Glass Fibers Reinforced Concrete: Overview on Mechanical,Durability and Microstructure Analysis

Prior studies in the literature show promising results regarding the improvements in strength and durability of concrete upon incorporation of glass fibers into concrete formulations. However, the knowledge regarding glass fiber usage in concrete is scattered. Moreover, this makes it challenging to understand the behavior of glass fiber-reinforced concrete. Therefore, a detailed review is required on glass fiber-reinforced concrete. This paper provides a compressive analysis of glass fiber-reinforced composites. All-important properties of concrete such as flowability, compressive, flexural, tensile strength and modulus of elasticity were presented in this review article. Furthermore, durability aspects such as chloride ion penetration, water absorption, ultrasonic pulse velocity (UPV) and acid resistance were also considered. Finally, the bond strength of the fiber and cement paste was examined via scanning electron microscopy. Results indicate that glass fibers improved concrete’s strength and durability but decreased the concrete’s flowability. Higher glass fiber doses slightly decreased the mechanical performance of concrete due to lack of workability. The typical optimum dose is recommended at 2.0%. However, a higher dose of plasticizer was recommended for a higher dose of glass fiber (beyond 2.0%). The review also identifies research gaps that should be addressed in future studies.     

Mechanical Experiments on Concrete with Hybrid Fiber Reinforcement for Structural Rehabilitation

Reinforced concrete is used in the construction of bridges, buildings, retaining walls, roads, and other engineered structures. Due to seismic activities, a lot of structures develop seismic cracks. The rehabilitation of such structures is necessary for public safety. The overall aim of this research study was to produce a high-performance hybrid fiber-reinforced concrete (HPHFRC) with enhanced properties as compared to plain high-performance concrete and high-performance fiber-reinforced concrete (HPFRC) for the rehabilitation of bridges and buildings. Kevlar fibers (KF) and glass fibers (GF) with lengths of 35 mm and 25 mm, respectively, were added and hybridized to 1.5% by mass of cement to create hybrid fiber-reinforced concrete mixes. Eight mixes were cast in total. The compressive strength (f′_c), flexural strength (f_r), splitting tensile strength (f_s), and other mechanical properties, i.e., energy absorption and toughness index values, were enhanced in HPHFRC as compared to CM and HPFRC. It was found that the concrete hybridized with 0.75% KF and 0.75% GF (HF-G 0.75 K 0.75) had the most enhanced overall mechanical properties, illustrating its potential to be utilized in the rehabilitation of bridges and structures.     

A Study on the Mechanical Characteristics of Glass and Nylon Fiber Reinforced Peach Shell Lightweight Concrete

In the current study, the utilization of glass and nylon fibers in various percentages are added to enhance the mechanical performance of peach shell lightweight concrete. Glass and nylon fibers were added at 2%, 4%, 6%, and 8% by cement weight. The results showed that, as we added the glass and nylon fibers, the density of peach shell concrete was reduced by 6.6%, and the compressive, split tensile and flexural strength were enhanced by 10.20%, 60.1%, and 63.49%. The highest strength that was obtained in compressive, split tensile, and flexural strength at 56 days was 29.4 MPa, 5.2 MPa, and 6.3 MPa, respectively, with 6% of glass fiber in peach shell concrete. Mechanical test results showed that post-failure toughness and modulus of elasticity of peach shell concrete is enhanced with the utilization of fibers. To verify our lab results, a statistical analysis, such as response surface methodology, was performed to make a statistical model, it was confirmed by both lab results and statistical analysis that the mechanical performance of peach shell concrete could be significantly improved by adding glass fibers as compared to nylon fibers. With the use of fibers, the water absorption and porosity were slightly increased. Hence, the glass and nylon fibers can be used to improve the peach shell concrete mechanical properties to make concrete eco-friendly, sustainable, and lightweight.     

