Effect of Organizational Evolution on the Stress Corrosion Cracking of the Cr-Co-Ni-Mo Series of Ultra-High Strength Stainless Steel

Different microstructures were obtained under various thermal conditions by adjusting the heat treatment parameters of the Cr-Co-Ni-Mo series of ultra-high strength stainless steel. The effect of organizational evolution on the stress corrosion cracking (SCC) of the Cr-Co-Ni-Mo series of ultra-high strength stainless steel was investigated using potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and other test methods in combination with slow strain rate tensile tests (SSRTs). The results show that the Mo- and Cr-rich clusters and precipitation of the Laves phase reduce the corrosion resistance, while increasing the austenite content can improve the corrosion resistance. The Cr-Co-Ni-Mo series of ultra-high strength stainless steel has a high SCC resistance after quenching at 1080 °C and undergoing deep cooling (DC) treatment at −73 °C. With increasing holding time, the strength of the underaged and peak-aged specimens increases, but the passivation and SCC resistance decreases. At the overaged temperature, the specimen has good SCC resistance after a short holding time, which is attributed to its higher austenite content and lower dislocation density. As a stable hydrogen trap in steel, austenite effectively improves the SCC resistance of steel. However, under the coupled action of hydrogen and stress, martensitic transformation occurs due to the decrease in the lamination energy of austenite, and the weak martensitic interface becomes the preferred location for crack initiation and propagation.     

Influence of Austempering of As-Cast Medium Carbon High-Silicon Steel on Wear Resistance

The aim of this study was to evaluate the effect of austempering compared to quenching and low-temperature tempering on wear resistance of an as-cast medium carbon high-silicon steel intended for rock breaking. Austempering was done by isothermal holding at 270, 300 and 350 °C in molten salt baths, while quenching was done in water. The austempering treatments resulted in microstructural combinations of bainite and martensite. The isothermal holding at 270 °C resulted in bainite and self-tempered martensite, while isothermal holdings at 300 and 350 °C resulted in bainite and untempered martensite. The two quench and temper treatments resulted in tempered martensite. In general austempering resulted in lower hardness values when compared to quenching and tempering but higher impact toughness. The wear resistance was best for quenching and low temperature tempering, followed by austempering at 270 °C, but at slightly lower hardness and 25% higher impact toughness. The other two austempering treatments resulted in worse wear resistance.     

Abrasive Wear of High-Carbon Low-Alloyed Austenite Steel: Microhardness,Microstructure and X-ray Characteristics of Worn Surface

A high-carbon, high-silicon steel (1.21 wt% C, 2.56 wt% Mn, 1.59 wt% Si) was subjected to quenching from 900 and 1000 °C, resulting in microstructures containing 60 and 94% of retained austenite, respectively. Subsequent abrasive wear tests of quenched samples were performed using two-body abrasion and three-body abrasion testing machines. Investigations on worn surface and subsurface were carried out using SEM, XRD, and microhardness measurement. It was found that the highest microhardness of worn surface (about 1400 HV0.05) was achieved on samples quenched from 900 °C after three-body abrasion. Microhardness of samples after two-body abrasion was noticeably smaller. with a maximum of about 1200 HV0.05. This difference correlates with microstructure investigations along with XRD results. Three-body abrasion has produced a significantly deeper deformed layer; corresponding diffractograms show bigger values of the full width at half maximum parameter (FWHM) for both α and γ alone standing peaks. The obtained results are discussed in the light of possible differences in abrasive wear conditions and differing stability of retained austenite after quenching from different temperatures. It is shown that a structure of metastable austenite may be used as a detector for wear conditions, as the sensitivity of such austenite to phase transformation strongly depends on wear conditions, and even small changes in the latter lead to significant differences in the properties of the worn surface.     

