The effect of resin cements and primer on retentive force of zirconia copings bonded to zirconia abutments with insufficient retention

PURPOSE

The purpose of this study was to investigate the effect of resin cements and primer on the retentive force of zirconia copings bonded to zirconia abutments with insufficient retention.

MATERIALS AND METHODS

Zirconia blocks (Lava, 3M ESPE, St. Paul, MN, USA) were obtained and forty sets of zirconia abutments and copings were fabricated using CAD/CAM technology. They were grouped into 4 categories as follows, depending on the types of resin cements used, and whether the primer is applied or not:Panavia F2.0 (P), Panavia F2.0 using Primer (PRIME Plus, Bisco Inc, Schaumburg, IL, USA) (PZ), Superbond C&B (S), and Superbond C&B using Primer (SZ). For each of the groups, the cementation was conducted. The specimens were kept in sterilized water (37℃) for 24 hours. Retentive forces were tested and measured, and a statistical analysis was carried out. The nature of failure was recorded.

RESULTS

The means and standard deviations of retentive force in Newton for each group were 265.15 ± 35.04 N (P), 318.21 ± 22.24 N (PZ), 445.13 ± 78.54 N (S) and 508.21 ± 79.48 N (SZ). Superbond C&B groups (S & SZ) showed significantly higher retentive force than Panavia F2.0 groups (P & PZ). In Panavia F2.0 groups, the use of primer was found to contribute to the increase of retentive force. On the other hand, in Superbond C&B groups, the use of primer did not influence the retention forces. Adhesive failure was observed in all groups.

CONCLUSION

This study suggests that cementation of the zirconia abutments and zirconia copings with Superbond C&B have a higher retentive force than Panavia F2.0. When using Panavia F2.0, the use of primer increases the retentive force.     

Microleakage in conservative cavities varying the preparation method and surface treatment

Objective

To assess microleakage in conservative class V cavities prepared with aluminum-oxide air abrasion or turbine and restored with self-etching or etch-and-rinse adhesive systems.

Material and Methods

Forty premolars were randomly assigned to 4 groups (I and II: air abrasion; III and IV: turbine) and class V cavities were prepared on the buccal surfaces. Conditioning approaches were: groups I/III - 37% phosphoric acid; groups II/IV -self-priming etchant (Tyrian-SPe). Cavities were restored with One Step Plus/Filtek Z250. After finishing, specimens were thermocycled, immersed in 50% silver nitrate, and serially sectioned. Microleakage at the occlusal and cervical interfaces was measured in mm and calculated by a software. Data were subjected to ANOVA and Tukey’s test (α=0.05).

Results

Forty premolars were randomly assigned to 4 groups (I and II: air abrasion; III and IV: turbine) and class V cavities were prepared on the buccal surfaces. Conditioning approaches were: groups I/III - 37% phosphoric acid; groups II/IV -self-priming etchant (Tyrian-SPe). Cavities were restored with One Step Plus/Filtek Z250. After finishing, specimens were thermocycled, immersed in 50% silver nitrate, and serially sectioned. Microleakage at the occlusal and cervical interfaces was measured in mm and calculated by a software. Data were subjected to ANOVA and Tukey’s test (α=0.05).

Conclusion

Marginal seal of cavities prepared with aluminum-oxide air abrasion was different from that of conventionally prepared cavities, and the etch-and-rinse system promoted higher marginal seal at both enamel and dentin margins.     

The effect of a desensitizer and CO2 laser irradiation on bond performance between eroded dentin and resin composite

PURPOSE

This study was aimed to evaluate effect of the desensitizing pretreatments on the micro-tensile bond strengths (µTBS) to eroded dentin and sound dentin.

MATERIALS AND METHODS

Forty-two extracted molars were prepared to form a flat dentin surface, and then they were divided into two groups. Group I was stored in distilled water while group II was subjected to a pH cycling. Each group was then subdivided into three subgroups according to desensitizing pretreatment used: a) pretreatment with desensitizer (Gluma); b) pretreatment with CO₂ Laser (Ultra Dream Pluse); c) without any pretreatment. All prepared surfaces were bonded with Single Bond 2 and built up with resin composite (Filtek Z250). The micro-tensile bond test was performed. Fracture modes were evaluated by stereomicroscopy. Pretreated surfaces and bonded interfaces were characterized by scanning electron microscope (SEM). The data obtained was analyzed by two-way ANOVA (α=0.05).