Flexural Tensile Strength of Concrete with Synthetic Fibers

Fiber reinforcement is currently most often used in floors, railway sleepers, prefabricated structural elements such as slabs, beams and tanks, and in small architecture elements. Designing elements or structures made of fiber-reinforced concrete requires knowledge of its basic mechanical parameters. In the case of concretes with metallic fibers, the literature can find many tests and standard guidelines regarding compressive, flexural, tensile strength and fracture energy. The properties of concretes with non-metallic fibers are slightly less recognized, especially concretes with new types of polymer fibers. Additionally, the lack of standardized methods of testing concrete with polymer fibers make their application much more difficult. In the article, the possibility of using the EN 14651 standard to assess the flexural tensile strength of concrete with the addition of 2.0 and 3.0 kg/m³ of synthetic fibers with different geometry and form was presented. There was a 5.5–13.5% increase in the flexural tensile strength depending on the mixture type. Moreover, in the case of fiber-reinforced concretes, the ductility was enhanced and the samples were characterized by significant residual flexural tensile strengths. Additionally, from the workability tests it was concluded that after the incorporation of fibers, the consistency class decreased by one, two or three. Nevertheless, the compressive strengths of concrete with and without fibers were very similar to each other, and varied from 58.05 to 61.31 MPa. Moreover, it was concluded that results obtained from three-point bending tests significantly differed from empirical formulas for the calculation of the flexural tensile strength of fiber-reinforced concretes with dispersed steel fibers present in the literature. As a result, the new formula determined by the authors was proposed for concrete with polymer fibers with a nominal fiber content ≤1.0% and slenderness of up to 200. It must be mentioned that the formula gave a very good agreement with studies presented in different literature positions. In addition, an attempt was made to evaluate the strengths of tested mixes in accordance with the Model Code 2010. However, it occurred that the proposed fiber-reinforced concrete mixtures would not be able to replace traditional reinforcement in a form of steel bars. Furthermore, in uniaxial tensile tests, it was not possible to determine the σ–w graphs, and received results for maximum tensile strength did not show the clear influence of fibers incorporation on concrete. Then, the fracture energy enhancement (from about 16 to 22 times) and dependencies: crack mouth opening displacement–deflection; crack mouth opening displacement–crack tip opening displacement; and crack tip opening displacement–deflection were analyzed. Finally, the results from flexural tensile tests were compared with measurements of the surface displacement field obtained through the Digital Image Correlation technique. It was concluded that this technique can be successfully used to determine the crack mouth and crack tip opening displacements with very high accuracy.     

The Influence of Short Coir,Glass and Carbon Fibers on the Properties of Composites with Geopolymer Matrix

The aim of the article is to analyze the influence of short coir, glass and carbon fiber admixture on the mechanical properties of fly ash-based geopolymer, such as: flexural and compressive strength. Glass fiber and carbon fibers have been chosen due to their high mechanical properties. Natural fibers have been chosen because of their mechanical properties as well as for the sake of comparison between their properties and the properties of the artificial ones. Fourth series of fly ash-based geopolymers for each fiber was cast: 1, 2, and 5% by weight of fly ash and one control series without any fibers. Each series of samples were tested on flexural and compressive strength after 7, 14, and 28 days. Additionally, microstructural analysis was carried out after 28 days. The results have shown an increase in compressive strength for composites with fibers—an improvement in properties between 25.0% and 56.5% depending on the type and amount of fiber added. For bending strength, a clear increase in the strength value is visible for composites with 1 and 2% carbon fibers (62.4% and 115.6%). A slight increase in flexural strength also occurred for 1% addition of glass fiber (4.5%) and 2% addition of coconut fibers (5.4%). For the 2% addition of glass fibers, the flexural strength value did not change compared to the value obtained for the matrix material. For the remaining fiber additions, i.e., 5% glass fiber as well as 1 and 5% coconut fibers, the flexural strength values deteriorated. The results of the research are discussed in a comparative context and the properties of the obtained composites are juxtaposed with the properties of the standard materials used in the construction industry.     

