含氟酪蛋白磷酸肽—磷酸钙复合物对酸蚀牙釉质显微硬度的影响

目的研究含氟酪蛋白磷酸肽-磷酸钙复合物(CPP-ACP)在体外对酸蚀牛牙釉质显微硬度的影响。方法选择新鲜拔除的牛下切牙60个,制成60个5mm×5mm正方形釉质开窗区,其余部分由抗酸指甲油涂抹封闭,将釉质块样本完全随机分为4组,每组15个,分别进行4种不同处理(A组为阴性对照组;B组为阳性对照组,使用碳酸饮料酸蚀处理;C组为碳酸饮料酸蚀后使用CPP-ACP进行再矿化;D组为酸蚀后使用含氟CPP-ACP(氟浓度为900ppm)再矿化。使用显微硬度仪测定样本显微硬度,比较各组显微硬度的差别。结果 D组显微硬度较C组高,C组及D组显微硬度均高于B组但低于A组,各组间的差异具有统计学意义(P0.01)。结论含氟酪蛋白磷酸肽-磷酸钙复合物可以提高酸蚀牙釉质的显微硬度。     

多乐氟、护牙素及含氟牙膏促进釉质再矿化的体外研究

目的:比较多乐氟、护牙素和含氟牙膏促进脱矿釉质再矿化的效果。方法:将40个牛牙釉质块人工龋试样随机分为4组(n=10),A组(对照组)置于人工唾液中浸泡12 d;B组(多乐氟组)釉质表面涂覆多乐氟涂膜,12 h后去除涂膜,置于人工唾液中浸泡12 d;C组(护牙素组)釉质表面涂覆护牙素1 min后,置于人工唾液中浸泡12 d;D组(含氟牙膏组)分别于每天早、晚将样本浸泡于含氟牙膏浆3 min,其余时间浸泡于人工唾液中,共12 d。脱矿前及处理前后,用硬度计测定各组釉质表面的显微硬度,计算其表面硬度恢复率(SMHR%);SEM观察表面结构。结果:SEM观察发现,B、C、D组再矿化处理前后釉质表面有新形成的羟基磷灰石晶体沉积。A、B、C、D组的SMHR(%)分别为20.43±5.91、60.55±14.05、67.69±11.74、52.82±3.61;除B、C组无统计学差异(P>0.05),其他各组间两两相比均有统计学差异(P<0.05)。结论:含氟材料或亚稳定无定形磷酸钙材料(护牙素)均可显著促进脱矿釉质的再矿化,护牙素的效果最好。     

含氟牙膏对釉质脱矿影响的体外研究

目的：探讨国内常见市售含氟牙膏对完整釉质及脱矿釉质的作用。方法：测定市售的3种含氟牙膏的氟含量,并选取釉质完好的牛牙及人工龋脱矿的牛牙,用3种含氟牙膏和不含氟牙膏刷洗釉面后,乳酸处理1min,用原子吸收光谱仪测定溶出的钙量。结果：含氟牙膏组和不含氟牙膏组均能使完整奥质的溶钙量明显降低,与空白对照组相比差异有显著性;含氟牙膏组和不含氟牙膏组均能使人工龋脱矿釉质的溶钙量明显下降,并且两组间有显著性差异。结论：含氟牙膏可以增强完整釉质及人工龋脱矿釉质的抗酸溶钙能力,且效果与其氟浓度相关,氟浓度为52.63umol/L时可显著提高牙齿抗酸力。     

精氨酸牙膏对釉质早期龋再矿化作用的研究

目的 研究精氨酸牙膏对人牙釉质早期龋的再矿化效果。方法 制备人牙釉质龋标本,随机分为 3组：空白组（去离子水处理）,对照组（普通市售含氟牙膏处理,含质量分数 0.14%单氟磷酸钠）,实验组（精氨酸牙膏处理,含质量分数 0.14%单氟磷酸钠和 8%精氨酸）。经体外 pH循环 10 d,测量 pH循环前后各组样本的表面显微硬度,计算其差值;并通过偏光显微镜观察各组样本再矿化前后的形态学改变。pH循环结束后,脱矿处理 2h,测量其表面显微硬度,计算与 pH循环前的差值,评估再矿化处理对釉质抗酸能力的影响。采用酸蚀法测定各组的氟摄入量。结果 与对照组和空白组比较,实验组釉质表面的显微硬度、抗酸能力,以及氟摄入量均明显升高。偏光显微镜下观察,实验组病损深度明显变浅,且有表层下再矿化条带,而空白组与对照组病损无明显变化。结论 精氨酸牙膏能有效促进人牙釉质龋表层及表层下再矿化,在早期龋的防治领域具有较大的临床应用前景。     

