Influence of microstructure on mechanical properties of mica-based glass-ceramics for dental restorations. |
| |
| QIN Yan jun,WANG Zhong yi,CAO Xiao gang,et al.. Influence of microstructure on mechanical properties of mica-based glass-ceramics for dental restorations.[J]. Journal of Oral Science Research, 2001, 17(2): 91-94 |
| |
| Authors: | QIN Yan jun WANG Zhong yi CAO Xiao gang et al. |
| |
| Affiliation: | QIN Yan jun,WANG Zhong yi,CAO Xiao gang,et al.Department of Prosthodontics,College of Stomatology,Fourth Military Medical University,Xi'an 710032 [ |
| |
| Abstract: | Objective:To investigate the influence of microstructure on mechanical properties of mica based machinable glass ceramics used for CAD/CAM restorations.Methods:According to the requirements of dental restorative materials, K 2O MgO MgF 2 SiO 2 system was chosen to form tetrasilicic fluormica glass ceramics and three different temperatures were used to finish crystallization process.Differential thermal analysis(DTA),X ray diffractometer(XRD) and scanning electron microscopy(SEM) were used to observe the crystallization behavior,crystalline phases and microstructures of the glass ceramics.Influence of microstructure on mechanical properties of the glass ceramics was compared.Results:Improving crystallization temperature can increase the grain sizes and aspect ratio of mica and improve the three point bending strength and fracture toughness of the glass ceramics.Vickers hardness and the index of brittleness decrease with increasing of temperature.Conclusion:The mechanical properties of the glass ceramic are determined by its microstructure,while the latter has a close relationship with crystallization temperature. [ |
| |
| Keywords: | Glass ceramics Tetrasilicic fluormica Microstructure Mechanical property |