Effects of Steel Fiber and Specimen Geometric Dimensions on the Mechanical Properties of Ultra-High-Performance Concrete

Ultra-high-performance concrete (UHPC) is an advanced concrete with superior mechanical strength, ductility and durability properties. However, the influence of steel fiber on its constitutive laws and the specimen geometric dimension effect on its strength had not been paid enough attention. To investigate the effect of steel fibers on the properties of UHPC, specimens with different fiber volume contents and fiber types were tested. Meanwhile, the mechanical properties of UHPC at different ages from 3 days to 28 days were conducted. Moreover, specimens with various geometric dimensions were also prepared to study the effect of specimen geometric dimensions (dog-bone-shaped, prism and cylinder specimens) on the properties of UHPC. The results indicated that elastic modulus, tensile peak stress and the corresponding strain increased as the fiber volume content and curing age increased. Specimens with hooked-end fibers exhibited better tensile performance than those with straight fibers. Furthermore, different geometric dimensions of specimens significantly influenced the tensile properties of UHPC. Based on the experimental results, conversion factors were suggested for the transformation of strength obtained from specimens with different geometric dimensions to reference specimens. In addition, both compressive and tensile constitutive laws were proposed to generate the stress–strain relationship of UHPC.     

An Investigation of the Properties of Expanded Polystyrene Concrete with Fibers Based on an Orthogonal Experimental Design

Expanded polystyrene (EPS) concrete is commonly used as the core material of commercial sandwich panels (CSPs). It is environmentally friendly and lightweight but has poor strength. Adding fibers can improve the microstructure of EPS concrete and reduce the weakening effect of EPS beads on the mechanical properties of concrete. An orthogonal experimental design (OED) was used in this paper to analyze the influence of length and content of polypropylene fiber (PF), glass fiber (GF), and carbon fiber (CF) on the physical and mechanical properties and micromorphology of EPS concrete. Among them, CFs have the most apparent impact on concrete and produce the most significant improvements in all properties. According to the requirements of the flexural performance of CSPs, the splitting tensile strength was taken as the optimization index, and the predicted optimal combination (OC) of EPS concrete with fibers was selected. The variations in the material properties, mechanical properties, and microstructure with age were analyzed. The results show that with increasing age, the dry density, compressive strength, and splitting tensile strength of concrete are markedly improved relative to those of the CSP core material and the control case (CC), and even the degree of hydration is improved.     

A Comparative Study on the Shear Behavior of UHPC Beams with Macro Hooked-End Steel Fibers and PVA Fibers

Structural members made of ultra-high-performance concrete (UHPC) have been attractive to engineers and researchers due to their superior mechanical properties and durability. However, existing studies were focused on the behavior of UHPC members reinforced with micro straight steel fibers at a volume fraction between 1 and 3%. There is a lack of studies on the influence of different types and amounts of fibers on the shear behavior of UHPC structural members. The objective of the study was to experimentally investigate the shear behavior of UHPC beams with macro hooked-end steel (MHS) fibers and polyvinyl alcohol (PVA) fibers, which are two of the most used fibers for high-performance fiber-reinforced cementitious composites. The shear behavior of ten large-scale non-prestressed UHPC beams was studied. The experimental parameters included the shear span-to-effective depth ratio, the fiber volume fraction, and the type of fibers. It was found that both MHS fibers and PVA fibers were effective in enhancing the shear performance of the UHPC beams whether the shear transfer mechanism was governed by arch action or beam action. Moreover, the measurement results of the average crack spacing imply the distinct difference in the fiber bridging effects of the MHS fibers and PVA fibers in the UHPC beams.     

The Effect of Steel and Basalt Fibers on the Shear Behavior of Double-Span Fiber Reinforced Concrete Beams

This study investigates the effects of adding different types of fibers to concrete mixes on the shear behavior of double-span fiber-reinforced concrete beams with or without shear reinforcement. As a part of the experimental study, a total of twenty-seven natural-scale double-span beams were tested. The beams, made of concrete with steel or basalt fiber, with fiber dosages of 78.5 and 5 kg/m³, were tested under shear force. The three tested series consisted of three beams with dimensions of 120 × 300 × 4150 mm, with various numbers of stirrups and contents of fiber reinforcement. During the tests, the shear capacity of the elements was determined. The values of support reactions, deflection in the middle of the span of both beam spans, deformations on the surface of the concrete member in the middle of the span in the compressive and tensile zone, and cracking (crack development and crack width) were also measured. The beams were tested using a digital image correlation (DIC) technique. Test results show that shear capacity increases in beams made of concrete with steel (1.87) or basalt fibers (1.23). Moreover, the failure mode changes from shear (brittle) to flexure-shear (less brittle). The experimental shear capacity of beams was compared with the theoretical values predicted by different design codes, i.e., fib Model Code 2010 and RILEM TC 162-TDF 2003. The results show that all the design codes underestimate the contribution of fiber-reinforced concrete beams to shear resistance and greatly overestimate the contribution of shear reinforcement.     

