Chemical Evaluation of Energy Dispersive X-ray Spectroscopy Analysis of Different Failing Dental Implant Surfaces: A Comparative Clinical Trial

The aim of the present study is to compare two different implant surface chemistries of failing dental implants. Sixteen patients (mean age: 52 ± 8.27 with eight females and eight males) and 34 implants were included in the study. Group-I implants consisted of a blasted/etched surface with a final process surface, while Group-II implants consisted of the sandblasted acid etching (SLA) method. The chemical surface analysis was performed by the energy dispersive X-ray spectroscopy (EDX) method from coronal, middle, and apical parts of each implant. Titanium (Ti) element values were found to be 20.22 ± 15.7 at.% in Group I and 33.96 ± 13.62 at.% in Group-II in the middle of the dental implants. Aluminum (Al) element values were found to be 0.01 ± 0.002 in Group-I and 0.17 ± 0.28 at.% in Group II in the middle of the dental implants, and statistically significant differences were found between the groups for the Al and Ti elements in the middle of the dental implants (p < 0.05). There was a statistically significant difference for the Ti, Al, O, Ca, Fe, P, and Mg elements in the coronal, middle, and apical parts of the implants in the intragroup evaluation (p < 0.05). It is reported that different parts of the implants affected by peri-implant inflammation show different surface chemistries, from coronal to apical, but there is no difference in the implants with different surfaces.     

Stress Distribution Pattern in Zygomatic Implants Supporting Different Superstructure Materials

The aim of this study was to assess and compare the stress–strain pattern of zygomatic dental implants supporting different superstructures using 3D finite element analysis (FEA). A model of a tridimensional edentulous maxilla with four dental implants was designed using the computer-aided design (CAD) software. Two standard and two zygomatic implants were positioned to support the U-shaped bar superstructure. In the computer-aided engineering (CAE) software, different materials have been simulated for the superstructure: cobalt–chrome (CoCr) alloy, titanium alloy (Ti), zirconia (Zr), carbon-fiber polymers (CF) and polyetheretherketone (PEEK). An axial load of 500 N was applied in the posterior regions near the zygomatic implants. Considering the mechanical response of the bone tissue, all superstructure materials resulted in homogeneous strain and thus could reconstruct the edentulous maxilla. However, with the aim to reduce the stress in the zygomatic implants and prosthetic screws, stiffer materials, such Zr, CoCr and Ti, appeared to be a preferable option.     

Relevant Aspects of Titanium and Zirconia Dental Implants for Their Fatigue and Osseointegration Behaviors

Osseointegration capacity and good mechanical behavior are key to the success of the dental implant. In many investigations, comparisons of properties are made using different dental implant designs and therefore the results can be influenced by the macrodesign of the dental implant. In this work, studies were carried out with the same dental implant model using different roughness and different materials—commercially pure titanium (grade 4) and zirconia. For this purpose, 80 smooth passivated titanium (Ti), 80 smooth zirconia (ZrO₂), and 80 rough passivated titanium (Ti-R) dental implants were used. The samples were characterized by their roughness, wettability, surface energy, residual stresses, and fatigue behavior. The implants were implanted in minipigs for 4 and 12 weeks. The animals were sacrificed, and histological studies were carried out to determine the osseointegration parameters for each of the implantation times. Ti and ZrO₂ dental implants have very similar wettability and surface energy properties. However, the roughness causes a decrease in the hydrophilic character and a decrease of the total surface energy and especially the dispersive component, while the polar component is higher. Due to the compressive residual stresses of alumina sandblasting, the rough dental implant has the best fatigue behavior, followed by Ti and due to the lack of toughness and rapid crack propagation the ZrO₂ implants have the worst fatigue behavior. The bone index contact (BIC) values for 4 weeks were around 25% for Ti, 32% for ZrO₂, and 45% for Ti-R. After 12 weeks the Ti dental implants increased to 42%, for Ti, 43% for ZrO₂, and an important increase to 76% was observed for Ti-R implants. In vivo results showed that the key factor that improves osseointegration is roughness. There was no significant difference between ZrO₂ and Ti implants without sandblasting.     

