Microstructure and Abrasive Wear Resistance of Metal Matrix Composite Coatings Deposited on Steel Grade AISI 4715 by Powder Plasma Transferred Arc Welding Part 1. Mechanical and Structural Properties of a Cobalt-Based Alloy Surface Layer Reinforced with Particles of Titanium Carbide and Synthetic Metal–Diamond Composite
Authors:Artur Czupryń  ski
Affiliation:Department of Welding Engineering, Faculty of Mechanical Engineering, Silesian University of Technology, Konarskiego 18A, 44-100 Gliwice, Poland;
Abstract:
The article discusses test results concerning an innovative surface layer obtained using the cladding with powder plasma transferred arc welding (PPTAW) method. The above-named layer, being a metal matrix composite (MCM), is characterised by high abrasive wear resistance, resistance to pressure and impact loads, and the possibility of operation at elevated temperatures. The layer was made using powder in the form of a cobalt alloy-based composite reinforced with monocarbide TiC particles and superhard spherical particles of synthetic metal–diamond composite provided with tungsten coating. The surface layer was deposited on a sheet made of low-alloy structural steel grade AISI 4715. The layer is intended for surfaces of inserts of drilling tools used in the extraction industry. The results showed the lack of the thermal and structural decomposition of the hard layer reinforcing the matrix during the cladding process, its very high resistance to metal-mineral abrasive wear and its resistance to moderate impact loads. The abrasive wear resistance of the deposited layer with particles of TiC and synthetic metal–diamond composite was about than 140 times higher than the abrasive wear resistance of abrasion resistant heat-treated steel having a nominal hardness of 400 HBW. The use of diamond as a metal matrix reinforcement in order to increase the abrasive resistance of the PPTAW overlay layer is a new and innovative area of inquiry. There is no information related to tests concerning metal matrix surface layers reinforced with synthetic metal–diamond composite and obtained using PPTAW method.
Keywords:PPTAW, cladding, deposition, abrasion, impact load, titanium carbide, synthetic metal–  diamond composite
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号