Comparison of Hook and Straight Steel Fibers Addition on Malaysian Fly Ash-Based Geopolymer Concrete on the Slump,Density, Water Absorption and Mechanical Properties

Geopolymer concrete has the potential to replace ordinary Portland cement which can reduce carbon dioxide emission to the environment. The addition of different amounts of steel fibers, as well as different types of end-shape fibers, could alter the performance of geopolymer concrete. The source of aluminosilicate (fly ash) used in the production of geopolymer concrete may lead to a different result. This study focuses on the comparison between Malaysian fly ash geopolymer concrete with the addition of hooked steel fibers and geopolymer concrete with the addition of straight-end steel fibers to the physical and mechanical properties. Malaysian fly ash was first characterized by X-ray fluorescence (XRF) to identify the chemical composition. The sample of steel fiber reinforced geopolymer concrete was produced by mixing fly ash, alkali activators, aggregates, and specific amounts of hook or straight steel fibers. The steel fibers addition for both types of fibers are 0%, 0.5%, 1.0%, 1.5%, and 2.0% by volume percentage. The samples were cured at room temperature. The physical properties (slump, density, and water absorption) of reinforced geopolymer concrete were studied. Meanwhile, a mechanical performance which is compressive, as well as the flexural strength was studied. The results show that the pattern in physical properties of geopolymer concrete for both types of fibers addition is almost similar where the slump is decreased with density and water absorption is increased with the increasing amount of fibers addition. However, the addition of hook steel fiber to the geopolymer concrete produced a lower slump than the addition of straight steel fibers. Meanwhile, the addition of hook steel fiber to the geopolymer concrete shows a higher density and water absorption compared to the sample with the addition of straight steel fibers. However, the difference is not significant. Besides, samples with the addition of hook steel fibers give better performance for compressive and flexural strength compared to the samples with the addition of straight steel fibers where the highest is at 1.0% of fibers addition.     

Mechanical Properties of Hybrid Fiber Reinforced Rubber Concrete

Orthogonal experiments were designed for hybrid fiber rubber concrete (HFRC). The mechanical properties of HFRC were tested and compared with ordinary concrete. The effects of basalt fiber volume ratio (V_BF), PVA fiber volume ratio (V_PF) and rubber volume ratio (V_R) on the compressive strength, splitting tensile strength and flexural strength of HFRC were analyzed. The results show that the strength of HFRC is the best when the volume ratio of basalt fiber is 0.3%, the volume ratio of PVA fiber is 0.2% and the volume ratio of rubber is 5%. Basalt fiber has the greatest influence on the strength of HFRC. The strength of HFRC mixed with hybrid fiber is greatly improved, which reflects the good fiber “positive hybrid effect”. With the increase of rubber volume ratio, the strength of HFRC decreases gradually. With the help of SEM and EDS, the toughening and cracking resistance mechanism of the fiber to HFRC was analyzed. Finally, the strength of HFRC was predicted by model.     