磷硅酸钠钙对乳牙釉质再矿化作用的研究

目的：研究生物活性材料磷硅酸钠钙（CSP）对人工脱矿的乳牙釉质表面再矿化的作用。方法：收集30颗健康离体乳磨牙,将每颗牙冠沿近远中径和颊舌径分成4个釉质块,每个釉质块随机分为4组（n ＝30）。样本经35％磷酸酸蚀2 min后分别进行如下处理：空白对照（A 组）、0．14％氟化物处理（B 组）、CSP 处理（C 组）、氟化物＋CSP 处理（D 组）,每天循环处理2次。在10、30 d 时扫描电镜观察釉质表面形态并测定釉质表面显微硬度值（SMH）。结果：扫描电镜观察显示,10 d 时A 组表面呈脱矿的蜂窝状表现,B、C 组脱矿不明显,D 组可见明显的矿化物沉积。30 d 时 A 组可见明显釉质脱矿和釉柱溶解表现,B、C 和 D 组可见程度不等的再矿化。10 d 时 D 组的 SMH 值高于 A 组（P ＜0．05）,30 d 时 B、C、D 组 SMH 值均高于 A组（P ＜0．05）,D 组 SMH 值显著高于 B 和 C 组（P ＜0．05）。结论：CSP 和氟化物具有促进乳牙釉质再矿化的作用,CSP 和氟化物联合应用优于二者的单独应用。     

含氟酪蛋白磷酸肽-磷酸钙复合物对牙齿耐磨性的影响

目的研究含氟酪蛋白磷酸肽-磷酸钙复合物(CPP-ACP)在体外对酸蚀牛牙釉质耐磨性的影响。方法选择新鲜拔除的牛下切牙40个,每个牙冠唇面形成5mm×5mm的釉质窗,其余部分由抗酸指甲油涂抹封闭,将釉质块样本完全随机分为4组,每组10个,A组为阴性对照组;B组使用20%磷酸溶液酸蚀;C组经酸蚀后使用CPP-ACP再矿化处理;D组则经酸蚀后使用含氟CPP-ACP再矿化。每组分别采取以上不同处理方式后进入磨损循环,每个循环磨损3600次,共4个循环,总计磨损次数14400次。使用三维白光干涉表面形貌仪,测定每个样本磨损深度,比较各组磨损量的差别。结果 D组磨损量小于C组,C组及D组磨损量均低于A组和B组,各组间的差异具有统计学意义(P<0.01)。结论含氟酪蛋白磷酸肽-磷酸钙复合物可以提高酸蚀牙釉质的耐磨性。     

局部应用氟化物对酸蚀釉质作用的体外研究

目的：评价局部应用氟化物对酸蚀釉质的作用。方法：收集正畸减数拔除的年轻前磨牙40个，制备釉质样本，随机分成对照组，lg／L氟化钠液组，含氟牙膏组，联合应用组。用饮料对釉质间断性酸蚀1周，然后使用不同的氟化物处理酸蚀的釉质表面1周。采用显微硬度计检测釉质表面显微硬度值（SMH），原子力显微镜（AFM）、扫描电镜（SEM）观察牙体硬组织表面的结构。结果：饮料浸泡后釉质的SMH明显下降。与对照组相比，氟化物处理后各氟化物处理组的釉质SMH均有明显增加（P＜0．001）。AFM和SEM均可见酸蚀后的釉质表面呈典型的蜂窝状结构，SEM观察显示氟化物处理后，各组釉质表面均有一定沉积物。结论：饮料会导致体外釉质表面的脱矿，氟化物能够促进体外酸蚀釉质的再矿化。     

几种牙膏对早期釉质龋再矿化效果的体外研究

目的比较几种不同成分牙膏促进脱矿釉质再矿化的作用。方法选择新鲜拔除的牛下颌切牙制备成釉质块,形成早期人工龋。随机分为5组,各组依次为精氨酸牙膏组、氟离子浓度为0．11％牙膏组、酪磷酸蛋白牙膏组、氟化钠组（阳性对照组）、去离子水组（阴性对照组）。分别进行pH循环后,试验样本依次用显微硬度仪、偏光显微镜、激光共聚焦镜对再矿化程度进行检测。运用SPSS17．0软件,对检测结果进行单因素方差分析及配对t检验分析。结果显微硬度检测结果显示：精氨酸牙膏组、氟化钠组及酪磷酸蛋白牙膏组比0．11％含氟牙膏组的显微硬度恢复的百分比高（P〈0．05）。偏振光显微镜检测结果显示：酪磷酸蛋白牙膏组脱矿深度恢复的百分比高于0．11％含氟牙膏组,而较精氨酸牙膏组、氟化钠组低。激光共聚焦显微镜检测结果显示：酪磷酸蛋白牙膏组与0．11％含氟牙膏组荧光渗透减少量较精氨酸牙膏组及氟化钠组少。结论在本实验条件下,精氨酸牙膏、酪磷酸蛋白牙膏都能一定程度的促进早期釉质龋的再矿化作用,其中以精氨酸牙膏作用最强。     