Biological Safety Evaluation and Surface Modification of Biocompatible Ti–15Zr–4Nb Alloy

We performed biological safety evaluation tests of three Ti–Zr alloys under accelerated extraction condition. We also conducted histopathological analysis of long-term implantation of pure V, Al, Ni, Zr, Nb, and Ta metals as well as Ni–Ti and high-V-containing Ti–15V–3Al–3Sn alloys in rats. The effect of the dental implant (screw) shape on morphometrical parameters was investigated using rabbits. Moreover, we examined the maximum pullout properties of grit-blasted Ti–Zr alloys after their implantation in rabbits. The biological safety evaluation tests of three Ti–Zr alloys (Ti–15Zr–4Nb, Ti–15Zr–4Nb–1Ta, and Ti–15Zr–4Nb–4Ta) showed no adverse (negative) effects of either normal or accelerated extraction. No bone was formed around the pure V and Ni implants. The Al, Zr, Nb, and Ni–Ti implants were surrounded by new bone. The new bone formed around Ti–Ni and high-V-containing Ti alloys tended to be thinner than that formed around Ti–Zr and Ti–6Al–4V alloys. The rate of bone formation on the threaded portion in the Ti–15Zr–4Nb–4Ta dental implant was the same as that on a smooth surface. The maximum pullout loads of the grit- and shot-blasted Ti–Zr alloys increased linearly with implantation period in rabbits. The pullout load of grit-blasted Ti–Zr alloy rods was higher than that of shot-blasted ones. The surface roughness (Ra) and area ratio of residual Al₂O₃ particles of the Ti–15Zr–4Nb alloy surface grit-blasted with Al₂O₃ particles were the same as those of the grit-blasted Alloclassic stem surface. It was clarified that the grit-blasted Ti–15Zr–4Nb alloy could be used for artificial hip joint stems.     

Introducing a Novel Experimental Model for Osseo-Disintegration of Titanium Dental Implants Induced by Monobacterial Contamination: An In-Vivo Feasibility Study

Background and Objectives: The aim of the current study was to establish an osseo-disintegration model initiated with a single microorganism in mini-pigs. Materials and Methods: A total of 36 titanium dental implants (3.5 mm in diameter, 9.5 mm in length) was inserted into frontal bone (n: 12) and the basis of the corpus mandible (n: 24). Eighteen implants were contaminated via inoculation of Enterococcus faecalis. Six weeks after implant insertion, bone-to-implant contact (BIC) ratio, interthread bone density (ITBD), and peri-implant bone density (PIBD) were examined. In addition to that, new bone formation was assessed via fluorescence microscopy, histomorphometry, and light microscopical examinations. Results: Compared to the sterile implants, the contaminated implants showed significantly reduced BIC (p < 0.001), ITBD (p < 0.001), and PBD (p < 0.001) values. Around the sterile implants, the green and red fluorophores were overlapping and surrounding the implant without gaps, indicating healthy bone growth on the implant surface, whereas contaminated implants were surrounded by connective tissue. Conclusions: The current experimental model could be a feasible option to realize a significant alteration of dental-implant osseointegration and examine novel surface decontamination techniques without impairing local and systemic inflammatory complications.     

Influence of Screw Length and Bone Thickness on the Stability of Temporary Implants

The purpose of this work was to study the influence of screw length and bone thickness on the stability of temporary implants. A total of 96 self-drilling temporary screws with two different lengths were inserted into polyurethane blocks (n = 66), bovine femurs (n = 18) and rabbit tibia (n = 12) with different cortical thicknesses (1 to 8 mm). Screws insertion in polyurethane blocks was assisted by a universal testing machine, torque peaks were collected by a digital torquemeter and bone thickness was monitored by micro-CT. The results showed that the insertion torque was significantly increased with the thickness of cortical bone from polyurethane (p < 0.0001), bovine (p = 0.0035) and rabbit (p < 0.05) sources. Cancellous bone improved significantly the mechanical implant stability. Insertion torque and insertion strength was successfully moduled by equations, based on the cortical/cancellous bone behavior. Based on the results, insertion torque and bone strength can be estimate in order to prevent failure of the cortical layer during temporary screw placement. The stability provided by a cortical thickness of 2 or 1 mm coupled to cancellous bone was deemed sufficient for temporary implants stability.     

