Surface modification of titanium by etching in concentrated sulfuric acid
Authors:Seiji Ban   Yukari Iwaya   Hiroshi Kono  Hideo Sato
Affiliation:Department of Biomaterials Science, Graduate School of Medical and Dental Sciences, Kagoshima University, Kagoshima, Japan. sban@denta.hal.kagoshima-u.ac.jp
Abstract:OBJECTIVE: The purpose of this study was to characterize the etching behavior of titanium in concentrated sulfuric acid and discuss its application on surface modification of titanium for biological use. METHODS: Commercially pure titanium (cpTi) plate was etched in 48% H2SO4 at RT -90 degrees C for 0.25-8 h. The weight loss was derived from the weight differences before and after etching. The surfaces after etching were characterized by surface roughness, X-ray diffractometry, and scannning electron spectroscopy. The apparent activation energy of the dissolution of cpTi into acid was derived from an Arrhenius plot of the rate of weight loss versus the acid temperature. RESULTS: The surface roughness of cpTi increased with the acid temperature and etching time. The surface roughness was strongly related to the weight loss. The weight loss increased drastically with the acid temperature after an initial period, which shortened with increasing acid temperature. The apparent activation energy for the dissolution of cpTi in H2SO4 was derived as 67.8 kJ/mol. SIGNIFICANCE: This study indicates that etching with concentrated sulfuric acid is an effective way to modify the surface of titanium for biological applications.
Keywords:Titanium   Acid etching   Surface modification   Surface characterization   Surface roughness   Surface topography
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号