纳米金刚石表面改性对义齿黏附剂黏度的影响

目的:观察不同表面处理的纳米金刚石作为功能填料加入到高分子树脂类义齿黏附剂中,对义齿黏附剂黏度产生的影响。方法:以不同比例配方的改性和非改性纳米金刚石作为功能填料,加入到义齿黏附剂中,测试其黏度。采用SPSS17.0软件包对数据进行统计学分析。结果:添加比例在0.1wt%以下时,义齿黏附剂黏度随着比例的增加而下降;0.1wt%时,黏度降低最显著;添加比例在0.1wt%以上时,义齿黏附剂黏度随着比例的增加而增加。金刚石改性与否对黏度的影响有显著差异。结论:偶联剂化学接枝到金刚石表面,改性后的金刚石在乙醇中的分散稳定性得到提高;适当比例的纳米金刚石能显著降低义齿黏附剂的黏度,增加其流动性;同时,改性纳米金刚石的作用显著高于未经改性的金刚石。     

自制中药义齿粘附剂的粘接性能

目的:测定自制中药义齿粘附剂的粘接性能,并与Protefix义齿粘附剂进行比较。方法:测定自制义齿粘附剂与Protefix义齿粘附剂在浸泡人工唾液0~12 h过程中粘接抗张强度值,并进行比较。结果:自制义齿粘附剂在未浸泡唾液时与Protefix义齿粘附剂的粘接抗张强度值无显著性差异。在浸泡人工唾液后,其最大值,平均值及12 h值均大于Protefix义齿粘附剂(P<0.05)。结论:自制中药义齿粘附剂具有较好的粘接性能。     

Comfort-DA Ⅱ型义齿粘附剂的粘接性能评价

目的:研制新型高分子树脂类义齿粘附剂Comfort-DA Ⅱ型,评价其粘接性能。方法:运用统计学方法筛选出Comfort-DA Ⅱ型的最佳配比,测定配制后0h及浸泡人工唾液12h过程中粘接抗张强度值,与Protefix义齿粘附剂进行比较。结果:Comfort-DA Ⅱ型义齿粘附剂在配制0h的粘接抗张强度值,以及浸泡人工唾液后粘接抗张强度的平均值、最大值与第12h值均大于Protefix义齿粘附剂(P<0.05)。结论:Comfort-DA Ⅱ型义齿粘附剂具有较好的粘结抗张强度。     

氧化锆和纳米金刚石比例对核树脂挠曲强度的影响

目的 探讨二氧化锆、纳米金刚石比例对核树脂挠曲强度的影响.方法 采用双酚A-甲基丙烯酸缩水甘油酯(Bis-GMA)和二甲基丙烯酸三甘醇酯(TEGDMA)为树脂基质, 钡玻璃粉(BG)为主填料, 选择不同比例的微米或纳米级二氧化锆,纳米金刚石作为功能填料, 采用原位聚合法生成光固化牙科核树脂,万能材料试验机测定其挠曲强度.结果 含60wt%钡玻璃粉、0.2wt%纳米金刚石的树脂中,加入纳米级或微米级的二氧化锆含量分别为2wt%、3.5wt%、5wt%,3.5wt%相应核树脂挠曲强度最高;含70wt%钡玻璃粉、0.1wt%纳米金刚石的树脂中,加入40 nm的二氧化锆含量为0wt%、2wt%、3.5wt%、5wt%,2wt%质量百分比相应核树脂挠曲强度最高.结论 适当比例填料的核树脂挠曲强度能达到相应的国家标准及ISO标准的规定,能满足临床需要.     

纳米金刚石填料对复合树脂显微硬度、抗压强度的影响

目的：观察含纳米金刚石填料对复合树脂机械性能的影响，探索纳米金刚石的最佳比例。方法：按不同比例将纳米金刚石添加到复合树脂中，检测其抗压强度和显微硬度。结果：添加比例在0．005％以下抗压强度、显微硬度无明显改变；添加比例在0．005％—0．3％之间抗压强度、显微硬度明显提高，0．02％比例提高最为明显；添加比例在0．3％以上抗压强度、显微硬度明显降低。结论：适当比例纳米金刚石的填料可以提高复合树脂的机械性能。     

高分子树脂类Comfort-DA Ⅱ型义齿粘附剂的制备

目的 改进原有配方,研制一种新型高分子树脂类义齿粘附剂,并测定其pH值。方法 运用多重线性回归分析和正交设计法对影响配制义齿粘附剂粘结抗张强度的各因素进行分析,筛选出最佳配比,且与Protefix义齿粘附剂对比。并测试Comfort-DAⅡ型的pH值。结果 聚氧化乙烯、甲基纤维素、海藻酸钠、羟乙基纤维素和90%乙醇对配制义齿粘附剂粘结抗张强度的影响有统计学意义(P<0.05),蒙脱石对义齿粘附剂粘结抗张强度的影响没有统计学意义(P>0.05)。Comfort-DAⅡ型粘结抗张强度优于Protefix义齿粘附剂(P<0.05)。其酸碱度为弱碱性。结论 Comfort-DAⅡ型义齿粘附剂具有较好的理化性能。     

