热凝树脂、聚合瓷、CAD/CAM树脂与牙本质粘接的粘接强度比较

比较3种暂时修复体材料（热凝树脂、聚合瓷和CAD/CAM树脂）与牙本质粘接的剪切粘接强度（SBS）的差异。制作直径4 mm,高4 mm的热凝树脂、聚合瓷、计算机辅助设计与制作（CAD/CAM）树脂试件各15个,采用Scotchbond通用型粘接剂和RelyXTMUltimate非自粘接树脂水门汀将试件恒定压力下粘接于45颗人离体牙颊侧或舌侧牙本质面上,然后于（37±2）℃蒸馏水中储存24 h后进行SBS测试,记录断裂峰值并进行比较。扫描电镜观察试件处理前、牙本质粘接断面及试件粘接断面的形态,使用体视显微镜观察试件粘接界面破坏形式。结果显示,热凝树脂、聚合瓷、CAD/CAM树脂的SBS分别为（4.84±0.95） MPa、（11.20±1.49） MPa、（5.93±1.81） MPa。3种暂时修复体材料的SBS比较差异有统计学意义（P <0.05）;其中聚合瓷的SBS最大,热凝树脂的SBS最小。扫描电镜观察结果显示,热凝树脂和CAD/CAM树脂粘接前表面均较光滑;而聚合瓷粘接前表面有一定粗糙度。体视显微镜观察结果显示聚合瓷组粘接界面断裂方式表现为内聚破坏和混合破坏,而热凝树脂组和...     

冷热循环刺激对粘接性树脂粘接性能的影响

目的探讨口腔内冷热循环刺激对不同粘接性树脂粘接性能的影响.方法选用临床常用的粘接性树脂[如Super-bond C&B(SB)和Panavia21(PV)等]为对象,采用破坏韧性试验的方法,分别对冷热循环试验前后各粘接性树脂的破坏韧性加以测试比较,并观察其粘接面的破坏方式变化.结果不含无机填料的粘接性树脂(SB)在冷热循环试验后,破坏韧性值明显下降,同时龟裂进展面由凝集破坏变为界面破坏;含无机填料的粘接性树脂(PV)在冷热循环试验后,破坏韧性值下降不明显,龟裂进展面始终为凝集破坏.由此可见,冷热循环试验对不含无机填料的粘接性树脂的影响明显高于对含无机填料的粘接性树脂的影响.结论口腔内的冷热循环刺激对不含无机填料的粘接性树脂的影响明显高于对含无机填料的粘接性树脂的影响.通过适当填加无机填料,可以改善粘接性树脂的耐久性能.     

无机填料对粘接性树脂粘接性能的影响

目的：探讨无机填料对粘接性树脂粘接强度与破坏韧性的影响,同时对４℃和６０℃冷热循环试验的影响进行探讨。方法：选用临床常用的不含无机填料及无机填料含量不同的粘接性树脂为对象,采用抗拉粘拉试验及破坏韧性试验方法,分别对冷热循环试验前后各材料的粘接强度及破坏韧性加以测试比较。结果：无机填料的有无及含量多少对粘接性树脂的粘接强度无显著影响,但对粘接性树脂的破坏韧性的影响有显著性,即无机填料的填加会使破坏韧性值降低。冷热循环测试结果表明：无机填料的填加可提高粘接性树脂的粘接耐久性。结论：粘接性树脂应该科学适量地添加无机填料。     

树脂粘接剂的厚度对热压铸瓷修复体颜色的影响

目的:探讨树脂粘接剂的厚度对热压铸瓷修复体颜色的影响。方法:制作21个直径10 mm、厚度1 mm的A2色的热压铸瓷试件,实验组在试件表面涂刷树脂粘接剂,厚度分别为0.1 mm和0.2 mm,各7个;未涂刷树脂粘接剂者为对照组。用PR-650分光光度仪测量各组试件的颜色参数并计算组间色差。对实验数据进行统计学分析。结果:树脂粘接剂厚度对热压铸瓷试件的颜色参数有显著影响(P<0.05),随着粘接剂厚度的增加,试件的明度值逐渐降低,色相和彩度逐渐增高;0.1 mm和0.2 mm实验组与对照组间及实验组间的色差分别为0.78,2.31和1.37,组间颜色差异有统计学意义(P<0.05)。结论:树脂粘接剂的厚度对热压铸瓷修复体的颜色有显著影响,且粘接剂越厚影响越大。     

