Internal Curing Effect of Pre-Soaked Zeolite Sand on the Performance of Alkali-Activated Slag

This study clarifies the effects of pre-soaked zeolite sand as an internal curing material on the hydration, strength, autogenous shrinkage, and durability of alkali-activated slag (AAS) mortars. The liquid-to-binder ratio (L/b) of all of the AAS mortars was 0.55. Sodium hydroxide solution was used as an alkali activator and an internal curing liquid. Calcined zeolite and natural zeolite sand replaced the standard sand at 15% and 30%, respectively. The setting time, autogenous shrinkage, compressive strength, ultrasonic pulse velocity, and surface electrical resistivity were tested. The following conclusions were drawn: (1) The addition of zeolite significantly reduces the autogenous shrinkage of AAS mortar. Compared with the control group, 30% calcined zeolite reduced the autogenous shrinkage by 96.4%. Moreover, the autogenous shrinkage of the AAS mortars was noticed in two stages (a variable temperature stage and an ambient temperature stage), and the two stages split at one day of age. (2) The compressive strength of all of the specimens increased as the zeolite sand content increased, and the highest compressive strength was obtained for AAS combined with 30% natural zeolite sand. (3) Internal curing accelerated the formation of the second peak of heat flow and reduced the accumulated heat release. (4) Calcined zeolite sand delayed the setting time of the AAS mortars. (5) The addition of zeolite significantly reduced the surface electrical resistivity of the AAS mortars. In summary, zeolite sand is extremely useful as an internal curing agent to reduce autogenous shrinkage and to increase the compressive strength of AAS mortars.     

Effect of Sulphur-Containing Tailings Content and Curing Temperature on the Properties of M32.5 Cement Mortar

The effect of the dosage of sulphur-containing tailings (STs) and curing temperature on the properties of M32.5 cement mortar was studied in this work. An experimental study was conducted to evaluate the effects of STs with different substitution ratios (0, 10%, 20%, 30%, 40%) on the compressive strength experiment, fluidity, expansion ratio, and pore structure of M32.5 cement mortar. The results showed that the addition of STs reduced the fluidity of mortar, and the fluidity decreased with the increase of the STs dosage. The compressive strength of mortars increased at a lower substitution rate (0~20%) but decreased at a higher substitution rate (>20%). Ettringite peaks and new sulfate peaks were found by X-ray diffraction (XRD) analysis. Scanning electron microscope (SEM) observation of the microstructure showed that a large number of hydrated products, such as ettringite, formed and filled in the interstitial space, which was conducive to the development of strength. The optimal STs replacement ratio of river sand was 10%. Then, the performance of mortar at curing temperatures of 23 ± 1, 40, 60, and 80 °C was further investigated under the optimal STs replacement ratio. Under high-temperature curing conditions, the early strength of M32.5 cement mortar with STs increased greatly, but the late strength decreased gradually with the increase in curing temperature. The early strength development of the mortar mainly depended on the high speed of hydration reaction, and the late strength variation was mainly affected by hydration products and the pore size distribution. After comprehensive consideration, the optimal curing temperature of M32.5 cement mortar with STs was 40 °C.     

Effect of Pre-Wetting Recycled Mortar Aggregate on the Mechanical Properties of Masonry Mortar

In this research we evaluated the use of recycled fine mortar aggregate (RFMA) as a fine aggregate for new masonry mortar creation. The pre-wetting effect on the aggregate before creating the mixture was analyzed as a method to reduce its absorption potential. A control mixture of conventional mortar and two groups of recycled mortars were designed with a partial replacement of natural sand by RFMA (pre-wetted and not pre-wetted) performed in different proportions. The results established that the pre-wetting process allows a reduction in the amount of water required during the creation of new mixtures, regulating the water/cement (W/C) ratio and improving the properties of recycled mortars such as air content, fresh and hardened densities, and compressive and adhesive strength for all substitution levels. Mortar made with a 20% substitution and pre-wetted until it was at 67% of its absorption capacity displayed adhesive values higher than the ones shown by the reference mortar. The pre-wetting process proves to be an easy performance technique; it is inexpensive, environmentally friendly, and the most valuable fact is that specialized equipment is not necessarily needed. This process is the most profitable option for improving RFMA exploitation and reuse.     