Changes in Microstructure and Abrasion Resistance during Miller Test of Hadfield High-Manganese Cast Steel after the Formation of Vanadium Carbides in Alloy Matrix

Hadfield cast steel is characterized by high wear resistance, but this is only when it is subjected to the effect of dynamic loads. During unloaded abrasion, e.g., sand abrasion, its wear resistance is very low and comparable to the wear of carbon cast steel. To increase the wear resistance of this alloy for operation under the conditions of low pressure or low stress, primary vanadium carbides were produced by the metallurgical process to obtain a two-phase structure after alloy solidification. Compared to samples made of Hadfield cast steel, the primary, very hard carbides, evenly distributed in an austenitic or austenitic-martensitic matrix, increase (at least three times) the wear resistance of samples tested in an abrasive mixture of silicon carbide and water. The changes in microstructure and hardness obtained in alloys after heat treatment (quenching at 1000–1150 °C in water and tempering at 600 °C) are presented. The bulk hardness of the matrix ranged from 370 HV to 660 HV. After heat treatment, the secondary, dispersed vanadium carbides, precipitated in the alloy matrix.     

Structure and Properties of Gas-Nitrided,Precipitation-Hardened Martensitic Stainless Steel

Nanoflex stainless steel is a promising material for medical applications. However, improvement of its mechanical properties without compromising its corrosion resistance is still a challenge. In order to investigate the effect of the nitriding process on the corrosion and wear resistance of Sandvik Nanoflex^TM steel, a number of processes were carried out in a gas atmosphere with differing ammonia contents in the temperature range of 425–475 °C for 4 h. The mechanical properties and wear resistance of the layers were tested using the nanoindentation and pin-on-disc methods, respectively. In order to assess corrosion resistance, potentiodynamic tests were carried out in Ringer’s artificial body fluid and in a 3% aqueous solution of sodium chloride. The results are discussed herein with respect to the microstructural characteristics of the layers studied using light and scanning electron microscopy, X-ray diffraction phase analysis and wavelength dispersive X-ray microanalysis. The structure of nitrided layers included three zones: the subsurface zone composed of nitrides and the zones composed of metastable phases, i.e., the S phase (γN) and expanded martensite (αN) with possible precipitates of nitrides. The third zone adjacent to the steel core was enriched with carbon. The nitrided samples showed significant improvement in the wear rate while maintaining good corrosion resistance in comparison to the non-treated steel. We concluded that nitriding should be carried out at a temperature below 450 °C and in an atmosphere containing no more than approximately 50% ammonia in order to avoid nitrides precipitation.     

Investigation into Changes of Microstructure and Abrasive Wear Resistance Occurring in High Manganese Steel X120Mn12 during Isothermal Annealing and Re-Austenitisation Process

Hadfield steel, under unit pressure conditions, strengthens itself by forming a high density dislocation structure, which results in increased resistance to dynamic impact wear. However, under abrasion conditions, the homogeneous microstructure of the cast steel is insufficient to achieve the expected service life. The aim of the research is to conduct a comparative analysis of the material in its as-delivered state and after two-stage heat treatment (isothermal annealing followed by re-austenitisation). It was found that after isothermal annealing of X120Mn12 grade steel at a temperature of 510 °C, a microstructure with a complex morphology consisting of colonies of fine-grained pearlite, (Fe,Mn)₃C carbides distributed along the grain boundaries of the former austenite and needle-like (Fe,Mn)₃C carbides was obtained in the austenite matrix. The subsequent thermal treatment of the steel with the use of supersaturating annealing at 900 °C resulted in a heterogeneous microstructure consisting of evenly distributed globular carbide precipitations in a matrix of considerably finer austenite grains in comparison with the as-delivered original state. As a result of the final microstructural changes achieved, a 16.4% increase in abrasion resistance was obtained compared to the delivered condition.     

Microstructure Evolution and Mechanical Properties of X6CrNiMoVNb11-2 Stainless Steel after Heat Treatment

X6CrNiMoVNb11-2 supermartensitic stainless steel, a special type of stainless steel, is commonly used in the production of gas turbine discs in liquid rocket engines and compressor disks in aero engines. By optimizing the parameters of the heat-treatment process, its mechanical properties are specially adjusted to meet the performance requirement in that particular practical application during the advanced composite casting-rolling forming process. The relationship between the microstructure and mechanical properties after quenching from 1040 °C and tempering at 300–670 °C was studied, where the yield strength, tensile strength, elongation and impact toughness under different cooling conditions are obtained by means of mechanical property tests. A certain amount of high-density nanophase precipitation is found in the martensite phase transformation through the heat treatment involved in the quenching and tempering processes, where M₂₃C₆ carbides are dispersed in lamellar martensite, with the close-packed Ni₃Mo and Ni₃Nb phases of high-density co-lattice nanocrystalline precipitation created during the tempering process. The ideal process parameters are to quench at 1040 °C in an oil-cooling medium and to temper at 650 °C by air-cooling; final hardness is averaged about 313 HV, with an elongation of 17.9%, the cross-area reduction ratio is 52%, and the impact toughness is about 65 J, respectively. Moreover, the tempered hardness equation, considering various tempering temperatures, is precisely fitted. This investigation helps us to better understand the strengthening mechanism and performance controlling scheme of martensite stainless steel during the cast-rolling forming process in future applications.     