3种无氟儿童牙膏对乳牙早期釉质龋再矿化作用的体外研究

目的 探究3种市售无氟儿童牙膏即生物活性玻璃儿童牙膏、双黄连儿童牙膏、木糖醇儿童牙膏对乳牙早期釉质龋的再矿化作用。方法 应用离体乳牙制备人工龋模型50例,随机分为5组：活性玻璃组、双黄连组、木糖醇组、NaF组、去离子水组。在体外进行pH循环后,测量各组乳牙的表面显微硬度,并结合偏光显微镜对乳牙的釉质龋损进行形态学观察。结果 活性玻璃组能显著提高乳牙早期釉质龋再矿化后的表面显微硬度（P<0.05）,但其提高的程度不如NaF组（P<0.05）,双黄连组、木糖醇组和去离子水组未能提高再矿化后的显微硬度（P<0.05）。偏光显微镜下,活性玻璃组与NaF组再矿化后乳牙表层釉质的脱矿深度明显变浅。结论 生物活性玻璃儿童牙膏能有效促进乳牙早期釉质龋再矿化,但其再矿化能力小于含氟牙膏,双黄连儿童牙膏和木糖醇儿童牙膏在本次实验中未能体现出再矿化能力。     

渗透树脂和多乐氟处理脱矿釉质后的抗酸性和再矿化能力比较

目的 通过观察渗透树脂与多乐氟处理脱矿釉质后其牙齿表面显微硬度和粗糙度的变化,对两种材料在釉质抗酸性和再矿化能力方面的性能进行评估。方法 选择正畸拔除的健康前磨牙48颗,建立釉质表面脱矿模型,按照不同材料的处理条件随机分为4组,A（不做任何处理）,B（渗透树脂）,C（多乐氟）;D（渗透树脂+多乐氟）,分别经脱矿液组（1d,3d）和再矿化液组（7d）浸泡处理后,测定牙齿表面的显微硬度和粗糙度。结果 不同材料处理脱矿模型后即刻,B、D组的显微硬度、粗糙度均明显增加（P<0.001）,B、D组之间无统计学差异（P>0.05）;而C组显微硬度、粗糙度均明显减低（P<0.001）。继续脱矿（1d,3d）后,各组的显微硬度均下降,而粗糙度却明显增加;再矿化7d后,A、C组显微硬度和粗糙度均显著增加（P<0.001）,B、D组增加不明显（P>0.05）。结论 渗透树脂具有良好的改善牙齿表面硬度的作用,但在抗酸性和促进牙齿再矿化方面无明显优势。而氟化物则在抗酸性和促进再矿化方面有突出表现。当两者联合应用时,可以起到较好协同作用,明显增强牙齿的硬度、抗酸性和再矿化性能。     

含氟充填材料释氟吸氟和再释氟的研究

目的 为了研究含氟充填材料能否长期稳定释放氟而发挥抗龋效能,本文观察了玻璃离子水门汀和含氟复合树脂在用含氟牙膏处理前后两个时期的释氟情况。方法 第一阶段,将玻璃离子水门汀和含氟复合树脂各６个标本,分别浸泡于去离子水中,测定其在不同时间氟的放量;第二阶段。用含氟牙膏处理各标本后,再测定其在不同时间氟的释放量。结果 当这两允填材料释氟水平降低后,用含氟牙膏处理,琪 释放量明显回升     

使用不同氟制剂后菌斑氟浓度的动态变化

目的 通过测定志愿者使用不同氟制剂后菌斑氟浓度，观察Fluor Protector，Bilfluoride，0．2％NaF漱口水，1．23％APF泡沫四种氟制剂使用后，氟在口腔菌斑中的动态变化，了解不同剂型的氟制剂在口腔中的释放情况，为临床选择有效的氟制剂提供实验依据。方法 选择56名志愿者，用离子选择性氟电极测定使用四种氟制剂后1、3、7天菌斑氟浓度，并与基线水平相比较。结果 无论是使用哪种类型的氟制剂，菌斑氟浓度都显著提高，0．2％NaF漱口水，1．23％APF泡沫只在第一天时高于基线，Fluor Protector和Bilfluoride在第一天、第三天都高于基线，Bilfluoride在第七天时仍然高于基线。结论 作为缓释制剂的双氟漆和氟保护漆延长了氟在菌斑中的停留时间，使氟的清除速度降低，这有利于防龋作用的发挥。     

