡环疲劳强度的影响.方法 于2010年5月至2010年11月,在哈尔滨工业大学航天材料与力学系研究室将20个铸造的纯钛卡环随机分为4组,分别在空气中和pH值分别为4.0、6.8和8.0的人工唾液中进行加载-形变测试,计算机自动记录初始载荷和疲劳失效时的载荷循环次数.应用扫描电子显微镜观察卡环在加载后的腐蚀形貌和疲劳裂纹.结果 纯钛卡环在不同测试条件下的初始载荷差异无统计学意义(P＞0.05).在pH值分别为4.0、6.8和8.0的人工唾液中的载荷循环次数与空气中的比较均明显减少,差异均有统计学意义(P＜0.01);但pH值为6.8和8.0的人工唾液中的载荷循环次数差异无统计学意义(P＞0.05),这两组与pH值为4.0的人工唾液中的载荷循环次数差异有统计学意义(P＜0.05).结论 纯钛卡环的疲劳强度在不同pH值的人工唾液都受影响而降低,且pH值呈酸性的人工唾液对试件的疲劳强度影响更大.     

Scratch test of thermoplastic denture base resins for non-metal clasp dentures

PurposeSeveral thermoplastic denture base resins have been introduced for the fabrication of non-metal clasp dentures. Although the surface of these materials is easily damaged, the surface roughness and characteristics of scratches created have not been evaluated. The purpose of this study was to evaluate the surface roughness of thermoplastic resins using a scratch test for the development of future materials.MethodsFour thermoplastic (polyamide: Valplast^®; VLP and Lucitone FRS^®; FRS, polyethylene terephthalate: EstheShot^®; ES, and polyester: EstheShot Bright^®; ESB) and two conventional acrylic (Heat-polymerizing: Urban^®; HC, and Pour type auto-polymerizing: Pro-Cast DSP^®; PR) denture base resins were examined. Eight specimens, approximately 10 mm × 10 mm × 30 mm in size, of each material were fabricated. Scratch test was performed by a scratch tester with a diamond indenter of 10-μm radius and cone angle 90°, applying a constant load of 500 mN, and 2-mm-long scratches were made. The scratch marks were studied under 3D laser measuring microscope and cross-section profiles at approximately 0.5 mm, 1.0 mm, and 1.5 mm from the starting point were extracted and measured with analysis software. Data from 24 cross-section profiles in each denture base material were analyzed.ResultsThe maximum depths of ES, ESB and FRS were greater than VLP, PR and HC, and the scratch widths of ES, ESB, FRS and VPL were greater than PR and HC.ConclusionsThe results showed that the surface of thermoplastic denture base resins was easily damaged compared to polymethyl methacrylate.     

Clinical application of removable partial dentures using thermoplastic resin. Part II: Material properties and clinical features of non-metal clasp dentures

This position paper reviews physical and mechanical properties of thermoplastic resin used for non-metal clasp dentures, and describes feature of each thermoplastic resin in clinical application of non-metal clasp dentures and complications based on clinical experience of expert panels. Since products of thermoplastic resin have great variability in physical and mechanical properties, clinicians should utilize them with careful consideration of the specific properties of each product. In general, thermoplastic resin has lower color-stability and higher risk for fracture than polymethyl methacrylate. Additionally, the surface of thermoplastic resin becomes roughened more easily than polymethyl methacrylate. Studies related to material properties of thermoplastic resin, treatment efficacy and follow-up are insufficient to provide definitive conclusions at this time. Therefore, this position paper should be revised based on future studies and a clinical guideline should be provided.     

��ȩ��֬�����ٴ�Ӧ�ú��о���չ

可摘局部义齿是牙列缺损主要的修复手段之一,目前在临床广为应用。但是,可摘局部义齿在前牙区容易暴露金属卡环而影响美观,在一定程度上制约了它的应用。20世纪90年代以来,随着缩醛树脂卡环的出现,有效地解决了暴露金属卡环的问题。本文就缩醛树脂卡环固位力的影响因素、缩醛树脂卡环的临床应用、研究现状做一综述。     

人工唾液和乳酸对Vitallium 2000钴铬钼合金卡环疲劳强度影响的研究

目的探讨人工唾液和乳酸对Vitallium 2000钴铬钼合金卡环疲劳强度的影响。方法用成品卡环蜡型制作Vitallium 2000钴铬钼合金卡环15个,分为3组,分别在空气、人工唾液和乳酸溶液中进行测试。自动记录初始载荷强度和疲劳失效前的载荷循环次数,扫描电镜分析疲劳裂纹。结果 Vitallium 2000钴铬钼合金卡环在不同测试条件下的初始载荷强度无差异(P>0.05)。在空气中的循环次数最高,在乳酸溶液中的循环次数最低。SPSS软件分析表明3组之间的疲劳强度有显著性差异(P<0.01)。结论人工唾液和乳酸溶液均使Vitallium 2000钴铬钼合金卡环的疲劳强度下降。     

T型卡环作用于烤瓷冠的固位力衰减及表面磨损观察

目的观察两种材料的T型卡环作用于烤瓷冠时,其固位力大小的变化趋势以及烤瓷冠相应表面的磨损情况。方法制作烤瓷冠标准试件及钴铬合金和纯钛的T型卡环,采用BOSE Electroforce测试仪进行15000次反复就位、脱位实验,记录分析卡环脱位力的峰值及其衰减曲线。用扫描电子显微镜观察烤瓷冠表面的磨损情况。结果两组卡环固位力衰减规律基本符合对数曲线,拟合曲线方程钴铬合金卡环为y=-5.043lnx＋51.494,纯钛卡环为y=-2.622lnx＋29.519。电镜可见钴铬合金卡环组烤瓷冠表面明显断层结构及较大面积的材料缺失;纯钛卡环组烤瓷冠材料剥脱较少,断层较薄。结论钴铬合金和纯钛的T型卡环固位力变化符合对数衰减;纯钛卡环的固位力维持优于钴铬合金卡环。对烤瓷冠表面的磨损程度,纯钛卡环明显低于钴铬合金卡环。