纳米非晶金刚石膜对镍铬合金烤瓷修复体弯曲强度的影响

目的:探讨纳米非晶金刚石膜对镍铬合金烤瓷修复体弯曲强度的影响.方法:36个镍铬合金烤瓷试件随机分为6组(n=6),其中5组的整个试件的表面分别镀覆非晶金刚石膜厚为20nm、40nm、60nm、80nm、100nm,对照组不镀膜;按照ISO9693-1标准的三点弯曲法测试试件的弯曲强度.结果:镀膜后镍铬合金烤瓷试件的弯曲强度分别是:20nm组为60.84 ±6.75MPa、40nm组为79.16±9.82MPa、60nm组为86.23±11.43MPa、80nm组为81.40±9.69MPa、100nm组为64.56±7.07MPa,未镀膜组为46.15±5.53MPa.结论:镍铬合金烤瓷复合体的整个试件经镀覆纳米非晶金刚石膜后其弯曲强度显著增加;镀膜时选择40-80nm的膜厚可以获得较高的弯曲强度.     

纳米非晶金刚石膜镀覆对镍铬及钴铬烤瓷合金离子析出的影响

目的：观测纳米非晶金刚石膜对镍铬及钴铬两种非贵金属烤瓷合金在人工唾液中金属离子析出的影响。方法：制备镍铬合金、钴铬合金圆片形试件各24个,镍铬及钴铬合金试件随机分成a1、b1及a2、b2各两组,a1、a2组试件表面不镀膜,b1、b2组试件表面完整镀膜膜厚60nm,将a1、a2、b1、b2每组试件平分两半,分别置于pH值为6.8和4.0的人工唾液中浸泡7天,检测各组试件的金属离子析出量。结果：a1、a2组试件在两种人工唾液中表现出其所含各种金属离子的析出,在pH=4酸性人工唾液中浸泡后的离子析出量显著高于其在pH=6.8中性人工唾液中浸泡后的离子析出量（P〈0.05）;b1、b2组试件在两种人工唾液中浸泡后,其离子析出量分别比a1、a2组试件显著降低（P〈0.01）。结论：镍铬合金、钴铬合金在中性和酸性人工唾液中表现出其所含各种金属离子的析出,在酸性人工唾液中其金属离子析出量显著增加;纳米非晶金刚石镀膜能显著降低镍铬、钴铬合金在中性和酸性人工唾液中的金属离子析出量,有良好的耐腐蚀性。     

纳米非晶金刚石膜镀覆镍铬合金烤瓷冠对基牙牙周组织的影响

目的:观察纳米非晶金刚石膜镀覆镍铬合金烤瓷冠对基牙牙周组织的影响。方法:应用镍铬合金烤瓷冠(未镀膜组)修复49例65颗牙,纳米非晶金刚石膜镀覆镍铬合金烤瓷冠(镀膜组)修复46例62颗牙,观察对比1年后两组烤瓷冠的基牙牙周组织变化。结果:镍铬合金烤瓷冠修复1年后,未镀膜组11颗基牙牙龈发生龈染色,镀膜组3颗基牙牙龈发生龈染色;未镀膜组牙龈指数(1.64±0.22)与修复前(0.79±0.16)比较差异有统计学意义,而镀膜组牙龈指数(0.83±0.21)与修复前(0.80±0.19)比较差异无统计学意义;未镀膜组和镀膜组的修复前、修复后菌斑指数、牙周探诊深度差异无统计学意义。结论:镍铬合金烤瓷冠修复对基牙牙周组织有一定的不良影响,纳米非晶金刚石膜镀覆镍铬合金烤瓷冠对基牙牙周组织的影响较小,镀覆纳米非晶金刚石膜能减轻镍铬合金烤瓷冠基牙的牙龈染色及牙龈指数。     

