Side-chain functionalized polysiloxanes were prepared via polymer-analogous esterification of poly[(3-chloroformylpropyl)methylsiloxane] with 4-(4-hydroxyphenylazo)nitrobenzene ( P1 ), 4-[4-(ω-hydroxyalkyloxy)phenylazo]nitrobenzene ( P2 – P4 ), 4-{4-[N-(2-hydroxyethyl)-N-methyl]anilinoazo}nitrobenzene ( P5 ), 4-(4-hydroxypiperidino)nitrobenzene ( P6 ), or 4-[4-(2-hydroxyethyl)piperidino]nitrobenzene ( P7 )., P1 , P3 , P4 and P5 exhibit liquid crystallinity, as deduced from differential scanning calorimetry, polarized microscopic observations and X-ray diffraction measurements. The liquid-crystalline phase of P1 and P5 is a nematic phase, and that of P3 and P4 is a smectic one. The second harmonic generation (SHG) measurement of a spin-coated film of P1 was carried out by the Maker fringe method using a Q-switched Nd:YAG laser (1064 nm). The SHG profile after the heat treatment of a spin-coated film suggests a perpendicular orientation of the mesogenic molecules to the glass substrate. The SH light intensity of a corona-poled film was 20-fold higher than that of a film which was only heated, though no differences were observed in their UV-vis absorption spectra. These findings suggest that the mesogenic-molecular dipole moments are aligned to the same direction in the crystalline or liquid-crystalline phase by a poling treatment. |