Properties of Blended Cement Containing Iron Tailing Powder at Different Curing Temperatures

The properties of blended cement containing 0%, 20%, and 50% iron tailing powder (ITP) at 20 °C and 60 °C were investigated by determining the hydration heat, microstructure, and compressive strength. The addition of ITP decreases the exothermic rate and cumulative hydration heat of blended cement at 20 °C. The high temperature increases the hydration rate and leads to the hydration heat of blended cement containing 20% ITP higher than that of Portland cement. Increasing the amount of ITP decreases the non-evaporable water content and Ca(OH)₂ content as well as compressive strength at both of the two studied temperatures. The addition of ITP coarsens the early-age pore structure but improves the later-age pore structure at 20 °C. The high temperature significantly improves the early-age properties of blended cement containing ITP, but it is detrimental to the later-age properties development. The reaction of ITP is limited even at high temperature. The large ITP particles bond poorly with surrounding hydration products under early high-temperature curing condition. The properties of blended cement containing a large amount of ITP are much poorer at high temperature.     

Influence of Cement Replacement with Sewage Sludge Ash (SSA) on the Heat of Hydration of Cement Mortar

The amount of fly ash from the incineration of sewage sludge is increasing all over the world, and its utilization is becoming a serious environmental problem. In the study, a type of sewage sludge ash (SSA) collected directly from the municipal sewage treatment plant was used. Five levels of cement replacement (2.5%, 5%, 7.5%, 10% and 20%) and unchanged water-to-binder (w/b) ratio (0.55) were used. The purpose of the study was to evaluate the effect of sewage sludge ash (SSA) on the hydration heat process of cement mortars. The heat of the hydration of cement mortars was monitored by the isothermal calorimetric method for 7 days at 23 °C. The analysis of chemical composition and particle size distribution was performed on the tested material. The tests carried out have shown that SSA particles have irregular grain morphology and, taking into account the chemical composition consists mainly of oxides such as CaO, P₂O₅, SiO₂ and Al₂O₃. The concentration of these compounds affects the hydration process of cement mortars doped with SSA. In turn, the content of selected heavy metals in the tested ash should not pose a threat to the environment. Calorimetric studies proved that the hydration process is influenced by the presence of SSA in cement mortars. The studies showed that the rate of heat generation decreased (especially in the initial setting period) with the increasing replacement of cement by SSA, which also reduced the amount of total heat compared to the control cement mortar. With increasing mass of the replacement of cement with SSA up to 20%, the 7-day compressive strength of the mortar samples decreases.     

Creep and Shrinkage Behaviour of Disintegrated and Non-Disintegrated Cement Mortar

One way to prevent cement from ending up in landfills after its shelf life is to regain its activity and reuse it as a binder. As has been discovered, milling by planetary ball mill is not effective. Grinding by collision is considered a more efficient way to refine brittle material and, in the case of cement, to regain its activity. There has been considerable research regarding the partial replacement of cement using disintegrated cement in mortar or concrete in the past few decades. This article determines and compares the creep and shrinkage properties of cement mortar specimens made from old disintegrated, old non-disintegrated, and new non-disintegrated Portland cement. The tests show that the creep strains for old disintegrated and old non-disintegrated cement mortars are close, within a 2% margin of each other. However, the creep strains for new non-disintegrated cement mortar are 30% lower. Shrinkage for old disintegrated and non-disintegrated cement mortar is 20% lower than for new non-disintegrated cement mortar. The research shows that disintegration is a viable procedure to make old cement suitable for structural application from a long-term property standpoint. Additionally, it increases cement mortar compressive strength by 49% if the cement is disintegrated together with sand.     

Recycling Blast Furnace Ferronickel Slag as a Replacement for Paste in Mortar: Formation of Carboaluminate,Reduction of White Portland Cement,and Increase in Strength

Blast furnace ferronickel slag (BFFS) is generated in the production of ferronickel alloys and is used as cement replacement in concrete or mortar. The effectivity in reducing cement consumption and improving performance are limited. By referring to the paste replacement method, this work used BFFS to replace an equal volume of the white Portland cement paste to obtain greater performance enhancement. BFFS was used with five levels of replacement (0%, 5%, 10%, 15%, 20%) and four water-to-cement ratios (0.40, 0.45, 0.50, 0.55) were designed. Fluidity, mechanical strength, hydration products, and pore structure of every mixture were measured. The results showed that the workability of the mortars decreased due to the reduced volume of water, but the 28-day compressive strength of the mortars increased, and the cement content of the mortars was also reduced by 33 wt %. The X-ray diffraction (XRD) patterns revealed that there existed a carboaluminate phase, and the presence of the ettringite was stabilized, indicating that the accumulating amount of the hydration products of the mortar increased. Furthermore, the BFFS could consume the portlandite and free water to form a higher amount of chemically bound water due to its pozzolanic activity. A high degree of hydration and a large volume of the hydration products refined the porosity of the hardened mortars, which explained the enhancement of the strength of the mortars. Compared to the cement replacement method, the paste replacement method was more effective in preparing eco-friendly mortar or concrete by recycling BFFS for reducing the cement content of the mortar while improving its strength.     