RESULTS

For both sound and eroded dentin, samples treated with desensitizer showed the greatest µTBS, followed by samples without any treatment. And samples treated with CO₂ laser showed the lowest µTBS. SEM study indicated that teeth with eroded dentin appeared prone to debonding, as demonstrated by existence of large gaps between adhesive layers and dentin.

CONCLUSION

Pretreatment with Gluma increased the µTBS of Single Bond 2 for eroded and sound teeth. CO₂ laser irradiation weakened bond performance for sound teeth but had no effect on eroded teeth.     

BOND STRENGTH AND MORPHOLOGY OF ENAMEL USING SELF-ETCHING ADHESIVE SYSTEMS WITH DIFFERENT ACIDITIES

Objectives:

To assess the bond strength and the morphology of enamel after application of self-etching adhesive systems with different acidities. The tested hypothesis was that the performance of the self-etching adhesive systems does not vary for the studied parameters.

Material and methods:

Composite resin (Filtek Z250) buildups were bonded to untreated (prophylaxis) and treated (burcut or SiC-paper) enamel surfaces of third molars after application of four self-etching and two etch-and-rinse adhesive systems (n=6/condition): Clearfil SE Bond (CSE); OptiBond Solo Plus Self-Etch (OP); AdheSe (AD); Tyrian Self Priming Etching (TY), Adper Scotchbond Multi-Purpose Plus (SBMP) and Adper Single Bond (SB). After storage in water (24 h/37°C), the bonded specimens were sectioned into sticks with 0.8 mm² cross-sectional area and the microtensile bond strength was tested at a crosshead speed of 0.5 mm/min. The mean bond strength values (MPa) were subjected to two-way ANOVA and Tukey''s test (α=0.05). The etching patterns of the adhesive systems were also observed with a scanning electron microscope.

Results:

The main factor adhesive system was statistically significant (p<0.05). The mean bond strength values (MPa) and standard deviations were: CSE (20.5±3.5), OP (11.3±2.3), AD (11.2±2.8), TY (11.1±3.0), SBMP (21.9±4.0) and SB (24.9±3.0). Different etching patterns were observed for the self-etching primers depending on the enamel treatment and the pH of the adhesive system.

Conclusion:

Although there is a tendency towards using adhesive systems with simplified application procedures, this may compromise the bonding performance of some systems to enamel, even when the prismless enamel is removed.     

Effect of composite surface treatment and aging on the bond strength between a core build-up composite and a luting agent

Objective

The purpose of this study was to assess the influence of conditioning methods and thermocycling on the bond strength between composite core and resin cement.

Material and Methods

Eighty blocks (8×8×4 mm) were prepared with core build-up composite. The cementation surface was roughened with 120-grit carbide paper and the blocks were thermocycled (5,000 cycles, between 5°C and 55°C, with a 30 s dwell time in each bath). A layer of temporary luting agent was applied. After 24 h, the layer was removed, and the blocks were divided into five groups, according to surface treatment: (NT) No treatment (control); (SP) Grinding with 120-grit carbide paper; (AC) Etching with 37% phosphoric acid; (SC) Sandblasting with 30 mm SiO₂ particles, silane application; (AO) Sandblasting with 50 mm Al₂O₃ particles, silane application. Two composite blocks were cemented to each other (n=8) and sectioned into sticks. Half of the specimens from each block were immediately tested for microtensile bond strength (µTBS), while the other half was subjected to storage for 6 months, thermocycling (12,000 cycles, between 5°C and 55°C, with a dwell time of 30 s in each bath) and µTBS test in a mechanical testing machine. Bond strength data were analyzed by repeated measures two-way ANOVA and Tukey test (α=0.05).

Results

The µTBS was significantly affected by surface treatment (p=0.007) and thermocycling (p=0.000). Before aging, the SP group presented higher bond strength when compared to NT and AC groups, whereas all the other groups were statistically similar. After aging, all the groups were statistically similar. SP submitted to thermocycling showed lower bond strength than SP without thermocycling.

Conclusion

Core composites should be roughened with a diamond bur before the luting process. Thermocycling tends to reduce the bond strength between composite and resin cement.     

CYTOTOXICITY EVALUATION OF TWO ROOT CANAL SEALERS AND A COMMERCIAL CALCIUM HYDROXIDE PASTE ON THP1 CELL LINE BY TRYPAN BLUE ASSAY

Objective:

The aim of this investigation was to evaluate the cytotoxicity of two brands of root canal sealers, epoxy-resin based and zinc oxide-eugenol based, and one commercial calcium hydroxide paste on a monocyte cell line THP-1.