The Influence of Surgical Experience and Bone Density on the Accuracy of Static Computer-Assisted Implant Surgery in Edentulous Jaws Using a Mucosa-Supported Surgical Template with a Half-Guided Implant Placement Protocol—A Randomized Clinical Study

The aim of our randomized clinical study was to analyze the influence of surgical experience and bone density on the accuracy of static computer-assisted implant surgery (CAIS) in edentulous jaws using a mucosa-supported surgical template with a half-guided implant placement protocol. Altogether, 40 dental implants were placed in the edentulous jaws of 13 patients (novice surgeons: 18 implants, 6 patients (4 male), age 71 ± 10.1 years; experienced surgeons: 22 implants, 7 patients (4 male), age 69.2 ± 4.55 years). Angular deviation, coronal and apical global deviation and grey level measurements were calculated for all implants by a blinded investigator using coDiagnostiX software. 3DSlicer software was applied to calculate the bone volume fraction (BV/TV) for each site of implant placement. There were no statistically significant differences between the two study groups in either of the primary outcome variables. There was a statistically significant negative correlation between angular deviation and both grey level measurements (R-value: −0.331, p < 0.05) and BV/TV (R-value: −0.377, p < 0.05). The results of the study suggest that surgical experience did not influence the accuracy of implant placement. The higher the bone density at the sites of implant placement, the higher the accuracy of static CAIS.     

Does the Modification of the Apical Geometry of a Dental Implant Affect Its Primary Stability? A Comparative Ex Vivo Study

(1) Background: Primary stability—one fundamental criterion for the success of dental implants—is influenced by implant geometry even if the effect of apical shape modifications on implant primary stability has not yet been examined. Therefore, the aim of the ex vivo study was to compare primary stability of implants differing in apically located screw threads (J-line) or a flat tip (K-line) only. (2) Methods: 28 implants of each group of the same diameter (4.3 mm) were randomly inserted into porcine bone blocks. The first group (9, 11 and 13 mm) was inserted into “hard”, the second (11 mm) into “soft” bone, here using a normal and an undersized drilling protocol. Insertion torque (Ncm), Periotest^® value, resonance frequency (implant stability coefficient, ISQ) and push-out force (N) were measured. (3) Results: In “hard” bone, primary stability increased with increasing length in both groups but it was significantly higher in J-line (p < 0.03). An undersized preparation of the implant bed in “soft” bone resulted in a significant increase in primary stability in both groups. Here, J-line also showed a significantly increased primary stability when compared to equally prepared K-line (insertion torque: 37 Ncm vs. 26 Ncm; Periotest^®: −6.5 vs. −4.3; push-out force: 365 N vs. 329 N; p < 0.05 each). (4) Conclusions: Primary stability is significantly higher with increasing implant length and apically located screw threads as well as with undersized drilling protocols. When preparing the implant site and subsequently selecting the implant system, modifying factors such as implant geometry (also at the tip) should be taken into account.     