两种氟防龋涂膜材料的释氟性及抗脱矿能力的研究

目的 比较两种氟防龋涂膜材料的释氟性及其提高釉质的抗脱矿能力。方法 将两种市售的FQ氟涂膜和多乐氟涂膜分别涂覆于20 mm×20 mm的方形聚酯塑料载片表面，每个聚酯塑料载片浸于20mL去离子水中，分别于浸水后3 h、6 h、12 h及24 h测定氟离子浓度，计算释氟率；扫描电镜观察氟涂膜表面形貌。制备5 mm×5 mm×3 mm的牛切牙釉质块，自凝树脂包埋后表面打磨抛光，测定初始表面显微硬度(SMH0)，在釉质块表面涂覆氟涂膜，浸水12 h，然后去除氟涂膜，对釉质块进行pH循环脱矿，7天后测定釉质块表面显微硬度(SMH1)，计算脱矿后釉质表面显微硬度下降率，设立阳性对照和阴性对照。结果 FQ氟涂膜和多乐氟3 h、6 h、12 h、24 h释氟率分别为(2.73±0.27)%、(3.19±0.05)%、(3.58±0.19)%、(3.63±0.08)%和(0.16±0.02)%、(0.34±0.03)%、(0.43±0.03)%、(0.48±0.03)%；经过pH循环脱矿后，应用过氟涂膜的釉质表面显微硬度下降率显著低于未用氟涂膜的釉质（85.95±3.50）%,FQ氟涂膜和多乐氟的硬度...     

使用不同氟制剂后唾液游离氟浓度的变化

目的　观测志愿者使用不同氟制剂后唾液游离氟浓度的动态变化 ,探讨各种氟制剂对唾液游离氟浓度的影响 ,为临床选择有效的氟制剂提供依据。方法　 4 0名志愿者 ,采用离子选择性氟电极测定使用氟保护漆(FluorProtector)、双氟漆、0 .2 %NaF漱口水、1.2 3%APF泡沫 4种氟制剂前后 0 .2 5、0 .5、1、2、6、2 4小时唾液游离氟的浓度 ,并与基线水平相比较。结果　各种氟制剂使用后 ,唾液氟浓度均迅速提高 ,以后降低。FluorProtector和0 .2 %NaF漱口水 2小时 ,1.2 3%APF泡沫和双氟漆 6小时唾液氟浓度回到基线水平 (P >0 .0 5 ) ;双氟漆在 2 4小时又显著高于基线 (P <0 .0 5 ) ,在唾液中停留的时间最长 ;FluorProtector 6小时氟浓度升高 ,与其它各组水平相当。结论　双氟漆和氟保护漆延长了氟在唾液中的停留时间 ,使唾液氟的清除速度降低 ,有利于防龋作用的发挥。     

Enamel fluoride uptake of a novel water-based fluoride varnish

Aim of the in situ-study was to evaluate fluoride retention in sound and demineralised enamel after application of a novel water-based fluoride (0.12% F) varnish Mirafluorid (Hager and Werken, Germany) compared to the resin-based varnish (2.26% F) Duraphat (Colgate, USA). Each five enamel specimens were prepared from 60 bovine incisors. In 150 of these specimens, incipient lesions were produced with acidic hydroxyethylcellulose (pH 4.8; 72 h), 150 specimens were not demineralised. The samples were equally (n=100) allotted to three groups (A: Mirafluord, B: Duraphat, and C: control). Each 80 specimens (40 demineralised and 40 sound) were varnished with either Mirafluorid or Duraphat or remained unfluoridated (controls). The other specimens were used for measuring base-line fluoride content of the respective tooth. Each six specimens (three demineralised and three sound) were fixed in intraoral appliances worn for 5 days by 10 volunteers in three series (A-C). During the experiment, the samples were brushed twice daily with fluoridated toothpaste. KOH-soluble and structurally bound fluoride (0-30 and 31-60 microm depth) was determined immediately, 1, 3 and 5 days after fluoridation. Fluoride uptake was calculated as compared to base-line content and statistically analysed. Immediately after fluoridation, uptake of KOH-soluble and structurally bound fluoride was similar for Mirafluorid and Duraphat in both demineralised and sound enamel. However, at day 1, 3 and 5 statistically significantly higher amounts of KOH-soluble and structurally bound fluoride were found in the samples treated with Duraphat. For Mirafluorid only the uptake for KOH-soluble fluoride and structurally bound fluoride in the first enamel layer (0-30 microm) of the demineralised samples was significantly higher compared to the controls (C). It is concluded that the novel fluoride varnish Mirafluorid deposits less KOH-soluble and structurally bound fluoride on both demineralised and sound enamel compared to Duraphat under in situ-conditions.     