Material and methods:

Undiluted (crude extract) and diluted extracts to 10%, 1%, 0.1%, 0.01%, 0.001% and 0.0001% of the sealers were tested for cytotoxicity to THP-1 cells using the trypan blue assay. Extracts were obtained according to ISO standard. Data were analyzed statistically by the Kruskal-Wallis and Mann-Whitney tests at 5% significance level.

Results:

Crude extract of AH Plus and Fill Canal killed approximately 90% of THP-1 cells versus 36% of THP-1 cells killed by L&C crude extract (p<0.05). Ten-fold dilutions of L&C, Fill Canal and AH Plus killed 24, 35 and 61% of THP-1 cells (p<0.05), respectively. Dilutions lesser than 1% caused minimal cell death as compared to the control groups (p>0.05), except for L&C 1% extract.

Conclusions:

The results revealed that the L&C paste crude extract was less cytotoxic to THP-1 cells than AH Plus or Fill Canal crude extracts.     

Effect of the application time of phosphoric acid and self-etch adhesive systems to sclerotic dentin

Objectives:

To evaluate the effect of application time on the resin-dentin bond strength (µTBS) and etching pattern of adhesive systems applied on sclerotic dentine.

Material and Methods:

A total of forty-two bovine incisors had their roots removed. The 1-step self-etch GO (SDI), the 2-step self-etch Adper SE Bond (3MESPE) and the 35% phosphoric acid (3MESPE) from the 2-step etch-and-rinse Adper Single Bond 2 (3MESPE) were applied on the bovine incisal surfaces according to the manufacturer''s instructions or duplicating the recommended conditioning time. After adhesive application, thirty teeth were restored with composite resin, stored for 24 h in distilled water at 37º C, and sectioned into resin-dentin bonded sticks (0.8 mm²⁾ and tested according to the µTBS at 0.5 mm/min. The etching pattern of the remaining twelve teeth (n=4 for each material) was examined under scanning electron microscopy. Each tooth was divided into a buccal-to-lingual direction into three thirds, and each third randomly assigned to the groups: control (no treatment), according to the manufacturers'' instructions and duplicating the recommended application time. The µTBS and the relative percentage of the tubule area opening were evaluated by two-way repeated measures ANOVA and Tukey''s tests (α=0.05).

Results:

The duplication of the conditioning time favored only the GO adhesive (p<0.05). Both application methods significantly increased the tubule area opening (p<0.05) compared to the controls.

Conclusions:

The efficacy of duplicating the conditioning time was only effective for the 1-step self-etch adhesive system tested.     

SHEAR BOND STRENGTH OF METALLIC BRACKETS: INFLUENCE OF SALIVA CONTAMINATION

Objective:

To evaluate the influence of saliva contamination on shear bond strength and the bond failure pattern of 3 adhesive systems (Transbond XT, AdheSE and Xeno III) on orthodontic metallic brackets bonded to human enamel.

Material and Methods:

Seventy-two permanent human molars were cut longitudinally in a mesiodistal direction, producing seventy-two specimens randomly divided into six groups. Each system was tested under 2 different enamel conditions: no contamination and contaminated with saliva. In T, A and X groups, the adhesive systems were applied to the enamel surface in accordance with manufacturer''s instructions. In TS, AS and XS groups, saliva was applied to enamel surface followed by adhesive system application. The samples were stored in distilled water at 37°C for 24 h, and then tested for shear bond strength in a universal testing machine (Emic, DL 2000) running at a crosshead speed of 1 mm/min. After bond failure, the enamel surfaces were observed under an optical microscope at 40x magnification.

Results:

The control and contaminated groups showed no significant difference in shear bond strength for the same adhesive system. However, shear bond strength of T group (17.03±4.91) was significantly higher than that of AS (8.58±1.73) and XS (10.39±4.06) groups (p<0.05). Regarding the bond failure pattern, TS group had significantly higher scores of no adhesive remaining on the tooth in the bonding area than other groups considering the adhesive remnant index (ARI) used to evaluate the amount of adhesive left on the enamel.

Conclusion:

Saliva contamination showed little influence on the 24-h shear bond strength of orthodontic brackets.     