Mechanical Properties and Axial Compression Deformation Property of Steel Fiber Reinforced Self-Compacting Concrete Containing High Level Fly Ash

The cement industry has brought serious environmental pollution problems. In the background of ecological civilization, accelerating rational use of waste resources plays an important role in protecting the environment. In this study, self-compacting concrete (SCC) is prepared using fly ash and lime powder as supplementary cementitious materials by replacing 50%, 60%, and 70% of ordinary Portland cement. By systematically analyzing the influence of the fly ash replacement rate on the workability and mechanical properties of SCC, steel-fiber-reinforced SCC containing 60% fly ash is chosen for further study, and steel fiber is added at the percentages of 0.25%, 0.50%, 0.75%, and 1.00%. The performances in fresh and hardened states are investigated in terms of workability, compressive strength, splitting tensile strength, flexural strength, and axial compression deformation property. The obtained outcomes indicate that although the incorporation of fly ash can improve the workability of the mixture, there is a negative correlation between the mechanical properties of SCC and the fly ash replacement rate. For steel-fiber-reinforced SCC containing 60% fly ash, when the content of steel fibers exceeds 0.75%, the workability decreases sharply, and even when the volume fraction is 1.00%, the passing ability cannot meet the requirements of the technical specifications for applications of self-compacting concrete. The analysis results for mechanical properties show that compressive strength is not changed significantly with increasing percentage of steel fibers. The steel fibers strengthen splitting tensile strength and flexural strength significantly, and compared with that of without steel fibers, they increased by 22% and 58%, respectively, with steel fibers up to 1.00%. Additionally, the parameters of the axial compression deformation property are improved by introducing steel fibers, especially the strain energy (Vε) and relative toughness (Γ) of steel-fiber-reinforced SCC containing a high level of fly ash.     

An Integrated Approach to Using Sheep Wool as a Fibrous Material for Enhancing Strength and Transport Properties of Concrete Composites

An important goal to achieve sustainable development is to use raw materials that are easily recyclable and renewable, locally available, and eco-friendly. Sheep wool, composed of 60% animal protein fibers, 10% fat, 15% moisture, 10% sheep sweat, and 5% contaminants on average, is an easily recyclable, easily renewable, and environmentally friendly source of raw material. In this study, slump testing, compressive and flexural strengths, ultrasonic pulse velocity, sorptivity, and chloride penetration tests were investigated to assess the influence of wool fibers on the strength and transport properties of concrete composites. Ordinary Portland cement was used to make five concrete mixes incorporating conventional wool fibers (WFs) ranging from 0.5 to 2.5% and a length of 70 mm. The wool fibers were modified (MWFs) via a pre-treatment technique, resulting in five different concrete compositions with the same fiber content. The addition of WF and MWF to fresh concrete mixes resulted in a decrease in slump values. The compressive strength of concrete was reduced when wool fibers were added to the mix. The MWF mixes, however, achieved compressive strength values of more than 30 MPa after a 90-day curing period. Furthermore, by including both WF and MWF, the flexural strength was higher than that of plain concrete. In addition, adding fibers with volume fractions of up to 2% reduced the concrete composite’s sorptivity rate and chloride penetration depths for both WF and MWF content mixes. Consequently, biomass waste like sheep wool could be recycled and returned to the field following the circular economy and waste valorization principles.     

Development of 3D Printable Cementitious Composites with the Incorporation of Polypropylene Fibers

Similar to conventional cast concrete, printable materials require reinforcement to counteract their low tensile strength. However, as traditional reinforcement strategies are not commonly used in 3D print applications, fiber reinforcement can serve as an alternative. This study aims to assess the influence of different polypropylene fiber lengths (3 and 6 mm, denoted as M3 and M6, respectively) and dosages (0.1 and 0.3% volume fraction) on the workability, pore structure, mechanical and shrinkage behavior of 3D printable cementitious materials. Fresh state observations revealed that the addition of a higher fiber volume decreased the workability of the material, irrespective of the fiber length as a result of the lower water film thickness (WFT). In hardened state, a marginal increase in total porosity could be observed when adding fibers to the mix composition. In addition, the flexural strength was found to increase with the addition of fibers, while no significant difference was observed in compressive strength. The increase in flexural strength was more pronounced in the case of longer-sized M6 fibers. Finally, the total drying shrinkage behavior was evaluated using mold-cast prisms. The addition of M6 fibers showed no beneficial effect in reducing total free shrinkage, while a reduction in total free shrinkage was observed when using M3 fibers.     