Comparative Assessment of the Shaping Ability of Reciproc Blue,WaveOne Gold,and ProTaper Gold in Simulated Root Canals

Maintaining the original trajectory of the root canal is a major challenge in endodontic therapy, especially in narrow and curved root canals. The present study aims to assess the shaping capacity of three endodontic systems made of different nickel–titanium alloys on simulated curved root canals. Thirty-six endodontic resin blocks (Ref. V040245, VDW) divided into three groups, each of twelve blocks (n = 12), were shaped, photographed, and analyzed: Group 1-Protaper Gold (PTG) (Dentsply Maillefer, Ballaigues, Switzerland) F2 25/08; Group 2-Reciproc Blue (RB), RB 25/08 (VDW, Munich, Germany); Group 3-WaveOne Gold (WOG) (Dentsply Maillefer), WOG 25/07. Each block was standardized and photographed before and after shaping in the same position, with the foramen oriented to the left. Post-shaping images were superimposed onto the initial ones. Thirteen measurement points were used for evaluation, spaced with 1 mm distance from one another, from level 0, apical foramen, to level 12, coronal orifice. The amount of removed resin from inner (X1) and outer (X2) walls, the direction of transportation (X1 − X2), and the centering ability (X1 − X2)/Y were measured, calculated, and comparatively analyzed. Statistical differences (p < 0.05) were observed between the shaping capacity of the considered systems in the middle and coronal thirds. PTG had a better centering ability than WOG and RB in the coronal third, while RB was more centered in the middle third in comparison to both WOG and PTG. In the apical third, the centering capacity of WOG was higher, without being statistically significant. WOG 25/07 and PTG 25/08 tend to cut more on the inner wall of the root canals, and RB 25/08 on the external one.     

Melatonin stimulates osteointegration of dental implants

Abstract:  The aim of this study was to evaluate the effect of the topical application of melatonin on osteointegration of dental implants in Beagle dogs 14 days after their insertion. In preparation for subsequent insertion of dental implants, upper and lower premolars and molars were extracted from 12 Beagle dogs. Each mandible received cylindrical screw implants of 3.25 mm in diameter and 10 mm in length. The implants were randomly assigned to the mesial and distal sites on each side of the mandible. Prior to implanting, 1.2 mg lyophylized powdered melatonin was applied to one bone hole at each side of the mandible. None was applied at the control sites. Eight histological sections per implant were obtained for histomorphometric studies. After a 2-wk treatment period, melatonin significantly increased the perimeter of bone that was in direct contact with the treated implants ( P  <   0.0001), bone density ( P  <   0.0001), new bone formation ( P  <   0.0001) and inter-thread bone ( P  <   0.05) in comparison with control implants. Topical application of melatonin may act as a biomimetic agent in the placement of endo-osseous dental implants.     

Graft Remodeling following Transcrestal Sinus Floor Elevation via the Gel-Pressure Technique (GPT) and Pasteous Nano-Crystalline Hydroxyapatite Bone Substitute

Bone grafting of the maxillary sinus is attempted to compensate for sinus pneumatization and permit reliable insertion of endosseous dental implants for prosthetic rehabilitation. The aim of the present clinical investigation was to study bone regeneration four months after transcrestal sinus floor elevation via the Gel-Pressure Technique (GPT) and application of pasteous nano-crystalline hydroxyapatite bone substitute. A total of 25 patients with deficient alveolar ridges in the posterior maxilla (mean residual bone height: 4.7 ± 1.8 mm) were subjected to 32 flapless transcrestal sinus floor augmentations and simultaneous insertion of 40 implants. Sinus membrane elevation height averaged 11.2 ± 2.7 mm and minimal vertical graft resorption of 0.1 mm was observed after four months. Radiographic bone density averaged 460 Hounsfield units in regions adjacent to the native jawbone (1 to 7 mm distance), while reduction of bone density by −7.2%, −11.3%, −14.8%, −19.6% and −22.7% was recorded in more apical regions of 8, 9, 10, 11, and ≥12 mm distance to the original sinus floor, respectively. The results suggest that graft remodeling is completed up to a distance of 7 mm within a healing period of four months after sinus augmentation using nano-crystalline hydroxyapatite bone substitute material.     