纳米金刚石填料对复合树脂耐磨性能及挠曲强度的影响

目的观察纳米金刚石填料对复合树脂耐磨性能、挠曲强度的影响,探索纳米金刚石填料的最佳比例。方法按不同比例将纳米金刚石添加到复合树脂中,检测其磨耗率、挠曲强度。结果添加比例为0.005%、1.000%组磨耗率、挠曲强度无明显变化。添加比例在0.020%～0.600%之间耐磨性能、挠曲强度明显提高,比例为0.600%时耐磨性能提高最为明显,添加比例为0.300%时挠曲强度提高最为明显。结论适当比例的纳米金刚石填料可以提高复合树脂的耐磨性能和挠曲强度。     

多重线性回归分析及优选义齿粘附剂配方

目的:优选Comfort-DA II型义齿粘附剂配方。方法:以粘结抗张强度值为评价标准,联用多重线性回归分析及正交设计法确定Comfort-DA II型义齿粘附剂的最佳配比。结果:聚氧化乙烯0.3125g、甲基纤维素1.250g、海藻酸钠0.5625g、羟乙基纤维素0.154g时,义齿粘附剂的粘结抗张强度值最高。结论:联用多重线性回归分析及正交设计法可有效地确定Comfort-DA II型义齿粘附剂的最佳配比。     

纳米金刚石填料对光固化窝沟封闭剂黏结剪切强度和表面显微硬度的影响

目的：观察纳米金刚石填料对窝沟封闭剂黏结剪切强度和表面显微硬度的影响，并比较其与气相二氧化硅之间的差别。方法：按不同比例将纳米金刚石添加到窝沟封闭剂中，检测其黏结剪切强度、表面显微硬度。结果：添加纳米金刚石后窝沟封闭剂的表面显微硬度明显提高，黏结剪切强度不受影响。添加5、10、20、40g／L的纳米金刚石比添加20g／L气相二氧化硅能获得更高的黏结剪切强度和表面显微硬度。结论：适当比例的纳米金刚石填料可以提高窝沟封闭剂的机械性能。     

新型高分子合成树脂类义齿粘附剂的研制

目的 :研制一种新高分子合成树脂类义齿粘附剂。方法 :用正交设计法设计出 12种不同的粘附剂配方 ,以粘结抗张强度为评分标准 ,运用方差分析对影响其粘度的各因素进行分析 ,筛选出粘附剂的最佳配比。结果和结论 :聚醋酸乙烯酯和纤维素醚的具体含量对粘附剂粘结抗张强度的影响无统计学意义 ,而乙醇及CMC -Na所占比例对其粘结强度的影响有统计学意义 ,且二者间有交互作用     

单瓶型通用粘接剂在牙本质粘接中的应用评价

［摘要］ 目的 评价2种单瓶型通用粘接剂在自酸蚀模式下应用与牙本质的粘接强度以及纳米渗漏情况。方法 制作40枚牙本质样本,分别使用Singlebond Universal和All-Bond Universal 2种单瓶型通用粘接剂在自酸蚀模式下处理牙本质表面,与复合树脂粘接制作粘接试件。各组粘接试件一半于24 h水储后（未老化）切割成细条,测试微拉伸粘接强度,另一半经受10 000次冷热循环后（老化）测试微拉伸粘接强度。数据以单因素方差分析和Tukey多重比较进行检验分析。各组代表性试件处理后以扫描电镜观察粘接界面,检测纳米渗漏情况。结果 不论是否经过老化,2种粘接剂组均获得了较高的粘接强度值,但扫描电镜均能发现纳米渗漏存在。结论 两种单瓶型通用粘接剂在自酸蚀模式下应用均能提供较好的粘接性能,但无法避免纳米渗漏的发生。     

Influence of carbamide peroxide-based bleaching agents on the bond strength of resin-enamel/dentin interfaces

In this bond strength study, a bleaching agent containing 10% carbamide peroxide was applied over composite-teeth bonded interfaces of two adhesive systems applied to enamel and dentin. Sixteen human third molars were used for bonding procedures. Single Bond (SB) and Clearfil SE Bond (CB) were applied to enamel and dentin according to the manufacturers' instructions. A resin composite cube-like structure was incrementally built on the bonded surfaces. The restored teeth were sectioned into 0.7 mm thick slices that were trimmed at enamel or dentin bonded interfaces to an hourglass shape with a cross-sectional area of approximately 0.5 mm2. Specimens were assigned to 8 groups (n = 10) according to the following factors under study: dental substrate (enamel and dentin); adhesive system (SB and CB) and treatment (10% carbamide peroxide and not bleached/control). The bleaching gel (Opalescence) was applied at the bonded interfaces for 6 hours during 14 days and after daily treatment specimens were stored in artificial saliva. Unbleached specimens were stored in artificial saliva for 14 days. Specimens were tested for tension and the data were analyzed by three-way ANOVA and Tukey's test (p < 0.05). Enamel tensile bond strength of CB was reduced after carbamide peroxide application. The bleaching treatment did not alter dentin bond strength of both adhesives. The results suggest that bleaching significantly affects bond strength of CB to enamel, but no influence on bond strength to dentin was noted for both adhesive systems.     