Effects of a Natural Mordenite as Pozzolan Material in the Evolution of Mortar Settings

This paper shows the results of a study focused on the evolution and properties of mortars made with a mixture of portland cement (PC) and natural mordenite (Mor). To begin, samples of mordenite, cement and sand were studied with X-ray diffraction (XRD), X-ray fluorescence (XRF) and granulometric analysis (GA). Next, mortars with a ratio of 75% PC and 25% mordenite were prepared to determine their initial and final setting times, consistency and density. Continuing, the density, weight and compressive strength of the specimens were determined at 2, 7, 28, 90 and 365 days. Finally, the specimens were studied using SEM, XRD and XRF. The results of the study of the mordenite sample showed a complex constitution where the major mineral component is mordenite, and to a lesser degree smectite (montmorillonite), halloysite, illite, mica, quartz, plagioclase and feldspar, in addition to altered volcanic glass. Tests with fresh cement/mordenite mortar (CMM) showed an initial setting time of 320 min and a final setting time of 420 min, much longer than the 212–310 min of portland cement mortar (PCM). It was established that the consistency of the cement/mordenite mortar (CMM) was greater than that of the PCM. The results of the density study showed that the CMM has a lower density than the PCM. On the other hand, the density of cement/mordenite specimens (CMS) was lower than that of portland cement specimens (PCS). The CMS compressive strength studies showed a significant increase from 18.2 MPa, at 2 days, to 72 MPa, at 365 days, with better strength than PCS at 28 and 365 days, respectively. XRD, XRF and SEM studies conducted on CMS showed a good development of primary and secondary tobermorite, the latter formed at the expense of portlandite; also, ettringite developed normally. This work proves that the partial replacement of PC by mordenite does not have a negative effect on the increase in the mechanical strength of CMS. It indicates that the presence of mordenite inhibits the spontaneous hydration of C₃A and controls the anomalous formation of ettringite (Ett). All this, together with the mechanical strength reported, indicates that mordenite has a deep and positive influence on the evolution of the mortar setting and is an efficient pozzolan, meaning it can be used in the manufacture of mortars and highly resistant pozzolanic cement, with low hydration heat, low density, stability in extremely aggressive places and a low impact on the environment.     

Properties of Cement Mortar by Use of Hot-Melt Polyamides as Substitute for Fine Aggregate

This paper presents an experimental study on use of hot-melt polyamide (HMP) to prepare mortar specimens with improved crack healing and engineering properties. The role of HMP in the crack repairing of cement mortar subjected to several rounds of heat treatment was investigated. Compatibility between HMP and hydraulic cement was investigated through X-ray diffraction (XRD) and Fourier transform infrared spectra (FTIR) technology. Mortar specimens were prepared using standard cement mortar mixes with HMP at 1%, 3% and 5% (by volume) for fine aggregate substitute. After curing for 28 days, HMP specimens were subjected to heating at temperature of 160 °C for one, two, and three days and then natural cooling down to ambient temperature. Mechanical and durability properties of the heated HMP mortars were evaluated and compared with those of the corresponding mortars without heating. The microscopic observation of the interfacial transition zone (ITZ) of HMP mortar was conducted through environmental scanning electron microscopy (ESEM). Results reveal that incorporation of HMP improves the workability of the HMP/cement binder while leading to decrease in compressive strength and durability. The heated HMP mortars after exposure to heating for one, two, and three days exhibit no obvious change in compressive strength while presenting notable increase in flexural strength and durability compared with the corresponding mortars without heating. The XRD, FTIR and ESEM analyses indicate that no obvious chemical reaction occurs between HMP and hydraulic cement, and thus the self-repairing for interfacial micro-crack in HMP/cement composite system is ascribed to the physical adhesion of HMP to cement matrix rather than the chemical bonding between them.     

Recycled Cellulose Fiber Reinforced Plaster

This paper aims to develop recycled fiber reinforced cement plaster mortar with a good workability of fresh mixture, and insulation, mechanical and adhesive properties of the final hardened product for indoor application. The effect of the incorporation of different portions of three types of cellulose fibers from waste paper recycling into cement mortar (cement/sand ratio of 1:3) on its properties of workability, as well as other physical and mechanical parameters, was studied. The waste paper fiber (WPF) samples were characterized by their different cellulose contents, degree of polymerization, and residues from paper-making. The cement to waste paper fiber mass ratios (C/WPF) ranged from 500:1 to 3:1, and significantly influenced the consistency, bulk density, thermal conductivity, water absorption behavior, and compressive and flexural strength of the fiber-cement mortars. The workability tests of the fiber-cement mortars containing less than 2% WPF achieved optimal properties corresponding to plastic mortars (140–200 mm). The development of dry bulk density and thermal conductivity values of 28-day hardened fiber-cement mortars was favorable with a declining C/WPF ratio, while increasing the fiber content in cement mortars led to a worsening of the water absorption behavior and a lower mechanical performance of the mortars. These key findings were related to a higher porosity and weaker adhesion of fibers and cement particles at the matrix-fiber interface. The adhesion ability of fiber-cement plastering mortar based on WPF samples with the highest cellulose content as a fine filler and two types of mixed hydraulic binder (cement with finely ground granulated blast furnace slag and natural limestone) on commonly used substrates, such as brick and aerated concrete blocks, was also investigated. The adhesive strength testing of these hardened fiber-cement plaster mortars on both substrates revealed lime-cement mortar to be more suitable for fine plaster. The different behavior of fiber-cement containing finely ground slag manifested in a greater depth of the plaster layer failure, crack formation, and in greater damage to the cohesion between the substrate and mortar for the observed time.     

Influence of the Type of Cement on the Action of the Admixture Containing Aluminum Powder

The study of the effect of cement type on the action of an admixture increasing the volume of concrete (containing aluminum powder), used in amounts of 0.5–1.5% of cement mass, was presented. The tests were carried out on cement mortars with Portland (CEM I) and ground granulated blast-furnace slag cement (CEM III). The following tests were carried out for the tested mortars: the air content in fresh mortars, compressive strength, flexural strength, increase in mortar volume, bulk density, pore structure evaluation (by the computer image analysis method) and changes in the concentration of OH⁻ ions during the hydration of used cements. Differences in the action of the tested admixture depending on the cement used were found. To induce the expansion of CEM III mortars, a smaller amount of admixture is required than in the case of CEM I cement. Using the admixture in amounts above 1% of the cement mass causes cracks of mortars with CEM III cement due to slow hydrogen evolution, which occurs after mortar plasticity is lost. The use of an aluminum-containing admixture reduces the strength properties of the cement mortars, the effect being stronger in the case of CEM III cement. The influence of the sample molding time on the admixture action was also found.     

Fresh and Rheological Performances of Air-Entrained 3D Printable Mortars

The effect of air-entraining admixture (AEA) on the fresh and rheological behavior of mortars designed to be used in 3D printers was investigated. Blast furnace slag, calcined kaolin clay, polypropylene fiber, and various chemical additives were used in the mortar mixtures produced with Super White Cement (CEM I 52.5 R) and quartz sand. In addition to unit weight, air content, and compressive strength tests, in order to determine the stability of 3D printable mortar elements created by extruding layer by layer without any deformation, extrudability, buildability, and open time tests were applied. Fresh and rheological properties of 3D printable mortars were also determined. It was concluded that the addition of AEA to the mortars decreased the unit weight, viscosity, yield, and compressive strength, but increased the air content, spread diameter, initial setting time, and thixotropy of 3D printable mortar. It is recommended to develop a unique chemical admixture for 3D printable mortars, considering the active ingredients of the chemical additives that affect fresh and rheological performance of mortar such as superplasticizer, viscosity modifying, and cement hydration control.     