Austenite Grain Growth Analysis in a Welded Joint of High-Strength Martensitic Abrasion-Resistant Steel Hardox 450

The paper presents the results of tests of a welded joint of Hardox 450 steel, belonging to the group of weldable high-strength boron steels with increased resistance to abrasive wear. As a result of the conducted research, apart from the basic structural indicators, an attempt was made to determine the correlation between the grain size of the prior austenite in the characteristic weld zones and its basic mechanical properties, such as yield point, tensile strength, percentage elongation after fracture, reduction of area, and impact strength. The scope of research quoted above was carried out for a welded joint of the considered steel at delivery state (directly after welding), in the normalising annealed state, as well as in water-quenched state, using different austenitisation temperatures in the range of 900–1200 °C. The results obtained showed a large influence of the parameters of the applied thermal heat treatment on the selected structural and mechanical properties of the welded joint.     

Wear-Resistance Improvement of 65Mn Low-Alloy Steel through Adjusting Grain Refinement by Cyclic Heat Treatment

Refined microstructures achieved by cyclic heat treatment significantly contribute to improving the wear resistance of steels. To acquire the refined microstructures of 65Mn low-alloy steel, first, the specimens were solid solution-treated; then, they were subjected to cyclic heat treatment at cyclic quenching temperatures of 790–870 °C and quenching times of 1–4 with a fixed holding time of 5 min. The mechanical properties of 65Mn low-alloy steel in terms of hardness, tensile strength, elongation and wear resistance were characterized. Afterwards, the effect of cyclic heat treatment on microstructure evolution and the relationships between grain refinement and mechanical properties’ improvement were discussed. The results show that the average grain size firstly decreased and then increased with the increase in the quenching temperature. Hardness increased with grain refinement when the temperature was lower than 830 °C. Once the temperature exceeded 830 °C, hardness increased with the temperature increase owing to the enrichment of carbon content in the martensite. With the increase in cyclic quenching times, hardness continuously increased with grain refinement strengthening. In addition, both tensile strength and elongation could be significantly improved through grain refinement. The relationships among wear loss, hardness and average grain size showed that wear resistance was affected by the synthesis reaction of grain refinement and hardness. Higher hardness and refined grain size contributed to improving the wear resistance of 65Mn low-alloy steel.     

Optimization of Pre-Heat Treatment for Nitriding

To achieve a core strength that meets the requirements during service life, components to be nitrided are subjected to a pre-heat treatment. Since a higher strength prior to nitriding also has a positive effect on the achievable strength in the nitrided layer, an optimization of the pre-heat treatment may lead to better service characteristics of nitrided components. For this purpose, different optimizations of pre-heat treatment were investigated on the nitriding and quenching and tempering steels EN31CrMoV9 and EN42CrMo4 (AISI4140). One strategy was a change of the austenitization temperature for EN31CrMoV9 from 870 °C to 950 °C in order to solve the coarse carbides of the as-delivered state and realize a finer distribution of the carbides in the quenched and tempered structure. This special treatment lead to a higher hardness compared to the conventional treatment. The second investigated pre-heat treatment variant was a bainitic treatment instead of quenching and tempering. The bainitic initial microstructure increased the diffusion depth compared to conventionally quenched and tempered specimens. In addition the maximum hardness of the nitrided layer, the core hardness was significantly higher on the specimens with the bainitic microstructure. During subsequent nitriding, however, the bainite is tempered and loses some of its hardness.     