Zirconia versus Titanium Implants: 8-Year Follow-Up in a Patient Cohort Contrasted with Histological Evidence from a Preclinical Animal Model

Zirconia ceramic (ZC) implants are becoming more common, but comparisons between preclinical histology and long-term clinical trials are rare. This investigation comprised (1) 8-year clinical follow-up of one-piece ZC or titanium (Ti) implants supporting full overdentures and (2) histomorphometric analysis of the same implants in an animal model, comparing implants with various surface treatments. Methods: (1) Clinical trial: 24 completely edentulous participants (2 groups of N = 12) received 7 implants (one-piece ball-abutment ZC or Ti; maxilla N = 4, mandible N = 3) restored with implant overdentures. Outcomes after 8-years included survival, peri-implant bone levels, soft-tissue responses, and prosthodontic issues. (2) Preclinical trial: 10 New Zealand sheep received 4 implants bilaterally in the femoral condyle: Southern Implants ZC or Ti one-piece implants, identical to the clinical trial, and controls: Southern ITC^® two-piece implants with the same surface or Nobel (NBC) anodised (TiUnite™) surface. %Bone-implant contact (%BIC) was measured after 12 weeks of unloaded healing. Results: 8 of 24 participants (33%) of an average age of 75 ± 8 years were recalled; 21% of original participants had died, and 46% could not be contacted. 80.4% of implants survived; excluding palatal sites, 87.5% of Ti and 79% of ZC implants survived. All failed implants were in the maxilla. Three ZC implants had fractured. Bone loss was similar for Ti vs. ZC; pocket depths (p = 0.04) and attachment levels (p = 0.02) were greater for Ti than ZC implants. (1.7 ± 1.6 mm vs. 1.6 ± 1.3 mm). All implants in sheep femurs survived. %BIC was not statistically different for one-piece blasted surface Ti (80 ± 19%) versus ZC (76 ± 20%) or ITC^® (75 ± 16 mm); NBC had significantly higher %BIC than ITC (84 ± 17%, p = 0.4). Conclusion: Short-term preclinical results for ZC and Ti one-piece implants showed excellent bone-implant contact in unloaded femoral sites. This differed from the long-term clinical results in older-aged, edentulous participants. While ZC and Ti implants showed equivalent performance, the risks of peri-implantitis and implant loss in older, completely edentulous patients remain a significant factor.     

Melatonin plus porcine bone on discrete calcium deposit implant surface stimulates osteointegration in dental implants

Abstract:  The aim of this study was to evaluate the effect of the topical application of melatonin mixed with collagenized porcine bone to accelerate the osteointegration on the rough discrete calcium deposit (DCD) surface implants in Beagle dogs 3 months after their insertion. In preparation for subsequent insertion of dental implants, lower premolars and molars were extracted from 12 Beagle dogs. Each mandible received three parallel wall implants with discrete calcium deposit (DCD) surface of 4 mm in diameter and 10 mm in length. The implants were randomly assigned to the distal sites on each side of the mandible in three groups: group I implants alone, group II implants with melatonin and group III implants with melatonin and porcine bone. Prior to implanting, 5 mg lyophylized powdered melatonin was applied to one bone hole at each side of the mandible. None was applied at the control sites. Ten histological sections per implant were obtained for histomorphometric studies. After a 4-wk treatment period, melatonin significantly increased the perimeter of bone that was in direct contact with the treated implants ( P <  0.0001), bone density ( P <  0.0001), new bone formation ( P <  0.0001) in comparison with control implants. Topical application of melatonin on DCD surface may act as a biomimetic agent in the placement of endo-osseous dental implants and enhance the osteointegration. Melatonin combined with porcine bone on DCD implants reveals more bone to implant contact at 12 wk (84.5 ± 1.5%) compared with melatonin treated (75.1 ± 1.4%) and nonmelatonin treated surface implants (64 ± 1.4%).     