金铂合金与镍铬合金烤瓷颜色和金瓷结合强度的比较研究

目的 探讨金铂合金烤瓷与镍铬合金烤瓷颜色和金瓷结合强度的差别,为临床选择修复材料 提供理论依据。方法 ①制作不同体瓷厚度的金铂、镍铬合金烤瓷圆盘试件各15件,用美能达CR-100色 度计测量试件上遮色瓷、体瓷后的L、a、b值,计算两种金属烤瓷颜色(A2)间的色差△E。②制作金铂、镍铬 合金烤瓷棒盘试件各5件,通过剪切实验测量金瓷结合强度。结果 ①金铂合金烤瓷颜色比镍铬合金烤瓷颜 色要偏黄、偏红,明度小,两种金属烤瓷颜色(A2)的色差△E在遮色瓷时最大,随体瓷增厚而减小。②金铂合 金烤瓷金瓷结合强度85.08±15.16MPa,镍铬合金烤瓷金瓷结合强度54.76±8.74MPa,统计学分析P<0.05。结论 金铂合金烤瓷不仅金瓷结合强度高,不易崩瓷,而且颜色更接近天然牙。     

自制镍铬烤瓷合金剪切结合强度的比较研究

目的探讨镍铬烤瓷合金中添加钛（Ti）、稀土金属以及不含铍（Be）对金瓷结合性能的影响。方法选用中国科学院金属研究所研制的镍铬烤瓷合金,按照是否含铍和稀土金属分为3个实验组（R1、R2、R3组）;以HI BONDNi-Cr烤瓷合金作为对照组（R4组）。对金瓷结合试件行剪切结合强度测试和金瓷界面的扫描电镜观察与能谱分析。结果R1、R2、R3、R4组剪切结合强度间差异无统计学意义（P＞0.05）。扫描电镜观察金瓷界面形貌可见,合金与瓷紧密接触,无裂缝。各组界面元素种类接近。结论自制镍铬烤瓷合金的金瓷结合良好,剪切结合强度可以达到临床应用的要求。在镍铬烤瓷合金中加入Ti和稀土金属且不含Be可作为临床使用的更好推荐。     

贵金属烤瓷与镍铬合金烤瓷修复体的效果评价

目的:观察比较贵金属烤瓷牙与镍铬合金烤瓷牙的临床修复效果.方法:2004年间,为48例患者制作贵金属烤瓷牙168颗,为另外48例患者制作镍铬合金烤瓷牙179颗.在修复体粘结后即刻以及完成后6个月、1a、2a、3a时复诊,检查修复体的完整性、固位、颜色、颈缘以及牙龈情况.采用SPSS12.0软件包对数据进行秩和检验.结果:修复后即刻检查,贵金属修复组与镍铬合金修复组临床效果良好,而修复后6个月、1a、2a、3a各时间点,2组修复体临床效果总体上比较,贵金属组显著优于镍铬合金组,差异有统计学意义,P＜0.05.结论:贵金属烤瓷冠是性能优良的长久性修复体,尤其在颜色方面优于镍铬合金烤瓷冠.     

高金合金与镍铬合金烤瓷冠临床应用效果的比较

目的：探讨和比较高金合金、含钛的镍铬合金（Tilite、钛莱特）、镍铬合金烤瓷冠的临床应用效果。方法：分别制作高金合金、钛莱特、镍铬合金烤瓷冠各60个，共180个。在烤瓷冠完成时和复查时，临床检查冠的颜色、颈缘染色、边缘密合度和牙折断、折裂情况，观察3年。结果：钛莱特和镍铬合金烤瓷冠在颜色、颈缘染色、边缘密合度方面无显性差异（P＞0.05）；高金合金烤瓷冠没有颈缘染色，在颜色和边缘密合度方面优于Tilite和镍铬合金烤瓷冠（P＜0.05）；3组都未见牙折断、折裂及组织过敏反应。结论：高金合金烤瓷冠比镍铬合金烤瓷冠有更好的临床效果。     