Nitriding of 316L Steel in a Glow Discharge Plasma

The article presents the results of the research on the nitriding process of 316L austenitic steel and the change in surface properties resulting from this process used in medicine, orthopedics, and in fuel cells. The processes were carried out with the following parameters: time from 5 to 17 h, temperature from 430 °C to 490 °C. The study presents the results of tests of the 316L austenitic steel substrate layer subjected to plasma nitriding of a direct current glow discharge, i.e., in the area isolated from both the cathode and the anode. Additionally, the influence of the active screen on the nitriding process in this area of the direct current discharge was studied. The following tests were carried out: nitrogen diffusion depth test, hardness test, wear resistance test, microstructure analysis, corrosion resistance, and distribution of the element concentration in the surface layer. The research allowed for the conclusion that each variant of nitriding contributed to a change in the examined properties, while the observed scale and nature of the changes were different.     

Effect of Temperature on Microstructure and Mechanical Properties of Fe-9Ni-2Cu Steel during the Tempering Process

In this paper, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray stress meter (XRSA), atom probe tomography (APT), hardness, and tensile tests were used to study the effect of tempering temperature on the microstructure and properties of Fe-9Ni-2Cu steel. The results show that after the quenched samples were tempered at 460 °C for 2 h, the hardness values increased from 373 to 397 HV, and elongation also increased from 13% to 16%. With the tempering temperature increasing from 460 to 660 °C, the hardness firstly decreases from 397 to 353 HV and then increases to 377 HV, while the elongation increases to 17% and then decreases to 11%. The variation of the mechanical properties greatly depends on the evolution of the Cu-rich phase and carbides. The precipitation strengthening of the Cu-rich phase and carbides leads to the increase of hardness, but when the precipitate is coarsened, the precipitation strengthening weakens, and then, the hardness increases. When the tempering temperature is 560 °C, a large amount of stable reverse transformation austenite was formed with a content of 7.1%, while the tensile strength reached the lowest value of 1022 MPa and the elongation reached the maximum value of 17%.     

Optimization of Heat Treatment for 38Si7 Spring Steel with Excellent Mechanical Properties and Controlled Decarburization

Optimizing the heat treatment procedure with 13 mm diameter 38Si7 spring steel is critical for developing high-performance, low-cost, large spring steel for railway clips. The effects of quenching temperature, holding time, tempering temperature, and tempering time on the microstructure and mechanical properties were investigated using an orthogonal experiment, designed with four factors and three levels. The best heat treatment settings were explored, as well as the variation laws of mechanical properties, decarburization behavior, and fracture morphology. The results demonstrated that quenching temperature and tempering temperature had the most impact on plasticity and tempering temperature, while time had the most effect on strength. The optimized heat treatment schemes made the elongation increase by up to 106% and the reduction in area increase by up to 67%, compared with the standard BS EN 10089-2002, and there were mixed fractures caused by ductility and brittleness. The fracture tests showed a good performance of 20.2 GPa·%, and the heat treatment processes’ minimum decarburization depth of 93.4 μm was determined. The optimized process would obtain stronger plastic deposition and better decarburization performance. The microstructure was simply lightly tempered martensite, and the matrix still retained the acicular martensite. The optimal heat treatment process is quenching at 900 °C for 30 min (water cooling), followed by tempering at 430 °C for 60 min (air cooling). The research led to a solution for increasing the overall mechanical characteristics and decreasing the surface decarburization of 38Si7 spring steel with a diameter of 13 mm, and it set the foundation for increasing the mass production of railway clips of this size.     

Influence of Post-Weld Heat Treatment on Microstructure and Toughness Properties of 13MnNiMoR High Strength Low Alloy Steel Weld Joint

Weld and base metals require hot or cold working during the steel equipment manufacturing process. As a result, the components should be subjected to a normalizing heat treatment in order to recover their mechanical properties. In this study, the submerged-arc welding of the high strength low alloy (HSLA) thick steel plate(13MnNiMoR) is adapted for the vessel head under the normalizing and tempering heat treatment. The findings showed that the material toughness decreases after heating to simulate a vessel head forming process. The stamping process is carried out under the conditions of 980 °C for one hour, normalizing at 920 °C for 1 h and tempering between 600–660 °C for 2 h, respectively. The martensite-austenite (M-A) constituent is distributed in granular bainite and the boundary of austenite in island constituent. Therefore, it was deemed to be the most detrimental to Charpy-V impact toughness. Between normalizing and tempering, intercritical normalizing at 740 °C was added. As a result of the ferrite with fine particles M-A constituent, the toughness increases significantly.     