人工唾液浸泡对牙本质黏结耐久性的影响

目的:研究人工唾液浸泡对牙本质黏结强度和黏结界面纳米渗漏的影响.方法:选取30个无龋损人磨牙,用600目碳化硅砂纸在流水冲洗下预备牙本质黏结面,分别用3种(Prime&Bond NT,Adper Prompt和Contax)黏结剂进行黏结处理,复合树脂充填.制备黏结面积为Imm2的条形树脂牙本质试件,在人工唾液中分别浸泡1天(对照组)、90天、180天,然后进行硝酸银染色后测定微拉伸黏结强度,场发射扫描电镜下比较界面纳米渗漏.结果:唾液浸泡180天后,Prime&Bond NT和Adper Prompt黏结强度显著小于对照组,界面纳米渗漏百分比与对照组相比显著增加,Contax黏结强度和界面纳米渗漏百分比与对照组无显著变化.结论:"2步法"自酸蚀黏结剂Contax牙本质黏结界面的耐久性优于"1步法"自酸蚀黏结剂AdperPrompt和全酸蚀黏结剂Prime&Bond NT.     

Influence of saliva contamination on zirconia ceramic bonding.

OBJECTIVES: The purpose of this study was to investigate the influence of saliva contamination and cleaning methods on adhesive bonding to dental zirconia ceramic with a phosphate-monomer-containing luting resin. METHODS: After saliva immersion, airborne-particle abraded ceramic specimens were cleaned with water rinsing, with isopropanol, with phosphoric acid gel, or with additional airborne-particle abrasion. Airborne-particle abraded specimens without contamination were used as the control group. Chemical analysis of the ceramic surfaces of all groups was done using X-ray photoelectron spectroscopy (XPS). The influence of contamination and cleaning methods on ceramic bond durability was examined by tensile bond strength (TBS) testing after 3 days or 150 days water storage with 37,500 thermal cycles. RESULTS: After saliva contamination XPS revealed an organic coating which was not removed completely with water rinsing, with isopropanol, or with phosphoric acid. Using TBS testing a strong influence of contamination and cleaning methods on resin bond strength and its durability was found. SIGNIFICANCE: Saliva contamination significantly affected resin bonds to zirconia ceramic and its durability. Airborne-particle abrasion was the most effective cleaning method.     

中药-壳聚糖混合物对白念菌的抑菌效果及作为义齿稳固剂的可行性

目的 观察加入不同中药后的水溶性壳聚糖对白念菌的抑菌效果及其作为义齿稳固剂的黏结抗张强度。方法采用水煎法将6种中药提纯并烘干,配制成不同浓度,分别与壳聚糖混合,筛选最有效抑制白念菌的混合物及其最小抑菌浓度（MIC）;测定此种混合物的黏结抗张强度值,并与Protefix义齿稳固剂进行比较。采用SPSS17.0软件包对数据进行统计学分析。结果6种中药-壳聚糖混合物中,以七叶一枝花-壳聚糖混合物抗菌效果最佳,其MIC为1.563 mg/mL;七叶一枝花的黏结抗张强度值在0 h及浸入人工唾液后12 h大于protefix义齿稳固剂,其平均值及最大值大于Protefix义齿稳固剂（P<0.05）。结论七叶一枝花-壳聚糖混合物具有良好的抑制白念菌效果及黏结抗张强度。     

生物活性玻璃改性树脂粘接剂对牙本质脱矿及树脂粘接强度的影响

目的 研究生物活性玻璃（BG）改性树脂粘接剂抑制牙本质脱矿及对树脂-牙本质微拉伸粘接强度的影响。方法 将硅烷偶联剂表面处理后的BG与Single Bond 2粘接剂混合制备出30%、40%和50%的BG改性的树脂粘接剂,选择上颌前磨牙40颗,随机分为4组,阴性对照组（不添加BG）、30%BG组、40%BG组、50%BG组,每组10颗。根据分组分别采用相应BG含量的粘接剂制备树脂-牙本质粘接试件。将制备的粘接试件在37 ℃水浴中浸泡24 h后进行微拉伸粘接强度测试。每组选择1个牙片浸泡在pH 4.0的人工唾液中1周,每24 h测试溶液的pH值。结果 阴性对照组、30%BG组、40%BG组、50%BG组的粘接强度分别为（27.76±0.29）、（27.05±0.58）、（26.95±0.69）和（25.12±0.24）MPa。对照组和30%BG组的粘接强度无统计学差异（P=0.06）,和40%BG组、50%BG组有统计学差异（P=0.04,P=0.00）;30%、40%BG组的粘接强度高于50%BG组（P=0.00,P=0.00）。随着BG含量的增加,pH值也逐渐增高。结论 含有BG的树脂粘接剂可以有效抑制牙本质的脱矿,30%BG组对短期的粘接强度无明显影响,50%BG组抑制脱矿能力最强,但是粘接强度较低。