不同烤瓷合金及预氧化处理对金瓷结合强度影响的研究

目的:测试比较3种烤瓷合金(BioHeradorN贵金属烤瓷合金,TILITE含钛医学合金,HeraeniumS不含铍烤瓷合金)的金瓷结合强度,研究预氧化处理对烤瓷合金金瓷结合强度的影响。方法:制作蜡片30个,随机分为3组,每组10件。采用BellavesSH包埋料真空包埋、铸造,铸件最终尺寸为25mm×3mm×0.5mm金属片。上瓷前对铸件按实验要求进行处理,然后上瓷、烧烤。测试金瓷结合强度。结果:3种烤瓷合金金瓷结合强度由大到小依次为BioHeradorN合金,TILITE合金、HeraeniumS合金。预氧化处理可增加BioHeradorN合金、TILITE合金的金瓷结合强度,而对HeraeniumS合金的金瓷结合强度无重要影响。结论:贵金属烤瓷合金的金瓷结合强度大于非贵金属烤瓷合金的金瓷结合强度,BioHeradorN合金、TILITE合金上瓷前应作预氧化处理,以利于提高合金的金瓷结合强度。HeraeniumS合金上瓷前可不作预氧化处理。     

纳米过渡性介质对新型牙用烤瓷支架钴铬合金金瓷结合强度影响的研究

目的：研究纳米过渡性介质对新型牙用烤瓷支架钴铬合金（简称DA9-4合金）金瓷结合强度的影响。方法：用DA9-4合金制成金属棒以及金属片,并在金属试件上瓷前涂附纳米二氧化硅和纳米金介质2种不同的过渡性介质;金属棒与VMK95瓷粉烧结生成金瓷棒盘试件用于测定金瓷结合强度;金属片与VMK95瓷粉烧结形成金瓷复合体,分别观察金瓷界面的形貌及元素分布情况。结果：涂附纳米过渡性介质后的金瓷结合强度明显高于对照组（P〈0.01）。结论：纳米过渡性介质有改善新型牙用烤瓷支架钴铬合金金瓷结合强度的作用。     

纳米非晶金刚石膜改善义齿基托表面变形链球菌黏附量的研究

目的:观察比较义齿基托材料镀用纳米非晶金刚石薄膜前后,表面变形链球菌黏附量变化情况,探索纳米非晶金刚石薄膜镀用义齿树脂基托表面后的抗菌可能性。方法:采用热凝牙托材料制作30mm×10mm×2mm标准试件30个。按不同粗糙度(280目、600目、1200目)分成3组,每组10个。相同粗糙度的10个试件再分成2组,每组5个,一组试件双面镀用纳米非晶金刚石薄膜作为实验组,一组不作处理作为对照组。结果:3组不同粗糙度试件实验组及对照组均存在变形链球菌黏附,实验组少于对照组,两者差异有显著性(1200目P<0.05;600及280目P<0.01);不论实验组还是对照组试件表面变形链球菌黏附量均随粗糙度增大而增多(P<0.05),实验组增多趋势相对较小。结论:纳米非晶金刚石薄膜能够改善义齿树脂基托表面的变形链球菌黏附量,具有部分抑菌功能。     

A comparative evaluation of bond strength of feldspathic porcelain to nickel-chromium alloy,when subjected to various surface treatments: An in vitro study

Purpose of the Study:

The purpose was to evaluate the effect of various surface treatments and sandblasting with different particle size on the bond strength of feldspathic porcelain with predominantly base metal alloys, using a universal testing machine.

Materials and Methods:

Totally, 40 specimen of nickel-chromium alloy were prepared in an induction casting machine. The groups divided were as follows: Group I-sandblasted with 50 μ Al₂O₃, Group II-sandblasted with 110 μ Al₂O₃, Group III-sandblasted with 250 μ Al₂O₃ and Group IV-sandblasted with 250 μ Al₂O_3, followed by oxidation and again sandblasted with 250 μ Al₂O₃. The dimensions of each specimen were adjusted so as to maintain the thickness of ceramic at 1 mm. The specimen were loaded on the assembly of the universal testing machine, and a cross head speed of 0.5 mm/min was used to apply a compressive force at the junction of metal and feldspathic porcelain. The force application continued until adhesive fracture occurred, and the readings of the load applied to that particular specimen were recorded.

Results:

The means for shear bond strength for Group I, II, III and IV were found to be (226.92 ± 1.67), (233.16 ± 3.85), (337.81 ± 16.97) and (237.08 ± 4.33), respectively. Means of shear bond strength among the groups were compared using one-way analysis of variance test. Comparison between individual groups were made with Tukey''s Honestly Significant Difference post-hoc test.