Er-YAG激光联合自酸蚀粘接处理儿童龋齿对患儿疼痛程度及口腔微生态影响

目的 探究饵（Er-YAG）激光联合自酸蚀粘接处理对龋齿患儿疼痛程度及口腔微生态的影响。方法 前瞻性选取2020年2月至2021年3月平顶山市口腔医院乳牙龋齿患儿152例作为研究对象,以电脑随机数字表法分为观察组（n=76）和常规组（n=76）。常规组采取自酸蚀粘接处理,观察组基于常规组联合Er-YAG激光。比较两组临床疗效、单次治疗时间、疼痛程度（FRS）、依从性（Frankl）、耐受程度（Houpt）、口腔微生态环境[中间普氏菌（Pi）、聚合梭杆菌（Fn）、伴放线菌（Aa）、牙龈卟啉单胞菌（Pg）、福赛坦菌（Tf）]、家长满意度及复发情况。结果 观察组治疗成功率（93.42%）高于常规组（78.95%）(P<0.05);治疗后,观察组单次治疗时间短于常规组,FRS、Frankl、Houpt评分低于常规组（P<0.05）;治疗后,两组Tf、Pg、Pi、Fn、Aa检出率均显著下降（P<0.05）,观察组下降幅度大于常规组（P<0.05）;观察组总满意度（90.79%）高于常规组（78.95%）(P<0.05);治疗1年后随访,观察组复发率（5.63%）与常...     

树脂托槽与瓷修复材料粘接抗剪切强度的实验研究

目的研究不同瓷表面处理方法对树脂托槽与瓷修复体粘接抗剪切强度的影响,找到适合瓷面与树脂托槽粘接的粘接剂和瓷表面处理方法。方法90颗制作好瓷贴面的离体牙随机均分为A、B、C三组:A组使用京津釉质粘合剂,B组使用光固化复合树脂,C组使用BISCO正畸单组分粘接剂粘接树脂托槽。每组再按照瓷表面处理方法的不同分为三组,在粘接前分别用酒精擦拭、打磨去釉氢氟酸酸蚀和打磨去釉氢氟酸酸蚀后涂硅烷偶联剂处理瓷贴面表面。所有样本在37℃恒温水浴中储存24小时后测定抗剪切粘接强度并记录去粘接后瓷贴面的破裂情况。结果BISCO正畸单组分粘接剂组的粘接强度明显高于京津釉质粘合剂组和光固化复合树脂粘接剂组(P<0.05),瓷贴面经打磨去釉氢氟酸酸蚀或再涂硅烷偶联剂处理后使用BISCO正畸单组分粘接剂粘接取得了正畸临床有效的粘接强度。各组去粘接后瓷破裂率没有显著性差异(P>0.05)。结论京津釉质粘合剂和光固化复合树脂粘接剂不适于正畸树脂托槽的粘接,BISCO正畸单组分粘接剂经打磨去釉、氢氟酸酸蚀后才能取得正畸临床有效的粘接强度,瓷面涂布硅烷偶联剂可增加其粘接强度且对去粘接后的瓷面破裂率无影响。     

牙齿表面性状对瓷贴面粘接力的影响

瓷贴面由于美观,颜色逼真,备牙量小、对牙齿损伤小等优点,逐渐得到众多医生及患者的认可。然而,瓷贴面、粘接剂与牙体成为粘接复合体,依赖于良好的粘接力。另外,由于牙体组织表面性状的多样性,产生了不同的处理方法。本文就牙齿表面性状对瓷贴面粘接力的影响因素作一综述,为临床在瓷贴面修复过程中,对牙体组织的处理提供参考依据。     

选择性釉质酸蚀结合自酸蚀粘结对釉质粘接剪切强度的影响

目的 评估选择性釉质酸蚀结合自酸蚀粘接、全酸蚀和自酸蚀粘接3种不同粘结系统对釉质粘接树脂的剪切强度影响.方法 在30颗无龋坏离体人磨牙分别制备60个牙釉质粘接界面试件,随机分为3组,每组10颗牙,第1组用35％磷酸预处理牙釉质结合可乐丽菲露SEbond粘接;第2组用35％磷酸和3M Singlebond2粘接;第3组用可乐丽菲露SEbond粘接.各试件在37℃生理盐水进行浸泡24 h,分别进行牙釉质抗剪切强度的测试.结果 3组剪切强度两两比较,P＜0.05,有统计学意义;第1组粘接强度明显好于第3组(P＜0.05),提示磷酸预酸蚀釉质处理后再联合使用自酸蚀粘接系统可大大提高粘接强度.结论 选择性釉质酸蚀结合自酸蚀可以显著提高树脂与牙釉质的粘接强度.     

自酸蚀与磷酸酸蚀粘接修复楔状缺损的疗效比较

目的比较自酸蚀和磷酸酸蚀两种粘接系统修复楔状缺损的临床疗效。方法选取22例在我院门诊口腔科就诊的患者共146颗患牙,随机分成试验组和对照组,试验组使用可乐丽菲露SE BOND和可乐丽菲露AP-X复合树脂充填患牙;对照组使用登士柏磷酸酸蚀粘接剂和登士柏复合树脂充填。充填后3,6,12,18个月进行复查和临床评价,根据Ryge G的改良USPHS评分系统进行评价。结果治疗18个月后,可乐丽菲露树脂及登士柏树脂充填体脱落率分别为7%,13%,差异无统计学意义。两种树脂均无继发龋,边缘着色、解剖形态、表面光滑度差异无统计学意义。颜色匹配、牙齿敏感方面可乐丽菲露优于登士柏。结论充填牙颈部楔状缺损自酸蚀粘接系统的树脂略优于磷酸酸蚀粘接系统的树脂。     

处理方式对唾液污染后氧化锆与树脂粘接强度的影响

目的:体外研究唾液污染后氧化锆经不同方式处理后与树脂粘接强度的变化。方法:制备氧化锆试件80个(9 mm×9 mm×3 mm),分成8组,分别为阴性对照组(C组):喷砂-底涂剂;阳性对照组(N组):喷砂-唾液污染-水冲洗-底涂剂;Zirclean组(A组):A1组为喷砂-唾液污染-Zirclean清洁剂-底涂剂;A2组为喷砂-底涂剂-唾液污染-Zirclean清洁剂-底涂剂;A3组为唾液污染-Zirclean清洁剂-喷砂-底涂剂;Ivoclean组(B组):B1、B2、B3各组处理顺序同A组对应组,仅清洁剂改为Ivoclean。每组选取2个试件,扫描电镜观察其表面。制作树脂样本(高度4 mm、直径4 mm)64个,将其以通用型树脂水门汀粘接于试件上,包埋,万能实验机测量剪切强度,显微镜(×10)下记录其断裂模式。结果:8组试件间剪切强度比较,差异有统计学意义(P<0.001)。B1组剪切强度较A1组高,A2组剪切强度较A1高,B2组剪切强度较B1、B3组高(P<0.05)。各组试件的断裂模式均主要是内聚破坏。结论:Zirclean和Ivoclean均能提升唾液污染后氧化锆与...     

Impact of cast-ceramic thickness and translucency on curing efficiency of dual-cured resin cement

目的 研究不同厚度和不同透明度铸瓷对双固化树脂黏结剂固化效率的影响.方法 选用4种不同透明度(高度透明HTA2、低度透明LTA2、中度不透明MO1、高度不透明HO1)的IPSe.max全瓷,制备成直径为6mm,厚度分别为0.5、1、2、3、4 mm的圆片,共计20个.二极管(LED)光固化灯作为固化光源,VariolinkⅡ作为实验中的双固化树脂黏结剂,根据光照过程中有无铸瓷作为中介分为实验组和空白组.利用傅里叶红外光谱仪检测树脂黏结剂的双键转换率,并通过显微硬度仪记录固化后树脂的表面努氏硬度值.结果 在同一透明度下,VariolinkⅡ树脂黏结剂表面努氏硬度值除HTA2和 LTA2的1.0 mm与2.0 mm之间无显著性差异外(P＞0.05),其余不同厚度组之间均存在显著性差异(P＜0.05),且随着瓷片厚度的增加努氏硬度值呈降低趋势;在相同厚度下,HTA2和LTA2的树脂黏结剂表面努氏硬度值显著高于HO1和MO1 (P ＜0.05),而HTA2与LTA2之间及HO1与MO1之间的努氏硬度值无显著性差异(P＞0.05).不同厚度和不同透明度铸瓷下VariolinkⅡ树脂黏结剂双键转换率均有显著性差异(P＜0.05),且随铸瓷透明度降低及厚度增加呈降低趋势.树脂黏结剂的表面努氏硬度值和双键转换率除了IPSe.max HTA2组外,其余实验组均显著低于空白组(P＜0.05).结论 双固化树脂黏结剂的固化效率受铸瓷厚度和透明度影响,且随其厚度增加及透明度降低固化效率降低.     

不同厚度和不同透明度铸瓷对树脂黏结剂固化效率的影响

目的研究不同厚度和不同透明度铸瓷对双固化树脂黏结剂固化效率的影响。方法选用4种不同透明度(高度透明HTA2、低度透明LTA2、中度不透明MO1、高度不透明HO1)的IPSe.max全瓷,制备成直径为6 mm,厚度分别为0.5、1、2、3、4 mm的圆片,共计20个。二极管(LED)光固化灯作为固化光源,VariolinkⅡ作为实验中的双固化树脂黏结剂,根据光照过程中有无铸瓷作为中介分为实验组和空白组。利用傅里叶红外光谱仪检测树脂黏结剂的双键转换率,并通过显微硬度仪记录固化后树脂的表面努氏硬度值。结果在同一透明度下,VariolinkⅡ树脂黏结剂表面努氏硬度值除HTA2和LTA2的1.0 mm与2.0 mm之间无显著性差异外(P>0.05),其余不同厚度组之间均存在显著性差异(P<0.05),且随着瓷片厚度的增加努氏硬度值呈降低趋势;在相同厚度下,HTA2和LTA2的树脂黏结剂表面努氏硬度值显著高于HO1和MO1(P<0.05),而HTA2与LTA2之间及HO1与MO1之间的努氏硬度值无显著性差异(P>0.05)。不同厚度和不同透明度铸瓷下VariolinkⅡ树脂黏结剂双键转换率均有显著性差异(P<0.05),且随铸瓷透明度降低及厚度增加呈降低趋势。树脂黏结剂的表面努氏硬度值和双键转换率除了IPSe.max HTA2组外,其余实验组均显著低于空白组(P<0.05)。结论双固化树脂黏结剂的固化效率受铸瓷厚度和透明度影响,且随其厚度增加及透明度降低固化效率降低。     

Er:YAG 激光和酸蚀预处理对自粘结树脂水门汀粘结强度的影响

目的:探讨Er:YAG 激光和酸蚀预处理对自粘结树脂水门汀粘结强度的影响?方法:44颗前磨牙根据对牙本质表面预处理方式的不同随机分为4组:对照组?Er:YAG 激光组?酸蚀组(35%磷酸)?Er:YAG 激光+酸蚀组?每组11颗牙中随机选出1颗切取3 mm厚牙本质片,按相应分组要求预处理后进行扫描电镜观察;每组剩余10颗牙制备一致标准牙本质表面后按相应分组要求预处理,用自粘结树脂水门汀RelyXTM Unicem将其与Everest ZS 氧化锆瓷片粘结,24 h后测试各组剪切粘结强度并进行统计分析?结果:扫描电镜观察显示采用不同方式预处理后,牙本质表面形态改变明显;统计分析结果显示剪切粘结强度由高到低为Er:YAG 激光组(7.18 ± 2.54)MPa?Er:YAG 激光+酸蚀组(5.50 ± 2.09)MPa?对照组(4.05 ± 1.04)MPa?酸蚀组(3.61 ± 0.70)MPa;Er:YAG 激光组?Er:YAG 激光+酸蚀组与对照组有显著性差异(P < 0.05),酸蚀组与对照组无显著性差异(P > 0.05)?结论:酸蚀对自粘结树脂粘结强度的改变无明显影响,Er:YAG 激光预处理能有效提高自粘结树脂与牙本质和氧化锆瓷的粘结强度?     