DESENSITIZING BIOACTIVE AGENTS IMPROVES BOND STRENGTH OF INDIRECT RESIN-CEMENTED RESTORATIONS: PRELIMINARY RESULTS

Objective:

The aim of this study was to assess the bond strength of indirect composite restorations cemented with a resin-based cement associated with etch-and-rinse and self-etching primer adhesive systems to dentin treated or not with a bioactive material.

Materials and Method:

Twenty bovine incisor crowns had the buccal enamel removed and the dentin ground flat. The teeth were assigned to 4 groups (n=5): Group I: acid etching + Prime & Bond NT (Dentsply); Group II: application of a bioactive glass (Biosilicato®)+ acid etching + Prime & Bond NT; Group III: One-up Bond F (J Morita); Group IV: Biosilicato® + One-up Bond F. Indirect composite resin (Artglass, Kulzer) cylinders (6x10mm) were fabricated and cemented to the teeth with a dualcure resin-based cement (Enforce, Dentsply). After cementation, the specimens were stored in artificial saliva at 37^oC for 30 days and thereafter tested in tensile strength in a universal testing machine (EMIC) with 50 kgf load cell at a crosshead speed of 1 mm/min. Failure modes were assessed under scanning electron microscopy. Data were analyzed statistically by ANOVA and Tukey''s test (95% level of confidence).

Results:

Groups I, II and III had statistically similar results (p>0.05). Group IV had statistically significant higher bond strength means (p<0.05) than the other groups. The analysis of the debonded surfaces showed a predominance of adhesive failure mode for Group III and mixed failure mode for the other groups.

Conclusion:

The use of desensitizing agent did not affect negatively the bonding of the indirect composite restorations to dentin, independently of the tested adhesive systems.     

ADHESIVES WITH DIFFERENT PHS: EFFECT ON THE MTBS OF CHEMICALLY ACTIVATED AND LIGHT-ACTIVATED COMPOSITES TO HUMAN DENTIN

Purpose:

To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites.

Material and Method:

Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37°C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm². Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min⁻¹). Data were analyzed using two-way ANOVA and Tukey’s tests (p<0.05).

Results:

The anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7±7.1ª; PB+Z100 = 23.8±5.7ª). However, with use of the chemically activated composite (B2B), PB (7.8±3.6^b MPa) showed significantly lower dentin bond strengths than OS (32.2±7.6ª).

Conclusion:

The low pH of the adhesive system can affect the bond of chemically activated composite to dentin. On the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.     

Shear bond strength of one-step self-etch adhesives with different co-solvent ingredients to dry or moist dentin

Objective

To evaluate the shear bond strength of one-step self-etch adhesives with different co-solvent ingredients to dry or moist dentin.

Materials and methods

A total of 60 extracted teeth were used in this study, and were divided according to the adhesive systems and dentin conditions into 6 groups of 10 teeth each [Xeno III – dry dentin, Xeno III – moist dentin, Adper Prompot L-Pop – dry dentin, Adper Prompot L-Pop – moist dentin, iBond – dry dentin, and iBond – moist dentin]. Resin composite cylinder was built up on each specimen, and then thermocycled. A shear load was applied to the specimens using universal testing (Instron machine) at a cross-head speed of 0.5 mm/min until failure occurred. Data were statistically analyzed by one-way ANOVA and Bonferroni multiple comparison test at 95% confidence level.

Results and conclusion

Based on the findings of this study: The highest mean shear bond strength to dry dentin was seen when Xeno III containing ethanol co-solvent ingredient was used. The highest mean shear bond strength to moist dentin was seen when iBond which contains acetone co-solvent ingredient was used. In the absence of a co-solvent ingredient in self-etch adhesive (Adper Prompot L-Pop), the mean shear bond strengths to dry and moist dentin were low with no significant difference between them.     

Influence of sodium hypochlorite and EDTA on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials.

Objective

The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (eDTA).

Material and Methods

Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% eDTA. The specimens received the self-etching adhesive system (XeNO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test.

Results

Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/ F=22.5763). The application of 1% NaOCl/17% eDTA resulted in statistically similar µTBS to the control group.

Conclusions

None of the irrigants affected negatively the µTBS of XeNO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% eDTA produced similar bond strength to that of untreated dentin.     