Conclusion:

Different particle size and surface treatment have an important role on the bond strength of ceramic-metal interface. Greater particle size demonstrated higher bond strength.     

不同粘接剂对烤瓷瓷面与金属托槽间剪切强度影响的体外研究

目的 研究不同粘接剂对烤瓷瓷面与金属托槽间剪切强度的影响.方法 40个烤瓷瓷面经打磨、氢氟酸酸蚀、冲洗干燥、硅烷偶联剂处理瓷面后,再根据使用粘接剂的不同分为A组:光固化复合树脂粘接剂、B组:单组份化学固化复合树脂粘接剂、C组:树脂改良型光固化玻璃离子粘接剂、D组:双组份化学固化复合树脂粘接剂.将40个金属托槽粘接于烤瓷瓷面,经水浴孵化24 h后测得样本剪切强度,并进行统计分析.结果 A组剪切强度大于其他组(P＜0.05),C组剪切强度小于B组(P＜0.05),D组与B、C组剪切强度差异无统计学意义(P＞0.05).结论 光固化复合树脂粘接剂可获得最大的剪切强度,树脂改良型光固化玻璃离子粘接剂对金属托槽与烤瓷瓷面的粘接效果欠佳.     

SiO2薄膜对镍铬合金烤瓷冠色彩再现的影响

目的 探讨SiO<,2>薄膜是否会影响镍铬合金烤瓷修复体的色泽.方法 采用溶胶-凝胶法在镍铬合金烤瓷基底冠表面镀SiO<,2>薄膜,以此将制作的12颗 1 B2色烤瓷冠分为基底冠镀膜组和无镀膜组,每组6个样本.用ShadeEyeNcc电脑比色仪测量基底冠镀膜组和无镀膜组与6个B2(Vitapan classical比色...     

不同瓷粘结系统及表面处理方式对瓷与釉质间粘结强度的影响

目的 :探讨瓷与牙釉质粘结时不同瓷粘结系统与瓷表面处理方式的优化组合。方法 :以不同的瓷粘结系统和表面处理方式为影响因素 ,将瓷片分成 8组 ,分别与釉质粘结 ,测其剪切强度 ,统计分析所得数据 ,观察其断裂方式。结果 :处理组中以不喷砂磷酸酸蚀组的粘结强度最低 ,其余各组间无统计学差异。PanaviaF组剪切强度均值最高为 2 9.3 8MP ,邦多为 2 6.19MP。结论 :PanaviaF和邦多陶瓷粘结系统结合喷砂后磷酸酸蚀和HF酸蚀使用都可获得理想的粘结效果     

不同厚度溶胶-凝胶法二氧化硅薄膜对钛瓷结合强度的影响

目的：探讨溶胶-凝胶法在纯钛表面制备不同厚度的二氧化硅薄膜对钛瓷结合强度的影响。方法：将纯钛试件随机分成四组。一次组、二次组和四次组钛试件分别经过一个、两个和四个（硅溶胶甩膜＋热处理）周期处理,对照组未经过以上处理。在各组试件中份熔附Ti-22钛专用瓷,用三点弯曲法测试钛瓷分离时的载荷。结果：一次组、二次组、四次组和对照组的钛瓷的分离载荷分别为：6.040±0.798N、5.604±0.742N、6.081±0.947N和8.816±0.923N,实验组的钛瓷结合强度明显小于对照组（P〈0.05）。结论：不同厚度的二氧化硅薄膜均不能提高钛瓷结合强度。     

A comparative study on the bond strength of porcelain to the millingable Pd-Ag alloy

PURPOSE

The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys.

MATERIALS AND METHODS

Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe''s tests (α=.05).

RESULTS

The 3-point bending test showed the strongest (40.42 ± 5.72 MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy (37.71 ± 2.46 MPa), precious metal alloy containing 83% of gold (35.89 ± 1.93 MPa), and precious metal alloy containing 32% of gold (34.59 ± 2.63 MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05).

CONCLUSION

The type of metal-ceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa).