不同表面处理方法对树脂-陶瓷复合材料微观形貌和粘接强度影响研究

目的 研究不同表面处理方法对树脂-陶瓷复合材料表面微观形貌及粘接强度的影响。方法 选择树脂-陶瓷复合材料Vita Enamic（以下简称“VE”）和Lava Ultimate（以下简称“LU”）,分别切割成2种不同尺寸瓷块。每种尺寸瓷块均随机分为8组,每组6 mm×6 mm×5 mm瓷块5个、16.0 mm×4.0 mm×1.5 mm瓷块4个。其中,对照组不做任何表面处理;其余7组为处理组,分别记为氢氟酸组（氢氟酸凝胶酸蚀）,25、50、110μm玻璃珠组（不同颗粒尺寸玻璃珠喷砂）,以及25、50、110μm氧化铝组（不同颗粒尺寸氧化铝喷砂）。使用共聚焦显微镜观察并测量表面粗糙度Ra值,扫描电镜观察表面微观形貌,并进行粘接强度测试。结果 共聚焦显微镜观察显示,相较于对照组,各处理组均表现为较尖锐的片瓦状凹凸表面,其中110μm氧化铝组2种材料瓷块表面均具有明显的凹坑和沟槽。测量各组表面粗糙度Ra值也发现,110μm氧化铝组2种材料瓷块表面粗糙度Ra值均较其他组显著增高（均P <0.05）;其次为50μm氧化铝组和110μm玻璃珠组,而这两组相同材料瓷块表面粗糙度Ra值比较,差异无...     

提高氧化锆陶瓷粘接性能新技术的研究进展

随着氧化锆陶瓷的广泛应用,氧化锆陶瓷的粘接问题一直是研究热点.本文就近年来研究的几种提高氧化锆陶瓷粘接性能的技术,从3个方面来进行综述:物理处理改变氧化锆的表面形貌;化学涂层提高氧化锆的表面性能;表面清洁去除唾液等污染.在传统处理方式的基础上,总结几项研究比较热门的表面处理方式,从技术原理、临床应用等方面进行阐述,为提...     

不同类型粘接底涂剂对氧化锆陶瓷树脂粘接耐久性的影响

目的:评估不同类型粘接底涂剂对致密烧结二氧化锆陶瓷与树脂粘接耐久性的影响。方法:2.5 mm厚氧化锆陶瓷片(Vita Inceram YZ)A3染色后,高温烧结成陶瓷试件。试件表面接受4种粘接底涂剂预处理(n=10):A,Clearfil CeramicPrimer;B,Alloy Primer;C,Metal/Zirconia Primer;D,Alumina/Zirconia primer。处理后的试件与树脂水门汀(Panavia F)的剪切粘接强度在冷热循环10 000次前后测量。试件表面未处理组作为对照组。用单因素方差分析对数据进行统计学处理。结果:冷热循环前,所有实验组的粘接强度均在10 MPa以上。冷热循环显著降低了所有实验组的粘接强度(P<0.001),A组的粘接强度显著高于对照组,对照组的粘接强度又显著高于其他各组(P<0.001)。结论:粘接底涂剂Clearfil Ceramic Primer对氧化锆陶瓷表面进行预处理,能够改善氧化锆陶瓷与树脂水门汀Panavia F的粘接耐久性。     

玻璃陶瓷粘接面预处理的研究进展

玻璃陶瓷具有优良的美学特性和生物相容性,现已成为全瓷修复常用材料。修复体与树脂界面的粘接强度对远期修复效果有重要影响,而粘接强度的影响要素是修复体的表面处理。常用方式包括：酸蚀、喷砂、激光、表面处理剂等。学者们就不同表面处理方式的应用原理、最佳处理方案以及过度处理造成的损伤进行研究,并比较单一处理方式和联合处理方式对粘接强度的增强效果,以期为口腔医生临床工作提供参考。该文就玻璃陶瓷的粘接面预处理对粘接强度的影响方面的研究进展作一综述。     

不同核材料与二氧化锆陶瓷树脂粘接耐久性的研究

目的 研究不同类型核材料与二氧化锆陶瓷树脂间的粘接强度及耐久性。方法 二氧化锆陶瓷盘经研磨后通过2种自粘接型树脂水门汀（Clearfil SA Luting和RelyX U100）与不同核材料包括流动型复合树脂核材料、充填型复合树脂、钴铬合金以及牙本质进行粘接,组成个8实验组。每个实验组再分成2个亚组,分别接受0、10 000次冷热循环后进行剪切粘接强度测试。结果 核材料、树脂水门汀材料及老化条件均会对粘接强度产生明显影响（P<0.001）。冷热循环后,只有Clearfil SA Luting与钴铬合金的粘接强度没有明显降低（P>0.05）,并高于其余各核材料组（P<0.05）;Clearfil SA Luting与钴铬合金、流动型复合树脂核材料及充填型复合树脂间的粘接强度均明显高于RelyX U100相对应的粘接强度（P<0.05）,而Clearfil SA Luting和RelyX U100与牙本质间的粘接强度的差异无统计学意义（P>0.05）。结论 不同类型核材料和树脂水门汀材料能够对二氧化锆陶瓷树脂粘接耐久性产生明显影响。     

氧化锆陶瓷与三种树脂粘接剂粘接剪切强度比较

目的探讨适合牙科氧化锆陶瓷的粘接材料。方法将烧结后的氧化锆陶瓷片分为3组,每组32片,分别采用三种自酸蚀粘接剂RelyX Unicem、PanaviaTM F、Superbond C﹠B与喷砂后的氧化锆陶瓷片粘接,水浴24h和水浴30d后,测试其粘接剪切强度。数据用SAS9.12软件进行统计学分析,粘接断面用扫描电镜观察。结果 PanaviaTMF树脂粘接材料粘接强度最好,分别为（31.36±3.49）MPa（水浴24h）、（29.52±3.44）MPa（水浴30d）。Superbond C﹠B能够取得较好的初期粘接强度（31.85±3.61）MPa（水浴24h）,但水浴30d后明显下降至（21.32±2.58）MPa,P〈0.05。RelyX Unicem的初期（水浴24h）粘接强度最小为（13.29±3.05）MPa,P〈0.0001,但水浴30d后粘接强度为（12.06±2.28）MPa,未见明显降低,P（0.05。结论含有MDP磷酸单体的树脂粘接材料可以使牙科氧化锆陶瓷获得最好的粘接效果。使用不含无机填料的化学固化型纯树脂粘接剂可以取得较好的初期粘接强度但长期效果欠佳。一步法自酸蚀树脂粘接剂虽然没有很高的初期粘接强度,但粘接效果尚能持久。     

玻璃渗透氧化铝陶瓷树脂粘接耐久性的研究

目的分析含有不同类型酸性树脂单体的硅烷偶联剂及不同类型树脂粘接剂的相互组合对玻璃渗透氧化铝陶瓷树脂粘接耐久性的影响。方法使用3种硅烷偶联剂处理玻璃渗透氧化铝陶瓷的表面,使用2种双重固化树脂粘接剂与之粘接。测量试件在0和30 000次冷热循环后的粘接强度。结果冷热循环前,粘接剂A与未硅烷化处理陶瓷间的粘接强度显著低于其他硅烷化处理组,粘接剂A、B与偶联剂B处理的陶瓷间的粘接强度显著低于其与偶联剂A和C的粘接强度。冷热循环30 000次后,粘接剂A与未硅烷化处理陶瓷组的试件全部脱落;而其他硅烷化处理陶瓷组中,只有偶联剂A处理的陶瓷表面与粘接剂A和B间的粘接强度达到了5 MPa以上。结论使用10-甲基丙烯酰氧癸基磷酸酯作为硅烷水解剂的硅烷偶联剂处理的玻璃渗透氧化铝陶瓷能够与不同类型的树脂粘接剂获得较好的粘接耐久性。     

氧化物陶瓷与3种树脂水门汀初期粘接强度比较

目的:通过对2 种修复用氧化物陶瓷与3 种树脂水门汀的粘接抗剪强度比较,探讨适合牙科氧化物陶瓷的粘接材料.方法: 分别用3 种树脂水门汀Superbond C&B、RelyX~(TM)Unicem、Panavia~(TM) F与喷砂后的氧化锆(ZrO2)及三氧化二铝(Al_2O_3)陶瓷的粘接面粘接,37 ℃水浴24 h后测试其粘接抗剪强度,数据用SAS 9.12 软件进行统计学分析.结果: Al_2O_3陶瓷组间均有显著性差异(P<0.000 1), Superbond C&B粘接强度最高为(37.60±2.06) MPa. ZrO2陶瓷组中Superbond C&B与Panavia~(TM) F的粘接强度差异无显著性(P>0.05),RelyX~(TM)Unicem粘接强度最低为(13.29±3.05) MPa.结论: Superbond C&B、Panavia~(TM) F与氧化物陶瓷均具有较高的粘接强度,一步法自酸蚀粘接剂RelyX~(TM)Unicem虽然操作简便、提高了工作效率,但不如多步法系统获得的粘接强度大.     

OCC铸造陶瓷表面处理对光化学固化树脂粘接强度的影响

用光化学固化型复合树脂粘接铸造陶瓷贴面修复体时，陶瓷粘接面的预处理直接影响到粘接效果。本实验对ＯＣＣ表面作氢氟酸、硅烷偶联剂及氧化铝喷砂处理后，与Ｐｏｒｃｅｌｉｔｅ Ｄｕａｌ Ｃｕｒｅ Ｃｅｍｅｎｔ粘接，测量剪切粘接强度。结果表明：氢氟酸不适宜用于ＯＣＣ的预处理；Ｐｏｒｃｅｌｉｔｅ对ＯＣＣ无粘接性，但经硅烷处理后可获得足够的粘接力；硅烷偶联剂和５０μ氧化铝喷砂处理并用时，粘接力最大为２９０ｋｇ／ｃ     

Comparative study on the impact-sliding wear behaviour of CAD/CAM resin-ceramic materials and tooth enamel

ObjectivesTo compare the impact-sliding wear of different CAD/CAM resin-ceramic materials and tooth enamel, and explore the corresponding wear damage mechanism.MethodsHuman tooth enamel (EN), Vita ENAMIC (Vita, VE), Lava Ultimate (3 M, LU), and GC CERASMART (GC, CS) were used in this study. The hardness, elastic modulus, and roughness values of the samples were measured. Further, impact-sliding wear tests were performed in a ball-on-flat configuration with spherical zirconia antagonists and the coefficients of friction (CoF) were recorded simultaneously. Additionally, a white light interferometer was used to determine the volume losses and scanning electron microscopy was used to observe the wear morphology of the wear scars and the damage feature in the vertical sections to clarify the damage mechanism during the impact-sliding wear test.ResultsEN exhibited the highest elastic modulus and CoF, followed by VE, LU, and CS. The hardness and roughness of EN and VE were similar and were higher than those of LU and CS. Throughout the wear tests, VE exhibited the highest volume loss, whereas CS exhibited the lowest. The wear damage characteristics of VE were similar to those of EN, displaying brittle fractures of inorganic substances and plastic deformation of organic substances in the impact part, exhibiting plough marks in the sliding parts. In the case of LU and CS, the entire wear areas displayed plastic deformation of the resin matrix, exfoliation of the filler particles, and plough marks.SignificanceEnamel and polymer-infiltrated ceramic network materials exhibit similar wear damage modes. Additionally, the high-density nanocomposite resin material is the most resistant to impact-sliding wear from a tribological perspective.     

刷牙对可切削复合树脂陶瓷表面粗糙度的影响

目的 研究刷牙对可切削复合树脂陶瓷材料表面粗糙度的影响。方法 以可切削复合树脂陶瓷U（Ultimate）、H（Hyramic）、E（Enamic）、G（Grandio）为实验组,以复合树脂Z（Z350XT）和玻璃陶瓷M（Vita MarkⅡ）为对照组,分别在其刷牙前及刷牙50 000次后测量表面粗糙度（Ra）,并通过扫描电子显微镜观察表面形貌。结果 刷牙前M组（0.021±0.004 μm）与G组（0.026±0.003 μm）平均表面粗糙度Ra值较小,其余各组Ra值在0.031~0.033 μm之间。刷牙后各组表面粗糙度均增加,且刷牙前后的粗糙度差异具有统计学意义（P<0.05）。刷牙后,M组（0.033±0.007 μm）与G组（0.034±0.005 μm）的Ra值最小、U组（0.044±0.010 μm）与E组（0.043±0.004 μm）次之、H组（0.051±0.007 μm）与Z组（0.055±0.005 μm）最大。SEM显示玻璃陶瓷M组刷牙后孔隙变大。其余各组复合树脂陶瓷材料刷牙后均出现脱颗粒现象。结论 刷牙会增加各类复合树脂陶瓷材料的表面粗糙度。G组耐磨性最高,与玻璃陶瓷相似。H组耐磨性最低,与树脂相似,E组及U组的耐磨性介于陶瓷与树脂之间。     

激光预处理牙本质对树脂粘结性能影响的研究进展

近年来,为提高牙本质与树脂的粘结性能,国内外学者围绕牙本质表面处理进行了大量的研究。激光技术的快速发展为牙本质的表面处理提供了新思路。该文从树脂水门汀的分类和特点、激光预处理原理、常用激光的种类和特点、激光预处理对牙本质表面形态的影响和对树脂粘结性能的影响五个方面作一简要综述。     

评价新型粘接剂在不同粘接模式下的牙本质粘接性能

目的评价1种新型单瓶型多模式粘接剂在不同粘接模式下与牙本质的粘接强度和粘接耐久性。方法制作3组牙本质/复合树脂粘接试件,其中每组牙本质在粘接前接受不同的表面调节。包括不处理(空白对照),Singlebond Universal粘接剂自酸蚀模式下调节牙本质,Singlebond Universal粘接剂在酸蚀冲洗模式下调节牙本质。测量各组粘接试件水储24 h和180 d的微拉伸粘接强度值并进行统计分析。以扫描电子显微镜观察各组试件的粘接界面。结果不论老化前还是老化后,3组间的粘接强度均存在显著性差异,其中空白组的粘接强度值最低,另两组间则无显著性差异。人工老化使空白组的粘接强度值显著下降,而对另两组则并无显著影响。结论 Singlebond Universal粘接剂在自酸蚀粘接模式和酸蚀冲洗粘接模式下均能够形成与牙本质良好的粘接。     

不同粘接剂对烤瓷瓷面与金属托槽间剪切强度影响的体外研究

目的 研究不同粘接剂对烤瓷瓷面与金属托槽间剪切强度的影响.方法 40个烤瓷瓷面经打磨、氢氟酸酸蚀、冲洗干燥、硅烷偶联剂处理瓷面后,再根据使用粘接剂的不同分为A组:光固化复合树脂粘接剂、B组:单组份化学固化复合树脂粘接剂、C组:树脂改良型光固化玻璃离子粘接剂、D组:双组份化学固化复合树脂粘接剂.将40个金属托槽粘接于烤瓷瓷面,经水浴孵化24 h后测得样本剪切强度,并进行统计分析.结果 A组剪切强度大于其他组(P＜0.05),C组剪切强度小于B组(P＜0.05),D组与B、C组剪切强度差异无统计学意义(P＞0.05).结论 光固化复合树脂粘接剂可获得最大的剪切强度,树脂改良型光固化玻璃离子粘接剂对金属托槽与烤瓷瓷面的粘接效果欠佳.     

锶强化生物活性玻璃牙釉质粘合树脂的抗菌性能与机械性能测试

目的通过向正畸牙釉质粘合树脂中添加锶强化生物活性玻璃,并对其抗菌性能及机械性能进行测试,寻求合适的添加比例,为正畸临床应用提供理论依据。方法分别将质量分数为1%、2%、3%、4%、5%的锶强化生物活性玻璃掺入到牙釉质粘合树脂中作为实验组,分别为1、2、3、4及5组,未掺入锶强化生物活性玻璃的牙釉质粘合树脂作为对照组,即0组。采用抑菌环法和贴膜法对以上各组进行抑菌活性测试;应用万能试验机对以上各组的剪切强度进行测试,观察并记录托槽脱落后牙面牙釉质粘合树脂残留指数(adhesive resin residual,ARI)。结果各实验组及对照组均未出现抑菌环,实验组4和5组的抗菌率达到99.9%,具有强抗细菌作用。实验各组的剪切强度与对照组相比,均有显著性差异(P<0.05)。实验各组之间比较,随掺入比例增加,剪切强度呈现降低趋势,但无统计学差异(P>0.05)。实验各组剪切强度均在临床可接受的剪切强度范围内,能够满足正畸临床要求。实验各组及对照组牙面均有牙釉质粘合树脂残留,ARI计分均在2~4分之间,各组间ARI计分比较无统计学差异(P>0.05)。结论掺入4%质量分数的锶强化生物活性玻璃的正畸牙釉质粘合树脂既表现出强抗菌作用,剪切强度又能够达到正畸临床需要,并对釉质表面粘合树脂的残留量无影响。     

表面不同处理方法对POPO纤维桩粘接固位力的影响

目的讨论不同表面处理方法对POPO纤维桩粘接固位力的影响。方法取50根POPO纤维桩,根据表面不同处理方法随机分为5组,每组10根。A组：不处理;B组：硅烷化处理60 s;C组：酸蚀处理30 s;D组：酸蚀处理60 s;E组：酸蚀处理120 s。选取45颗离体前磨牙截冠后随机分到5个实验组,树脂粘接纤维桩于根管内,包埋后在电子万能试验机上进行拉力测试。扫描电镜（SEM）观察处理后POPO纤维桩的表面形态。结果不同表面处理方法时纤维桩粘接力差异有统计学意义（P<0.05）,D组的粘接力最大,为（207.33±7.58）N。D组和E组间粘接固位力差异有统计学意义（P=0.027）,D组和C组间粘接固位力差异无统计学意义（P=0.112）。SEM观察处理后纤维桩的表面树脂基质粗糙度及纤维暴露数量有明显改变。结论不同表面处理方法增强了POPO纤维桩的粘接固位力。     

义齿稳固剂的研究进展

义齿稳固剂作为辅助活动义齿固位及稳定的有效制剂,在患者中的认知率仍不足.本文就义齿稳固剂的研究进展进行综述,指出义齿稳固剂可以增加义齿稳定性和适合性.     

新型抗菌性牙本质粘接剂抗菌性和粘接性能的研究

目的：研究甲基丙烯酸十二烷基二甲铵（dimethylaminododecyl methacrylate,DMADDM）对牙本质粘接系统的粘接强度和菌斑生物膜的影响。方法：合成 DMADDM,并以质量分数为10％的比例添加到商品化的牙本质粘接剂中作为实验组,商品化的牙本质粘接剂作为对照组。使用人唾液培养所得到牙菌斑全菌生物膜模型来研究粘接剂的抗菌性,检测死/活细菌染色;检测蒸馏水和口腔全菌生物膜培养14 d前后,实验组和对照组粘接强度的差异。结果：添加 DMADDM的粘接系统显著降低了菌斑生物膜活性;蒸馏水浸泡14 d对粘接强度没有明显影响（P＞0．05）,菌斑生物膜浸泡14 d 后,对照组粘接强度明显下降（P＜0．05）,实验组没有明显变化（P＞0．05）。结论：含有 DMADDM的牙本质粘接系统具有很强的抗菌性,能够抵抗口腔环境对粘接性能的影响,具有一定的临床应用前景。     

光固化胶粘剂性能的初步研究

目的：制备一种光固化纳米胶粘剂,对其性能进行初步研究。方法：正交法制备出多个胶粘剂样品,讨论各个因素对材料力学性能的影响,探索合适的配方比例和工艺参数。结果：光固化胶粘剂最优配比为引发剂Darocur1173含量占1％,纳米SiO2含量占50％,基质树脂与稀释单体（Bis—GMA：TEGDMA）的比例为1：1。结论：制备的光固化胶粘剂配方的综合性能最优,可应用于临床。