Mechanical Behavior of Bi-Layer and Dispersion Coatings Composed of Several Nanostructures on Ti13Nb13Zr Alloy

Titanium implants are commonly used because of several advantages, but their surface modification is necessary to enhance bioactivity. Recently, their surface coatings were developed to induce local antibacterial properties. The aim of this research was to investigate and compare mechanical properties of three coatings: multi-wall carbon nanotubes (MWCNTs), bi-layer composed of an inner MWCNTs layer and an outer TiO₂ layer, and dispersion coatings comprised of simultaneously deposited MWCNTs and nanoCu, each electrophoretically deposited on the Ti13Nb13Zr alloy. Optical microscopy, scanning electron microscopy, X-ray electron diffraction spectroscopy, and nanoindentation technique were applied to study topography, chemical composition, hardness, plastic and elastic properties. The results demonstrate that the addition of nanocopper or titanium dioxide to MWCNTs coating increases hardness, lowers Young’s modulus, improves plastic and elastic properties, wear resistance under deflection, and plastic deformation resistance. The results can be attributed to different properties, structure and geometry of applied particles, various deposition techniques, and the possible appearance of porous structures. These innovative coatings of simultaneously high strength and elasticity are promising to apply for deposition on long-term titanium implants.     

Characterization of Hydroxyapatite Film Obtained by Er:YAG Pulsed Laser Deposition on Sandblasted Titanium: An In Vitro Study

The surface of titanium (Ti) dental implants must be modified to improve their applicability, owing to the biological inertness of Ti. This study aims to use sandblasting as a pretreatment method and prepare a hydroxyapatite (HA) coating on Ti to improve its biocompatibility and induce bone bonding and osteogenesis. In this paper, sandblasted Ti discs were coated with α-tricalcium phosphate (α-TCP) via Er:YAG pulsed laser deposition (Er:YAG-PLD). An HA coating was then obtained via the hydrothermal treatment of the discs at 90 °C for 10 h. The surface characteristics of the samples were evaluated by SEM, SPM, XPS, XRD, FTIR, and tensile tests. Rat bone marrow mesenchymal stem cells were seeded on the HA-coated discs to determine cellular responses in vitro. The surface characterization results indicated the successful transformation of the HA coating with a nanorod-like morphology, and its surface roughness increased. In vitro experiments revealed increased cell attachment on the HA-coated discs, as did the cell morphology of fluorescence staining and SEM analysis; in contrast, there was no increase in cell proliferation. This study confirms that Er:YAG-PLD could be used as an implant surface-modification technique to prepare HA coatings with a nanorod-like morphology on Ti discs.     

Actions of melatonin mixed with collagenized porcine bone versus porcine bone only on osteointegration of dental implants

Abstract: This study evaluated the effect of the topical application of melatonin mixed with collagenized porcine bone on the osteointegration on the rough discrete calcium deposit (DCD) surface implants in Beagle dogs 3 months after their insertion. In preparation for subsequent insertion of dental implants, lower molars were extracted from 12 Beagle dogs. Each mandible received two parallel wall expanded platform implants with a DCD surface of 4 mm in diameter and 10 mm in length. The implants were randomly assigned to the distal sites on each mandible in the molar area and the gaps were filled with 5 mg lyophilized powdered melatonin and porcine bone and collagenized porcine bone alone. Ten histological sections per implant were obtained for histomorphometric studies. After a 4‐wk treatment period, melatonin plus porcine bone significantly increased the perimeter of bone that was in direct contact with the treated implants (P < 0.0001), bone density (P < 0.0001), and new bone formation (P < 0.0001) in comparison with porcine bone alone around the implants. Melatonin plus collagenized porcine bone on DCD surface may act as a biomimetic agent in the placement of endo‐osseous dental implants and enhance the osteointegration. Melatonin combined with porcine bone on DCD implants reveals more bone in implant contact at 12 wk (84.5 ± 1.5%) compared with porcine bone alone treated area (67.17 ± 1.2%).     