Hardness of resin cement cured under different thickness of lithium disilicate-based ceramic

Background  The lithium disilicate-based ceramic is a newly developed all-ceramic material, which is lithium disilicate-based and could be used for fabricating almost all kinds of restorations. The extent of light attenuation by ceramic material was material-dependent. Ceramic materials with different crystal composition or crystalline content would exhibit distinct light-absorbing characteristics. The aim of this study was to analyze the influence of ceramic thickness and light-curing time on the polymerization of a dual-curing resin luting material with a lithium disilicate-based ceramic.

Methods  A lithium disilicate-based ceramic was used in this study. The light attenuation caused by ceramic with different thickness was determined using a spectral radiometer. The commercial dual-cured resin cement was light-cured directly or through ceramic discs with different thickness (1, 2 and 3 mm, respectively) for different times (10, 20, 30, 40, 50 and 60 seconds, respectively). The polymerization efficiency of resin cement was expressed in terms as Vickers hardness (VHN) measured after 24 hours storage. Two-way analysis of variance (ANOVA) and Tukey’s HSD tests were used to determine differences.

Results  Intensity of polymerizing light transmitted through ceramic discs was reduced from 584 mW/cm² to about 216 mW/cm², 80 mW/cm² and 52 mW/cm² at thicknesses of 1 mm, 2 mm and 3 mm, respectively. Resin cement specimens self-cured alone showed significantly lower hardness values. When resin cement was light-cured through ceramic discs with a thickness of 1 mm, 2 mm and 3 mm, no further increasing in hardness values was observed when light-curing time was more than 30 seconds, 40 seconds and 60 seconds, respectively.

Conclusions  Within the limitation of the present study, ceramic thickness and light-curing time had remarkable influence on the polymerization of dual-cured resin cement. When resin cement is light-cured beneath a lithium disilicate ceramic with different thickness, prolonging light-curing time accordingly may still be necessary to insure complete polymerization.

     

调拌纸板厚度对玻璃离子水门汀抗压强度的影响

目的: 探讨调拌纸板厚度变化对玻璃离子水门汀抗压强度的影响。方法: 在相同的实验条件下,分别采用60、40、20、1张纸的纸板(P60、P40、P20、P1)对3种不同的玻璃离子水门汀进行调拌,在其凝固后进行抗压强度检测,并用扫描电镜观察不同组别材料断面气泡形成情况。结果: (1) 抗压强度：①ChemFil Superior玻璃离子材料(CF)：P1组平均抗压强度最高,与P40、P60组相比差异有统计学意义(P=0.041、0.032);②而至富士IX GP玻璃离子材料(IX)：P1组平均抗压强度最高,与P40、P60组相比差异有统计学意义(P=0.042、0.038);③Glaslonomer FX-Ⅱ玻璃离子材料(FX)：P1组平均抗压强度最高,与P20、P40、P60组相比差异有统计学意义(P=0.031、0.040、0.041),其余各组间差异无统计学意义,三种材料均显示出随着调拌纸板厚度的下降,玻璃离子抗压强度逐渐升高,纸板厚度与玻璃离子抗压强度成高度线性负相关,CF、IX、FX相关系数分别为-0.927、-0.989、-0.892。(2)扫描电镜下观察：三种材料均显示P1组气泡最少。结论: 采用1张纸的纸板调拌玻璃离子水门汀的气泡最少,并可以获得更高的抗压强度。     