Evaluating resin-enamel bonds by microshear and microtensile bond strength tests: effects of composite resin

Objectives

The aims of this study were to evaluate the effect of resin composite (Filtek Z250 and Filtek Flow Z350) and adhesive system [(Solobond Plus, Futurabond NR (VOCO) and Adper Single Bond (3M ESPE)] on the microtensile (µTBS) and microshear bond strength (µSBS) tests on enamel, and to correlate the bond strength means between them.

Material and methods

Thirty-six extracted human molars were sectioned to obtain two tooth halves: one for µTBS and the other one for µSBS. Adhesive systems and resin composites were applied to the enamel ground surfaces and light-cured. After storage (37ºC/24 h) specimens were stressed (0.5 mm/ min). Fracture modes were analyzed under scanning electron microscopy. The data were analyzed using two-way ANOVA and Tukey''s test (α=0.05).

Results

The correlation between tests was estimated with Pearson''s product-moment correlation statistics (α =0.05). For both tests only the main factor resin composite was statistically significant (p<0.05). The correlation test detected a positive (r=0.91) and significant (p=0.01) correlation between the tests.

Conclusions

The results were more influenced by the resin type than by the adhesives. Both microbond tests seem to be positive and linearly correlated and can therefore lead to similar conclusions.     

EVALUATION OF INTERNAL ADAPTATION OF CLASS V RESIN COMPOSITE RESTORATIONS USING THREE TECHNIQUES OF POLYMERIZATION

Objective:

The purpose of this in vitro study was to evaluate the internal adaptation of Class V composite restorations to the cavity walls using three different techniques of polymerization.

Methods:

Standard cavities were prepared on the buccal and lingual surfaces of 24 extracted human third molars with margins located above and below the cementoenamel junction. Restorations were placed in one increment using two restorative systems: 3M Filtek A110/ Single Bond (M) and 3M Filtek Z250/ Single Bond (H) in the same tooth, randomly in the buccal and lingual surfaces. Resin composites were polymerized using three techniques: Group 1 – Conventional (60 s - 600 mW/cm²); Group 2 – Soft-start (20 s – 200 mW/cm², 40 s - 600 mW/cm²); Group 3 – Pulse Activation (3 s - 200 mW/cm², 3-min hiatus, 57 s - 600 mW/cm²). Buccolingual sections were polished, impressions taken and replicated. Specimens were assessed under scanning electron microscopy up to X1000 magnification. Scores were given for presence or absence of gaps (0 – no gap; 1 – gap in one wall; 2 – gap in two walls; 3 – gap in three walls).

Results:

The mean scores of the groups were (±SD) were: G1M–3.0 (± 0.0); G2M–2.43 (± 0.8); G3M– 1.71 (± 0.9); G1H– 2.14 (± 1.2); G2H- 2.00 (± 0.8); G3H- 1.67 (± 1.1). Data were analyzed using Kruskal-Wallis and Dunnet’s tests. No statistically significant difference (p>0.05) was found among groups. Gaps were observed in all groups.

Conclusions:

The photocuring technique and the type of resin composite had no influence on the internal adaptation of the material to the cavity walls. A positive effect was observed when the slow polymerization techniques were used.     

WATER SORPTION AND SOLUBILITY OF DIFFERENT CALCIUM HYDROXIDE CEMENTS

Objectives:

Calcium hydroxide cements have been largely used in deep cavities due to their abilities to stimulate dentin formation. However, their resistance can be relatively low and their solubility relatively high, in many instances. This study evaluated water sorption and solubility of different calcium hydroxide cements, in order to show alterations that may reduce their effectiveness.

Material and methods:

Five discs (20 mm in diameter and 1.5 mm thick) of three different materials (Biocal^®, Dycal^® and Hidro C^®) were prepared with the aid of a ring-shaped metallic matrix. After being stored at 37°C for 24 h, the discs were weighed on a precision weight scale, dehydrated and weighed again. Immediately after weighing, discs were stored for a week in 50 mL of distilled water at 37°C and, then, weighed again, dehydrated and submitted to a new weighing. The loss of soluble material and its water sorption was obtained from the difference between the initial and the final dry mass of each disc, after 1 week of immersion in water. Data were analyzed for significant differences by two-way ANOVA and Tukey''s test (p<0.05).

Results:

Mean water sorption values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal^® (0.006 ± 0.001 / 2.15); Dycal^® (0.016 ± 0.004 / 5.49); and Hidro C^® (0.025 ± 0.003 / 8.27). Mean solubility values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal^® (0.002 ± 0.001 / 0.72); Dycal^® (0.013 ± 0.004 / 4.21); and Hidro C^® (0.023 ± 0.004 / 7.65).