Implants Survival Rate in Regenerated Sites with Innovative Graft Biomaterials: 1 Year Follow-Up

In thirteen different dental clinics in Singapore, Spain, Czech Republic and Italy, 504 patients were selected, and 483 dental implants were placed in maxillary sites after alveolar socket preservation (ASP) procedures with an autologous demineralized tooth extracted as graft material from an innovative Tooth Transformer device was obtained. All procedures used were reported in n°638 Ethical Committee surgical protocol of University of Chieti and approved. After 4 months, at dental implant placing, bone biopsies were performed to evaluate the histologic outcomes, and 12 months after implant loading, global implant survival rate, failure percentage and peri-implant bone loss were detected. After ASP, only 27 post-operative complications were observed and after 4 months, bone biopsy histomorphometric analysis showed a high percentage of bone volume (BV) 43.58 (±12.09), and vital new bone (NB) 32.38 (±17.15) with an absence of inflammation or necrosis areas. Twelve months after loading, only 10 dental implants failed (2.3%), with a 98.2% overall implant survival rate, nine cases showed mucositis (1.8%) and eight showed peri-implantitis (1.6%). At mesial sites, 0.43 mm (±0.83) of bone loss around the implants was detected and 0.23 mm (±0.38) at the distal sites with an average value of 0.37 mm (±0.68) (p > 0.568). Several studies with a longer follow-up will be necessary to confirm the preliminary data observed. However, clinical results seem to suggest that the post-extraction socket preservation procedure using innovative demineralized autologous tooth-derived biomaterial may be a predictable procedure to produce new vital bone able to support dental implant rehabilitation of maxilla edentulous sites.     

Approach to the Fatigue and Cellular Behavior of Superficially Modified Porous Titanium Dental Implants

In this work, the fatigue and cellular performance of novel superficially treated porous titanium dental implants made up using conventional powder metallurgy and space-holder techniques (30 vol.% and 50 vol.%, both with a spacer size range of 100–200 µm) are evaluated. Before the sintering stage, a specific stage of CNC milling of the screw thread of the implant is used. After the consolidation processing, different surface modifications are performed: chemical etching and bioactive coatings (BG 45S5 and BG 1393). The results are discussed in terms of the effect of the porosity, as well as the surface roughness, chemical composition, and adherence of the coatings on the fatigue resistance and the osteoblast cells’ behavior for the proposed implants. Macro-pores are preferential sites of the nucleation of cracks and bone cell adhesion, and they increase the cellular activity of the implants, but decrease the fatigue life. In conclusion, SH 30 vol.% dental implant chemical etching presents the best bio-functional (in vitro osseointegration) and bio-mechanical (stiffness, yield strength and fatigue life) balance, which could ensure the required characteristics of cortical bone tissue.     

Bone Response to Conventional Titanium Implants and New Zirconia Implants Produced by Additive Manufacturing

The aim of the present study was to evaluate the in vivo bone response to an additively manufactured zirconia surface compared to osseointegration into titanium (Ti) surfaces. Scanning electron microscopy, confocal laser scanning microscopy, and electron spectroscopy for chemical analysis were performed to assess the surface characteristics of implant specimens. For the in vivo evaluation, eight Ti implants and eight 3D-printed zirconia implants were used. The surface of four Ti implants was sandblasted, large-grit, and acid-etched (Ti-SLA group), while those of the other four Ti implants were left untreated (Ti-turned group). The zirconia implants had no further surface modification. Implants were placed into the tibiae of four rabbits; two received the Ti-SLA and zirconia implants and the other two received Ti-turned and zirconia implants. The experimental animals were sacrificed after four weeks of surgery, and the undecalcified microscopic slides were prepared. The bone–implant interface was analyzed by histomorphometry to evaluate the bone response. The degree of surface roughness showed that Ti-SLA was the highest, followed by zirconia and Ti-turned surfaces. The 3D-printed zirconia surface showed similar bone-to-implant contact to the Ti-turned surface, and Ti-SLA had the most bone-to-implant contact. The additively manufactured zirconia implant surface is biocompatible with respect to osseointegration compared to the commercially pure Ti surface.