| Abstract: | In the past morphological changes, caused by uni-axial drawing of flexible polymers have been studied mostly under conditions, quite different from the drawing conditions. This could give rise to certain artefacts, leading to mis-interpretations. Up to now very little was known about this possibility. Therefore, X-ray patterns obtained by conventional drawing studies and by real-time X-ray drawing studies are compared in this paper. It will be shown, that although some results on melt-crystallized polyethylene discussed here show indeed small differences, conventional X-ray studies can be used without any problem for qualitative studies. However, studies of deformation phenomena in elastic deformable regions as well as quantitative X-ray studies require real-time measurements. |