ObjectiveTo characterize the effect of pigmentation techniques on the fatigue behavior of a 4YSZ ceramic adhesively luted onto dentin analog (glass fiber-reinforced epoxy resin).Methods4YSZ ceramic discs (Ø= 10 mm, 1 mm thickness) were allocated into 5 groups: Ctrl – unshaded (IPS e.max ZirCAD MT BL); Manuf – shaded by the manufacturer (IPS e.max ZirCAD MT A2); Brush – unshaded pigmented, pre-sintering, using a brush; Stain – unshaded pigmented, post-sintering, during glaze application; Brush+Stain – combination of both techniques. Color assessments ensured the same perceived color (Vita Classical A2). Dentin analog discs (Ø= 10 mm, 2.5 mm thickness) were obtained, paired with the 4YSZ discs, and adhesively luted using a resin cement. Cyclic fatigue testing (n = 15) was run (20 Hz; 10,000 cycles/step, initial load 200 N; step-size 100 N up to 700 N; then 50 N until specimen failure). Fractographic, roughness and topography analyses were performed.ResultsNo statistical (p > 0.05) detrimental influence were observed for fatigue outcomes (Ctrl = Manuf = Brush = Stain = Brush+Stain). However, the Brush+Stain technique induced inferior statistical (p < 0.05) fatigue performance compared to Stain. All failures were radial cracks with origin at the ceramic intaglio surface. The staining technique triggered statistically higher roughness (p < 0.05). Uniformly sized zirconia crystals were seen in the Ctrl, Manuf and Brush groups, and a smooth vitreous surface with encrusted pigments in the Stain and Brush+Stain groups.SignificancePigmentation techniques (Vita Classical A2 shade) have no detrimental effect on the mechanical fatigue properties of 4YSZ ceramic adhesively luted onto dentin analog.