铸瓷固位钉对牙本质-树脂界面粘结强度的影响

目的:探讨自行研制的铸瓷固位钉对牙本质-复合树脂界面粘结强度的影响,为铸瓷固位钉进一步的临床应用提供实验依据?方法:将40颗离体牙随机分为4组:A组,铸瓷固位钉组;B组,金属自攻螺纹钉组;C组,复合树脂钉组;D组,树脂直接充填组?采用IPS e. max Press热压铸瓷系统制作铸瓷牙本质固位钉,制备标准化牙本质-固位钉-复合树脂块试件,微拉伸实验测试各组试件粘结强度,体视显微镜下观察试件断裂面形态?结果:A?B两组试件粘结强度显著高于C?D两组,差异有统计学意义(P < 0.05);A组与B组?C组与D组组间粘结强度差异无统计学意义(P > 0.05)?A?C?D三组试件断裂模式以牙本质-树脂界面断裂为主,B组以牙本质内聚断裂为主?结论:作为一种新型牙本质固位钉,IPS e.max Press铸瓷固位钉可显著提升牙本质-复合树脂界面的粘结强度?     

髓腔内压对树脂水门汀与牙本质粘接强度的影响

目的: 评价髓腔内压条件对树脂水门汀与牙本质微拉伸粘接强度的影响。方法: 选择新拔除的人无龋第三磨牙30颗分成2组,去除咬合面釉质制备牙本质平面,选取剩余牙本质厚度为0.5~2.5 mm的牙本质试样,在有染料的髓腔内压条件下,观察牙本质表面与牙面处理剂Single Bond Universal(SBU)固化后表面在即刻、5 min、30 min、2 h的染料渗透情况。保持最小剩余牙本质厚度为(1.0±0.1) mm,分别在有或无髓腔内压条件(15或0 cmH₂O,1 cmH₂O=0.098 kPa)下维持30 min,使用SBU并光照固化,然后使用模具在牙本质表面堆塑RelyX Ultimate(RLX)树脂水门汀(直径10 mm,高4 mm),制备牙本质-树脂水门汀粘接试样。试样在37 ℃蒸馏水中储存24 h后,将牙本质-树脂水门汀试样垂直于粘接界面切割形成横截面积为0.9 mm×0.9 mm条状试样,使用微拉伸测试仪测试计算其粘接强度(两独立样本t检验,双侧检验水平α=0.05),用扫描电镜观察统计试样断裂类型(Fisher精确检验,双侧检验水平α=0.05)。将牙本质-树脂水门汀试样垂直粘接界面做切片,厚度0.8 mm,扫描电镜下观察粘接界面形貌。结果: 在髓腔内压条件下,随时间延长,粘接表面染料渗出增加。有髓腔内压时和无髓腔内压时RLX与牙本质微拉伸粘接强度分别为:(26.26±9.78) MPa和(28.70±9.09) MPa,两者差异无统计学意义(P>0.05)。两组试样断裂类型无明显差异(P>0.05),都以混合断裂为主。两组试样粘接界面可见4~8 μm指状树脂突,分布及长短较均匀,形貌无明显差异。结论: SBU预处理牙本质后,髓腔内压不影响树脂水门汀RLX的即刻牙本质粘接强度。     

粘固剂影响桩核冠修复上颌中切牙的应力分析

目的分析不同的粘固剂厚度对上颌中切牙桩核冠修复后剩余牙本质和粘固剂应力状况的影响。方法采用三维有限元分析方法,建立不同粘固剂厚度的上颌中切牙桩核冠修复的三维有限元模型,模拟前伸和正中加载,选取指标为Von Mises应力、最大主应力和剪切力,分析粘固剂层厚度变化对牙本质和粘固剂的应力分布以及应力峰值的影响。结果随着粘固剂层的增厚,各模型牙本质应力分布基本相似,前伸加载时3个模型牙本质内Von Mises应力和最大主应力集中区均在根尖,正中加载时两种应力的集中区同时出现在舌侧颈缘及根颈1/3;牙本质内Von Mises应力和最大主应力的峰值略有减小,而粘固剂层的Von Mises应力峰值、最大主应力峰值以及剪切应力峰值均明显减小,其中在前伸加载、粘固剂厚度为100μm时粘固剂层XY和YZ方向剪切应力峰值下降最为明显,分别达到了63.22%和51.46%。结论粘固剂的厚度变化对牙本质的应力影响较小,而对粘固剂本身影响较大,适当增加粘固剂的厚度可以降低粘固剂的应力峰值。     