Conclusions:

Biocal^® absorbed less water and was less soluble than the other evaluated cements; Hidro C^® exhibited the highest water sorption and solubility values; and there were significant differences among all evaluated experimental groups.     

Bond strength of three luting agents to zirconia ceramic - influence of surface treatment and thermocycling

Objective

This in vitro study aimed to evaluate the influence of different surface treatments, 3 luting agents and thermocycling on microtensile bond strength (µTBS) to zirconia ceramic.

Material and Methods

A total of 18 blocks (5x5x4 mm) were fabricated from zirconia ceramic (ICE Zirkonia) and duplicated into composite blocks (Alphadent). Ceramic blocks were divided into 3 groups (n=6) according to the following surface treatments: airborne-particle abrasion (AA), silica-coating, (SC) (CoJet) and silica coating followed by silane application (SCSI) (ESPE Sil). Each group was divided into 3 subgroups (n=2) according to the 3 luting agents used. Resin-modified glass-ionomer cement (RMGIC, Ketac Cem Plus), self-adhesive resin cement (UN, RelyX Unicem) and adhesive resin cement (ML, MultiLink Automix) were used for bonding composite and zirconia blocks. Each bonding assembly was cut into microbars (10 mm long and 1±0.1 mm²). Seven specimens of each subgroup were stored in water bath at 37ºC for 1 week. The o ther 7 specimens were stored in water bath at 37ºC for 30 days then thermocycled (TC) for 7,500 cycles. µTBS values were recorded for each specimen using a universal testing machine. Statistical analyses were performed using a 3-way ANOVA model followed by serial 1-way ANOVAs. Comparison of means was performed with Tukey''s HSD test at (α=0.05).

Results

µTBS ranged from 16.8 to 31.8 MPa after 1 week and from 7.3 to 16.4 MPa after 30 days of storage in water and thermocycling. Artificial aging significantly decreased µTBS (p<0.05). Considering surface treatment, SCSI significantly increased µTBS (p<0.05) compared to SC and AA. Resin cements (UN and ML) demonstrated significantly higher µTBS (p<0.05) compared to RMGIC cement.

Conclusions

Silica coating followed by silane application together with adhesive resin cements significantly increased µTBS, while thermocycling significantly decreased µTBS.     

Comparative evaluation of the calcium release from mineral trioxide aggregate and its mixture with glass ionomer cement in different proportions and time intervals – An in vitro study

Background

Addition of glass ionomer cement (GIC) has been suggested to improve the setting time and handling characteristics of mineral trioxide aggregate (MTA). This study evaluated the effect of adding GIC to MTA in terms of calcium release, an issue that has not been previously studied.

Materials and methods

The study comprised four groups with five samples each: a control group of MTA alone and experimental groups I (1MTA:1GIC), II (2MTA:1GIC), and III (1MTA:2GIC) based on the mixture of MTA and GIC powders in the respective proportions by volume. Calcium release from the samples was measured by atomic absorption spectrophotometry at 15 min, 6 h, 24 h, and 1 week after setting. The level of statistical significance was set at p < 0.05.

Results

Groups I (1MTA:1GIC) and III (1MTA:2GIC) released significantly less calcium than the control group at all time periods, except at 15 min for group I. Group II (2MTA:1GIC) showed no significant difference in calcium release compared to the control at any time period. Group II exhibited greater calcium release than group I or III at all time periods, with significant differences between groups I and II at 1 week and between groups I and III at 24 h and 1 week. There were no statistical differences in calcium release between groups I and III.

Conclusions

Adding GIC to improve the setting time and handling properties of the MTA powder can be detrimental to the calcium-releasing ability of the resultant mixture, depending on the proportion of GIC added. Adding MTA and GIC at a proportion of 2:1 by volume did not impact calcium release from the mixture. These findings should be verified through further clinical studies.     

Effect of natural gel product on bovine dentin erosion in vitro

Objective

To evaluate the efficacy of Neem (Azadirachta indica) experimental gel for the prevention of erosive wear on bovine dentin, in vitro.