Enhancement of Confinement in Scaled RC Columns using Steel Fibers Extracted from Scrap Tyres

Steel fibers are widely extracted from scrap tyres, causing environmental concerns. This paper presents the use of steel fibers in variable proportions extracted from scrap tyres. The enhancement of the confinement was envisaged through the addition of steel fibers obtained from scrap tyres. The study included an experimental program for the development of constitutive material models for ordinary Portland cement (OPC) concrete and concrete with added steel fibers. A mix design was carried out for OPC, targeting a compressive strength of 3000 psi. Steel fibers were added to OPC in ratios of 1.0% to 3.0%, with an increment of 0.5%. Concrete columns, with cross-sectional dimensions of 6 × 6 inches and a length of 30 inches, were cast with both OPC and fiber-reinforced concrete. The column confinement was evaluated with a different spacing of ties (3- and 4-inch center-to-center). Compression tests on the concrete columns indicate that the addition of steel fibers to a concrete matrix results in an appreciable increase in strength and ductility. Overall, increasing the percentage of steel fibers increased the compression strength and the ductility of concrete. The maximum strain in the concrete containing 2.5% steel fibers increased by 285% as compared to the concrete containing 1% of steel fibers. An optimum percentage of 2.5% steel fibers added to the concrete resulted in a 39% increase in compressive strength, accompanied by a significant improvement in ductility. The optimum content of steel fibers, when used in confined columns, showed that confined compression strength increased with the addition of steel fibers. However, it is recommended that additional columns on the basis of the optimum steel fiber content shall be tested to evaluate their effectiveness in reducing the stirrup spacing.     

Insight into the Mechanical Performance of the UHPC Repaired Cementitious Composite System after Exposure to High Temperatures

In this paper, the mechanical performance of an ultra-high-performance concrete (UHPC) repaired cementitious composite system, including the old matrix and the new reinforcement (UHPC), under various high temperature levels (20 °C, 100 °C, 300 °C, and 500 °C) was studied. In this system, UHPC reinforced with different contents of steel fibers and polypropylene (PP) fibers was utilized. Moreover, the physical, compressive, bonding, and flexural behaviors of the UHPC repaired system after being exposed to different high temperatures were investigated. Meanwhile, X-ray diffraction (XRD), baseline evaluation test (BET), and scanning electron microscope (SEM) tests were conducted to analyze the effect of high temperature on the microstructural changes in a UHPC repaired cementitious composite system. Results indicate that the appearance of the bonded system changed, and its mass decreased slightly. The average percentage of residual mass of the system was 99.5%, 96%, and 94–95% at 100 °C, 300 °C, and 500 °C, respectively. The residual compressive strength, bonding strength, and flexural performance improved first and then deteriorated with the increase of temperature. When the temperature reached 500 °C, the compressive strength, bonding strength, and flexural strength decreased by about 20%, 30%, and 15% for the UHPC bonded system, respectively. Under high temperature, the original components of UHPC decreased and the pore structure deteriorated. The cumulative pore volume at 500 °C could reach more than three times that at room temperature (about 20 °C). The bonding showed obvious deterioration, and the interfacial structure became looser after exposure to high temperature.     

Increasing Impact Strength of a Short Glass Fiber Compression Molded BMC by Shortening Fibers without Change in Equipment

Bird strike, volcanic rock, hailstones, micrometeoroids, or space debris can cause damage to aircraft and space vehicles, therefore their composite materials must have high impact resistance to maximize safety. In a 55% wt. CaCO₃ compression molded short glass fiber polyester GFRP-BMC (bulk molded compound), shortening the nominal 6.4 mm fiber length formulation, by 30 min extended mixing, to 0.44 mm was found to increase Charpy impact values, a_uc, without a change in the compression molding equipment. Specimens were cut from square panels in a spiral configuration in conformity with ASTM D 6110-02 for orthotropic panels, the flow direction approximately radially outward from the charge. At a median-fracture probability of P_f = 0.50, extended mixing improved a_uc by 29%, from 7.43 to 9.59 kJm⁻², and for each solidification texture angle, namely, 0 to 90 (random), 71, 45 and 18 deg, the a_uc increased by 25% (6.26 to 7.86 kJm⁻²), 18% (9.36 to 11.07 kJm⁻²), 35% (7.68 to 10.37 kJm⁻²), and 20% (6.96 to 8.36 kJm⁻²), respectively. This strengthening can be explained by an increased number of thermal compressive stress sites between the glass fiber and matrix due to a difference in the coefficient of thermal expansion (CTE) during cool-down, and shrinkage, with an increased number of spaces between fibers, |S_f| from 217 to approximately 2950 per mm³, enhancing impact energy.     