微波辐射聚合对树脂义齿基托孔隙的影响

目的：探讨不同条件微波辐射聚合对树脂义齿基托孔隙的影响。方法：用4种不同的聚合方法2种树脂基托材料制作3种规格的标准试样120件,分为MH1、MH2、MH3和CH四组,每组每种材料和厚度规格的试样各5件。每试样截取3个测试面,用计算机显微摄影方法采集孔隙图像,记录孔隙的密度数据,统计分析。4种聚合方法分别是：实验组为3种不同的微波辐射聚合方法（Microwave Heating treatment,MH）即①MH1：162W,12 min分次间歇辐射;②MH2：162W,12 min持续辐射;③MH3：900W,3 min持续辐射;对照组选用传统水浴聚合方法（Conventional Heating treatment,CH）即（74±1）℃,12 h水浴恒温。2种材料即传统树脂（Conventional Resin,CR）和微波专用树脂（Microwave special design Resin,MR）。3种规格的试样分别为40 mm×10 mm×2 mm,40 mm×10 mm×4 mm和40 mm×10 mm×6 mm。结果：不同聚合方法,不同材料和不同厚度因素所得树脂试样的孔隙密度差异均有统计学意义（F聚合=3826.40,P〈0.0001;F材料=27.13,P〈0.0001;F厚度=37.81,P〈0.0001）。MH1与CH组两者之间试样的孔隙密度差异无统计学意义（F=0.41,P=0.5209）。MH2,MH3与CH组以及MH1,MH2,MH3组两两之间试样的孔隙密度差异均有统计学意义（FMH2与CH=825.64,FMH3与CH=8661.88,FMH1与MH2=789.30,FMH2与MH3=4139.03,P值均小于0.0001）。2 mm,4 mm和6 mm试样的孔隙密度两两之间差异均有统计学意义[F2与4=27.37（P〈0.0001）,F2与6=74.50（P〈0.0001）,F4与6=11.56（P=0.0010）]。聚合方法与材料（F=9.47,P〈0.0001）,聚合方法与厚度（F=84.56,P〈0.0001）,聚合材料与厚度（F=4.00,P=0.0213）两两之间均有交互作用。结论：微波低功率、短时间、间歇辐射可使树脂基托孔隙密度降到最小。     

全膝关节置换术中止血带应用对假体骨水泥厚度影响的对照研究

目的 探讨全膝关节置换术(TKA)中是否使用止血带对膝关节假体骨水泥厚度的影响.方法 2013年6月至2014年6月采用人工TKA治疗中重度骨性关节炎患者112例,其中94例为初次置换.按照选择标准共82例(82膝)患者纳入研究.所有患者随机分为非止血带组(41例膝)和止血带组(41例膝),止血带组术中全程使用止血带,非止血带组不使用止血带.所有患者术后行膝关节正侧位片检查,测量侧位片上股骨2个测量点,胫骨2个测量点和正位片上胫骨2个测量点假体下骨水泥厚度,同时记录分析两组的显性失血量、血红蛋白(Hb)降低值、输血率、平均输血量、视觉模拟评分法(VAS)疼痛评分、膝关节活动度、肢体肿胀、肌间静脉血栓、皮下淤斑等.结果 两组均无术后感染、伤口坏死等并发症,非止血带组在围术期显性失血量、Hb降低值、输血率、平均输血量、膝关节活动度方面比较明显高于止血带组(P＜0.05),在VAS疼痛评分、肢体肿胀、肌间静脉血栓、皮下淤斑发生率方面明显低于止血带组(P＜0.05).术后测量胫骨骨水泥厚度[非止血带组(3.57±0.62)mm,止血带组(3.74±0.71)mm)],股骨骨水泥厚度[非止血带组(2.00±0.43)mm,止血带组(2.19±0.48)mm],两组比较差异均无统计学意义(P＞0.05).结论 TKA中使用止血带可以减少显性失血量、输血率及平均输血量,但不使用止血带有更好的临床效果.