Effect of Tempering Temperature on Microstructure and Sulfide Stress Cracking of 125 Ksi Grade Casing Steel

The influence of tempering temperature on the microstructure of 0.5Cr0.4W steels was investigated by scanning electron microscope, and the roles of grain boundary character, dislocation, and Taylor factor in sulfide stress cracking (SSC) resistance were interpreted using the election backscattered diffraction technique. The 0.5Cr0.4W steels tempered at 690 °C, 700 °C, and 715 °C all showed tempered martensites. The specimen tempered at 715 °C exhibited a higher critical stress intensity factor (K_ISSC) of 34.58 MPa·m^0.5, but the yield strength of 800 MPa did not meet the criterion of 125 ksi (862 MPa) grade. When the specimen was tempered at 690 °C, the yield strength reached 960 MPa and the K_ISSC was only 21.36 MPa·m^0.5, displaying poorer SSC resistance. The 0.5Cr0.4W steel tempered at 700 °C showed a good combination of yield strength (887 MPa) and SSC resistance (K_ISSC: 31.16 MPa·m^0.5). When increasing the tempering temperature, the local average misorientation and Taylor factor of the 0.5Cr0.4W steels were decreased. The reduced dislocation density, and greater number of grains amenable to slippage, produced less hydrogen transport and a lower crack sensitivity. The SSC resistance was, thus, increased, owing to the minor damage to hydrogen aggregation. Therefore, 700 °C is a suitable tempering temperature for 0.5Cr0.4W casing steel.     

The Role of Elements Partition and Austenite Grain Size in the Ferrite-Bainite Banding Formation during Hot Rolling

The partitioning and diffusion of solute elements in hot rolling and the effect of the partitioning and diffusion on the ferrite-bainite banding formation after hot rolling in the 20CrMnTi steel were experimentally examined by EPMA (electron probe microanalysis) technology and simulated by DICTRTA and MATLAB software. The austenite grain size related to the hot rolling process and the effect of austenite grain size on the ferrite-bainite banding formation were studied. The results show that experimental steel without banding has the most uniform hardness distribution, which is taken from the edge of the cast slab and 1/4 diameter position of the cast slab, heating at 1100 °C for 2 h and above 1200 °C for 2–4 h during the hot rolling, respectively. Cr, Mn, and Si diffuse and inhomogeneously concentrate in austenite during hot rolling, while C homogeneously concentrates in austenite. After the same hot rolling process, ΔA_e3 increases and ferrite-bainite banding intensifies with increasing initial segregation width and segregation coefficient K of solute elements. Under the same initial segregation of solute elements, ΔA_e3 drops and ferrite-bainite banding reduces with increasing heating temperature and extension heating time. When ΔA_e3 drops below 14 °C, ferrite-bainite banding even disappears. What is more, the austenite grain size increases with increasing heating temperature and extension heating time. When the austenite grain size is above 21 μm, the experimental steel will not appear to have a banded structure after hot rolling.     

Effect of Intercritical Tempering Temperature on Microstructure Evolution and Mechanical Properties of High Strength and Toughness Medium Manganese Steel

The effect of intercritical tempering temperature (TT) on the microstructure evolution and mechanical properties of 3.6Mn medium manganese steel, which contained martensite and austenite, was investigated by X-ray diffraction, electron backscattering diffraction and transmission electron microscopy, as well as Thermo-Calc calculation. The results showed that the volume fraction of reversed austenite (RA) increased firstly and then decreased with the increasing TT in the range of 550~650 °C. When the TT was below 620 °C, lath-like RA with good stability was mainly displayed between martensite laths and its size is about 100 nm. When the TT was higher than 650 °C, larger-size and block RA was formed in the martensite block boundaries, and part of the RA transformed into fresh martensite during cooling. The yield strength and tensile strength of the experimental steels decreased gradually as the TT increased, but the tensile strength increased gradually with the formation of block RA and fresh martensite. Lath-like RA could significantly improve the toughness and plasticity with slight loss of yield strength, but block RA decreased slightly them.     