Material and Methods

One hundred dentin blocks were allocated into 5 experimental groups (20 samples each): C (control group, without gel); CG (control group, only base gel); F (fluoride gel, 1.23% NaF; pH 4.1, Dentsply; Brazil); N (Neem gel, 10% neem extract; pH 4.1, manipulation); NF (Neem+fluoride gel, 10% Neem extract and 1.23% NaF; pH 4.1, manipulation). The blocks were stored in artificial saliva for 24 hours. After this, they were submitted to six alternating re- and demineralization cycles. The blocks were analyzed for wear (profilometry). The results were submitted to statistical analysis by ANOVA and Tukey tests (P<0.05).

Results

The mean wear (±SD, µm) was shown as follows in groups: C (13.09±0.99), CG (10.60±1.99), F (10.90±1.44), N (12.68±1.13) and NF (10.84±1.65). All gels showed some preventive action when compared with control group. However, significant differences were found only between Neem+fluoride gel and fluoride gel.

Conclusion

A single application of a neem-containing fluoride gel reduced dentin erosion, thus it is a possible alternative in reducing dental wear. Further research should investigate the action mechanism and the synergism between them.     

Evaluation of bond strength of silorane and methacrylate based restorative systems to dentin using different cavity models

Objective

The aim of this in vitro study was to evaluate the microtensile bond strength (µTBS) to dentin of two different restorative systems: silorane-based (P90), and methacrylate-based (P60), using two cavity models.

Material and Methods

Occlusal enamel of 40 human third molars was removed to expose flat dentin surface. Class I cavities with 4 mm mesial-distal width, 3 mm buccal-lingual width and 3 mm depth (C-factor=4.5) were prepared in 20 teeth, which were divided into two groups (n=10) restored with P60 and P90, bulk-filled after dentin treatment according to manufacturer''s instructions. Flat buccal dentin surfaces were prepared in the 20 remaining teeth (C-factor=0.2) and restored with resin blocks measuring 4x3x3 mm using the two restorative systems (n=10). The teeth were sectioned into samples with area between 0.85 and 1.25 mm² that were submitted to µTBS testing, using a universal testing machine (EMIC) at speed of 0.5 mm/min. Fractured specimens were analyzed under stereomicroscope and categorized according to fracture pattern. Data were analyzed using ANOVA and Tukey Kramer tests.

Results

For flat surfaces, P60 obtained higher bond strength values compared with P90. However, for Class I cavities, P60 showed significant reduction in bond strength (p<0.05). No statistical difference between restorative systems was shown for Class I cavity model (p>0.05), or between Class I Cavity and Flat Surface group, considering P90 restorative system (p>0.05). Regarding fracture pattern, there was no statistical difference among groups (p=0.0713) and 56.3% of the fractures were adhesive.

Conclusion

It was concluded that methacrylate-based composite µTBS was influenced by cavity models, and the use of silorane-based composite led to similar bond strength values compared to the methacrylate-based composite in cavities with high C-factor.     

Bond strength to root dentin and fluid filtration test of AH Plus/gutta-percha,EndoREZ and RealSeal systems

Objectives

To investigate the bond strength and seal ability produced by AH Plus/gutta-percha, EndoREZ and RealSeal systems to root canal dentin.

Material and Methods

Sixty extracted single-root human teeth, instrumented manually to size 40, were divided into three groups (n=20) according to the sealer used; G1: AH Plus, G2: EndoREZ, and G3: RealSeal sealers. After filling using the lateral condensation technique, each sealer group was randomly divided into two subgroups according to the tests applied (n=10 for µPush-out test and n=10 for fluid filtration test). A fluid filtration method was used for quantitative evaluation of apical leakage. Four 1-mm-thick slices (cervical and medium level) were obtained from each root sample and a µPush-out test was performed. Failure modes were examined under microscopy at 40x, and a one-way ANOVA was applied to analyze the permeability. Non-parametrical statistics for related (Friedman''s and Wilcoxon''s rank tests) or unrelated samples (Kruskal-Wallis'' and Mann-Whitney''s tests) allowed for comparisons of µPush-out strength values among materials at the different levels. Statistical significance was accepted for p values <.05.

Results

There are no significant differences among fluid filtration of the three sealers. The sealer/core material does not significantly influence the µPush-out bond strength values (F=2.49; p=0.10), although statistically significant differences were detected with regard to root level (Chi²=23.93; p<0.001). AH Plus and RealSeal obtained higher bond strength to intraradicular dentin in the medium root slices.

Conclusions

There are no significant differences between the permeability and global µPush-out bond strength to root canal dentin achieved by AH Plus/gutta-percha, EndoREZ and RealSeal systems.