Mechanical Properties of Mortars Reinforced with Amazon Rainforest Natural Fibers

The addition of natural fibers used as reinforcement has great appeal in the construction materials industry since natural fibers are cheaper, biodegradable, and easily available. In this work, we analyzed the feasibility of using the fibers of piassava, tucum palm, razor grass, and jute from the Amazon rainforest as reinforcement in mortars, exploiting the mechanical properties of compressive and flexural strength of samples with 1.5%, 3.0%, and 4.5% mass addition of the composite binder (50% Portland cement + 40% metakaolin + 10% fly ash). The mortars were reinforced with untreated (natural) and treated (hot water treatment, hornification, 8% NaOH solution, and hybridization) fibers, submitted to two types of curing (submerged in water, and inflated with CO₂ in a pressurized autoclave) for 28 days. Mortars without fibers were used as a reference. For the durability study, the samples were submitted to 20 drying/wetting cycles. The fibers improved the flexural strength of the mortars and prevented the abrupt rupture of the samples, in contrast to the fragile behavior of the reference samples. The autoclave cure increased the compressive strength of the piassava and tucum palm samples with 4.5% of fibers.     

Mechanical Properties of Aramid/Carbon Hybrid Fiber-Reinforced Concrete

In this study, aramid fiber (Kevlar^® 29 fiber) and carbon fiber were added into concrete in a hybrid manner to enhance the static and impact mechanical properties. The coupling agent presence on the surface of carbon fibers was spotted in Scanning Electron Microscope (SEM) and energy-dispersive X-ray spectroscopy (EDS) graphs. The carbon fiber with a coupling agent affected the mechanical strength of the reinforced concrete. At 1% fiber/cement weight percentage, the hybrid fiber-reinforced concrete (HFRC) prepared using Kevlar fiber and carbon fiber of 12 and 24 mm in length under different mix proportions was investigated to determine the maximum mechanical strengths. From the test results, the mechanical strength of the HFRC attained better performance than that of the concrete with only Kevlar or carbon fibers. Foremost, the mix proportion of Kevlar/carbon fiber (50–50%) significantly improved the compressive, flexural, and splitting tensile strengths. Under different impact energies, the impact resistance of the HFRC specimen was much higher than that of the benchmark specimen, and the damage of the HFRC specimens was examined with an optical microscope to identify slippage or rupture failure of the fiber in concrete.     

Flexural Behavior of T-Shaped UHPC Beams with Varying Longitudinal Reinforcement Ratios

In order to investigate the transverse flexural behavior of the UHPC waffle deck, a total of six T-shaped UHPC beams, with varying longitudinal reinforcement ratios, were tested and analyzed. The experiments, including material tests of UHPC and beam tests, were conducted. The material tests of UHPC revealed that strain-hardening behavior in tension was exhibited, and the ratio of uniaxial compressive strength-to-cubic compressive strength was 0.85. The beam tests showed that all the T-shaped UHPC beams, even without longitudinal rebar, exhibited ductile behavior that was similar to that of properly reinforced concrete beams. As the longitudinal reinforcement ratio increased, more flexural cracks developed and a larger load-carrying capacity was provided. Furthermore, the sectional analysis for the ultimate flexural capacity of T-shaped UHPC beams was conducted. Simplified material models, under tension and compression, for UHPC were developed. Based on the reverse calculation from the experimental result, the relation between reduction factor to the ultimate tensile strength of UHPC, and longitudinal reinforcement ratios was formulated. As a result, the predictive equations for the ultimate flexural capacity of T-shaped UHPC beams were proposed, and agreed well with the experimental results in this study and existing studies, which indicates good validity of the proposed equations.