The Correlation Analysis of Microstructure and Tribological Characteristics of In Situ VCp Reinforced Iron-Based Composite

In this study, four kinds of heat treatments were performed to obtain a certain amount of retained austenite, which can result in good toughness and low brittleness accompanied with wear resistance of an in situ VC particle reinforced iron-based composite (VCFC). Microstructure, mechanical properties and wear resistance of the samples under heat treatment of QP, QPT, MQP and MQPT were compared. The experimental results indicated that there is a huge difference in microstructure between MQPT and the other heat treatments. High-proportion retained austenite and white net-like precipitates of M₇C₃ carbide existed in the MQPT-treated sample, but thick M₇C₃ carbide with brittleness was discovered in the other sample. Thereby, high-proportion retained austenite contributed to its low hardness of 634 HV and high tensile strength of 267 MPa, while a maximum hardness of 705.5 HV and a minimum tensile strength of 205 MPa were exhibited in the QPT-treated sample with a V-rich carbide of high hardness, a Cr-rich carbide of brittleness and a high-proportion martensite. Meanwhile, a phase transformation from retained austenite to martensite could increase the hardness and enhance wear resistance based on the transformation-induced plasticity (TRIP) effect; its wear rate was only 1.83 × 10⁻⁶ mm⁻³/(N·m). However, the wear rates of the samples under QP, QPT and MQP heat treatments increased by 16.4%, 44.3% and 41.0%, respectively. The wear mechanism was a synergistic effect of the adhesive wear mechanism and the abrasive wear mechanism. The adhesive wear mechanism was mainly considered in the MQPT-treated sample to reduce the wear rate attributed to high-proportion retained austenite and the existence of wear debris with a W element on the surface of the wear track. However, the abrasive wear mechanism could exist in the other samples because of a lot of thick, brittle M₇C₃, thereby resulting in a higher wear rate due to immediate contact between the designed material and the counterpart.     

Effects of Intercritical Annealing Temperature on Mechanical Properties of Fe-7.9Mn-0.14Si-0.05Al-0.07C Steel

A medium Mn steel has been designed to achieve an excellent combination of strength and ductility based on the TRIP (Transformation Induced Plasticity) concept for automotive applications. Following six passes of hot rolling at 850 °C, the Fe-7.9Mn-0.14Si-0.05Al-0.07C (wt.%) steel was warm-rolled at 630 °C for seven passes and subsequently air cooled to room temperature. The sample was subsequently intercritically annealed at various temperatures for 30 min to promote the reverse transformation of martensite into austenite. The obtained results show that the highest volume fraction of austenite is 39% for the sample annealed at 600 °C. This specimen exhibits a yield stress of 910 MPa and a high ultimate tensile stress of 1600 MPa, with an elongation-to-failure of 0.29 at a strain rate of 1 × 10⁻³/s. The enhanced work-hardening ability of the investigated steel is closely related to martensitic transformation and the interaction of dislocations. Especially, the alternate arrangement of acicular ferrite (soft phase) and ultrafine austenite lamellae (50–200 nm, strong and ductile phase) is the key factor contributing to the excellent combination of strength and ductility. On the other hand, the as-warm-rolled sample also exhibits the excellent combination of strength and ductility, with elongation-to-failure much higher than those annealed at temperatures above 630 °C.     

Effect of Deep Cryogenic Treatment on Corrosion Behavior of AISI H13 Die Steel

AISI H13 die steel specimens were subjected to heating at 1020 °C followed by oil quenching and double tempering at 520 °C. Subsequently, these specimens were subjected to deep cryogenic treatment at −185 °C in liquid nitrogen environment for 16 h and then subjected to soft tempering at 100 °C once the specimens attained room temperature. Thereafter, the specimens were subjected to scanning electron microscopy (SEM) analysis and electron backscatter diffraction (EBSD) analysis. The electrochemical corrosion activity was investigated in 3.5% NaCl at 23 ± 0.5 °C by evaluating the evolution of open circuit potential over time and potentiodynamic curves, and electrochemical impedance spectroscopy study was also carried out. The heat-treated specimens exhibited better resistance to corrosion through more electropositive values of open circuit potential. This could be attributed to lower grain boundary area in heat-treated specimens as compared to 16 h cryogenically treated specimen as higher grain boundary areas behave as an anode in an electrochemical cell, thereby enhancing the rate of corrosion. According to electrochemical tests, the cryogenically treated surface is more resistant to corrosion, followed by heated alloy. However, both surface modification treatments improved the corrosion behavior of the untreated alloy.