Microstructural,Mechanical and Radiological Characterization of Mortars Made with Granite Sand

The study reported the effect of granite sand on strength and microstructural developments in mortars prepare from OPC with a high coal fly ash (FA) content or from hybrid alkaline cements. The radiological behaviour of the resulting mortars was compared to materials prepared with siliceous sand (with particles sizes of <2 mm) and the relationship between such radiological findings and mortar microstructure and strength was explored. A new method for determining natural radionuclides and their activity concentration Index (ACI) on cement mortars (specifically to solid 5-cm cubic specimens) was applied and validated. The microstructural changes associated in mortars have no effect on mortar radiological content measurements. The mortars with granite sand exhibited very high ACI > 0.96, which would ultimately limit their use. A conclusion of interest is that where information is at hand on the starting materials (OPC, FA, sand, admixtures), their proportions in the mortar and the mixing liquid content (water or alkaline activators) their radiological content is accurately predicted. The inference is that a mortar’s radiological content and ACI can be known prior to mixing, providing a criterion for determining its viability. That in turn lowers environmental risks and the health hazards for people in contact with such materials.     

Comparative Study of Effects of Air-Entraining Plasticizing Admixture and Lime on Physical and Mechanical Properties of Masonry Mortars and Plasters

This article presents research on selected physical and mechanical properties of cement-based plasters and masonry mortars with consistency-improving additives, namely, traditional hydrated lime and a plasticizing and aerating mixture (APA), which, in practice, is often considered to be a lime substitute. Comparative analysis of the properties of mortars with alternative additives—lime or APA—was carried out, taking into consideration possible effects of cement, as two types of Portland cement were used for the research. For fresh mortar, mixture consistency, air content, resistance to segregation, and water retention were determined. Tests on hardened mortars included tests of porosity and impermeability, depth of penetration of water under pressure, drying shrinkage, as well as compressive and bending strength, modulus of elasticity, and adhesion of mortars to the base. In addition, research has shown that cement–lime mortars and cement mortars with APA admixture of similar consistency in the fresh state are characterized by significantly different properties. The results show, in most of the features analyzed, more favorable properties of mortars with the use of traditional lime. For shrinkage only, the use of admixture turned out to be more advantageous.     

Effect of High-Dispersible Graphene on the Strength and Durability of Cement Mortars

Graphene’s outstanding properties make it a potential material for reinforced cementitious composites. However, its shortcomings, such as easy agglomeration and poor dispersion, severely restrict its application in cementitious materials. In this paper, a highly dispersible graphene (TiO₂-RGO) with better dispersibility compared with graphene oxide (GO) is obtained through improvement of the graphene preparation method. In this study, both GO and TiO₂-RGO can improve the pore size distribution of cement mortars. According to the results of the mercury intrusion porosity (MIP) test, the porosity of cement mortar mixed with GO and TiO₂-RGO was reduced by 26% and 40%, respectively, relative to ordinary cement mortar specimens. However, the TiO₂-RGO cement mortars showed better pore size distribution and porosity than GO cement mortars. Comparative tests on the strength and durability of ordinary cement mortars, GO cement mortars, and TiO₂-RGO cement mortars were conducted, and it was found that with the same amount of TiO₂-RGO and GO, the TiO₂-RGO cement mortars have nearly twice the strength of GO cement mortars. In addition, it has far higher durability, such as impermeability and chloride ion penetration resistance, than GO cement mortars. These results indicate that TiO₂-RGO prepared by titanium dioxide (TiO₂) intercalation can better improve the strength and durability performance of cement mortars compared to GO.     

Properties of Chemically Combusted Calcium Carbide Residue and Its Influence on Cement Properties

Calcium carbide residue (CCR) is a waste by-product from acetylene gas production. The main component of CCR is Ca(OH)₂, which can react with siliceous materials through pozzolanic reactions, resulting in a product similar to those obtained from the cement hydration process. Thus, it is possible to use CCR as a substitute for Portland cement in concrete. In this research, we synthesized CCR and silica fume through a chemical combustion technique to produce a new reactive cementitious powder (RCP). The properties of paste and mortar in fresh and hardened states (setting time, shrinkage, and compressive strength) with 5% cement replacement by RCP were evaluated. The hydration of RCP and OPC (Ordinary Portland Cement) pastes was also examined through SEM (scanning electron microscope). Test results showed that in comparison to control OPC mix, the hydration products for the RCP mix took longer to formulate. The initial and final setting times were prolonged, while the drying shrinkage was significantly reduced. The compressive strength at the age of 45 days for RCP mortar mix was found to be higher than that of OPC mortar and OPC mortar with silica fume mix by 10% and 8%, respectively. Therefore, the synthesized RCP was proved to be a sustainable active cementitious powder for the strength enhanced of building materials, which will result in the diversion of significant quantities of this by-product from landfills.     

Accelerated Curing for Glass-Based Mortars Using Water at 80 °C

The substitution of river sand with glass aggregate (GA) and cement with glass powder (GP) is a mainstream method to recycle waste glass. Traditionally, standard curing was widely used for glass-based mortars. However, it is time-consuming and cannot address low mechanical strengths of the early-age mortars. Therefore, the effect of water curing at 80 °C on the properties of GA mortars is investigated. Furthermore, the effect of the GP size is also considered. Results show that compared with the expansion of alkali-silica reaction (ASR), water curing at 80 °C has a negligible effect on the volume change. Moreover, the compressive strength of GA mortars under 1-day water curing at 80 °C is comparable with that under 28-day water curing at 20 °C. Therefore, the 1-day water curing at 80 °C is proposed as an accelerated curing method for GA mortars. On the other hand, the addition of GP with the mean size of 28.3 and 47.9 μm can effectively mitigate the ASR expansion of GA mortars. Compared with the size of 28.3 μm, GA mortars containing GP (47.9 μm) always obtain higher compressive strength. In particular, when applying the 1-day water curing at 80 °C, GA mortars containing GP (47.9 μm) can even gain higher strength than those containing fly ash.     

The Effect of Fine-Ground Glass on the Hydration Process and Properties of Alumina-Cement-Based Composites

This paper discusses studies regarding the impact of fine-ground glass additives on the hydration and properties of alumina cement pastes and mortars. Fine-ground glass was added to pastes and mortars instead of high-alumina cement and calcium aluminate cement in quantities of 5% and 10%. The findings are inconclusive as to the impact of glass on the properties of tested alumina cement types. The effect produced via the addition of glass instead of cement depends on the type of alumina cement used. Adding fine-ground glass to high-alumina cement enhances the paste’s density while improving paste and mortar strength. Using the same additive for calcium aluminate cement reduces its density and strength. The addition of glass to high-alumina cement adversely affects its strength at higher temperatures.     

The Effects of Temperature Curing on the Strength Development,Transport Properties,and Freeze-Thaw Resistance of Blast Furnace Slag Cement Mortars Modified with Nanosilica

This investigation studies the effects of hot water and hot air curing on the strength development, transport properties, and freeze-thaw resistance of mortars incorporating low-heat blast furnace slag cement and nanosilica (NS). Mortar samples were prepared and stored in ambient conditions for 24 h. After demolding, mortar samples were subjected to two different hot curing methods: Hot water and hot air curing (40 °C and 60 °C) for 24 h. For comparison purposes, mortar reference mixes were prepared and cured in water and air at ambient conditions. Strength development (from 1 to 180 days), capillary water porosity, water sorptivity, and freeze-thaw resistance were tested after 180 days of curing. The experimental results showed that both curing regimes accelerate the strength development of mortars, especially in the first seven days of hydration. The highest early strengths were reported for mortars subjected to a temperature of 60 °C, followed by those cured at 40 °C. The hot water curing regime was found to be more suitable, as a result of more stable strength development. Similar findings were observed in regard to durability-related properties. It is worth noting that thermal curing can more efficiently increase strength in the presence of nanosilica, suggesting that NS is more effective in enhancing strength under thermal curing.     

Properties and Strength Prediction Modeling of Green Mortar with Brick Powder Subjected to a Short-Term Thermal Shock at Elevated Temperatures

The cement industry is responsible for 8% of global CO₂ production. Therefore, a clear trend has been observed recently to replace to some extent the main binder of cement composites with environmentally friendly or recycled materials with a lower carbon footprint. This paper presents the effect of brick powder (BP) on the physico-chemical and mechanical properties of cement mortars. The effect of a short-term thermal shock on morphology and strength properties of green mortars was investigated. BP addition caused increase in porosity and decrease in compressive and flexural strength of mortars. The best results were obtained for samples with 5% wt. BP addition. Above this addition the strength decreased. The mechanical performance of the samples subjected to thermal loading increased compared to the reference samples, which is the result of a process called as the “internal autoclaving”. The BP addition positively affects the linear shrinkage, leading to its reduction. The lowest linear shrinkage value was achieved by the mortar with the highest BP addition. An intelligent modeling approach for the prediction of strength characteristics, depending on the ultrasonic pulse velocity (UPV) is also presented. To solve the model problem, a supervised machine-learning algorithm in the form of an SVM (support vector machines) regression approach was implemented in this paper. The results indicate that BP can be used as a cement replacement in cement mortars in limited amounts. The amount of the additive should be moderate and tuned to the features that mortars should have.