Effects of CO2 Concentration and the Uptake on Carbonation of Cement-Based Materials

Carbonation seriously deteriorates the durability of existing reinforced concrete structures. In this study, a thermodynamic model is used to investigate the carbonation reactions in cement-based materials. The effects of the concentration and amounts of CO₂ on the carbonation behaviors of mortar are discussed. The simulation results show that the mechanisms of the carbonation reaction of cement-based materials at different CO₂ concentrations may be different. Nearly all of the hydrate phases have a corresponding CO₂ concentration threshold, above which the corresponding carbonation reaction can be triggered. The thresholds of the C-S-H phases with different Ca/Si ratios are different. The calculation results also show that the phase assemblages in cement paste after being completely air-carbonated, primarily consist of a low-Ca/Si ratio C-S-H, strätlingite, CaCO₃ and CaSO₄. The pH of the pore solution exhibits a significant decrease when a higher Ca/Si ratio C-S-H phase is completely decalcified into a lower Ca/Si ratio C-S-H phase, by increasing the CO₂ uptake. Additionally, the experimental results and the previously published investigations are used to validate the simulation results.