牙膏氟含量对学龄前儿童氟摄入影响的研究

目的 通过检测使用3种不同氟含量含氟牙膏后24小时尿氟排泄的变化。观察含氟牙膏氟含量及年龄对3个年龄组学龄前儿童氟化物摄入水平的影响，推测学龄前儿童使用含氟牙膏较为安全的氟含量，方法 采用离子选择性氟电极测定使用不同氟含量含氟牙膏后24小时尿氟排泄量，以使用含氟牙膏前尿氟排泄量作为自身对照，结果 含氟牙膏氟含量及年龄对学龄前儿童24小时尿氟排泄有显著影响，结论 学龄前儿童刷牙时因误咽部分含氟牙膏引起机体氟化物摄入水平的变化，含氟牙膏氟含量等于或超过1000μg/g时，可致每日总摄氟量超过产生氟牙症的域值，因此对于6岁以下的儿童要选用低氟含量牙膏，使用500μg/g含氟牙膏较为安全。     

矿化液、低浓度氟化物溶液和氟泡沫再矿化作用比较

目的本研究对矿化液、低浓度氟化物溶液和氟泡沫再矿化作用进行了比较,从而寻找出一种再矿化效果较好的制剂.方法采用实验室研究,分别用三种制剂处理表面脱矿釉质.应用显微硬度仪检测处理前后的釉质表面硬度值,通过对比前后硬度差异反映脱矿釉质的再矿化的情况.结果矿化液处理后的釉质表面硬度明显增加,有显著性统计学意义.低浓度氟化物溶液和氟泡沫处理后釉质的表面硬度无明显改变.结论在体外,矿化液的再矿化效果优于低浓度氟化物溶液和氟泡沫.它可用于治疗正畸过程中早期釉质脱矿.     

含氟牙膏刷牙后菌斑和唾液中氟离子浓度的变化

目的 :测定正常人使用含氟牙膏刷牙后 ,菌斑及唾液中氟离子浓度 ,并探讨其对龋病预防的意义。方法 :选择 16名自愿者 ,用离子选择性氟电极测定含氟牙膏刷牙后 2小时菌斑及唾液中氟离子浓度 ,并与基线水平相比较。结果 :含氟牙膏刷牙后 2小时 ,牙菌斑及唾液中氟浓度分别为 5 1.5 5± 14.15 μg/g菌斑湿重和 13.36± 3.81μmol/L ,较基线水平有显著性提高 (P <0 .0 1)。结论 :用含氟牙膏刷牙后使菌斑和唾液达到并维持的氟浓度 ,尤其是菌斑中氟浓度 ,可有效地抑制菌斑细菌的糖酵解过程 ,从而起到预防龋病发生的作用     

Effects of periodic fluoride treatment on fluoride ion release from fresh orthodontic adhesives

Objective

Periodic fluoride treatment may contribute to the ability of fresh orthodontic adhesives to provide long-term F⁻ release. The effects of periodic fluoride treatment on the amount of F⁻ release from fresh orthodontic adhesives was investigated.

Methods

F⁻ release was measured from a nonfluoride-releasing composite, a fluoride-releasing composite, a polyacid-modified composite (compomer), and two resin-modified glass-ionomer cements (RMGICs) at 1, 2, and 5 days after one of the following treatments: 225 ppm F⁻ solution, 900 ppm F⁻ solution, acidulated phosphate fluoride gel (APF), fluoridated dentifrice, and deionised water (control). F⁻ release was measured in a 5-day cycle, which was repeated 9 consecutive times. The amount of F⁻ release for each group was analysed using the repeated measures analysis of variance. Statistical significance was set at a level of α = 0.05.

Results

Periodic fluoride treatment temporarily increased F⁻ release in fresh fluoride-releasing orthodontic adhesives, but not in fresh nonfluoride-releasing composite. The order of effective fluoride-release was RMGICs > compomer > fluoride-releasing composite > nonfluoride-releasing composite. The application of APF or 900 ppm F⁻ solution was the most effective way to maintain F⁻ release from fresh orthodontic adhesives. However, the amount of F⁻ release gradually decreased with increasing specimen age.

Conclusion

Given the difficulty of routine use of APF at home, the results of this study show that a combination of RMGICs and high-dose fluoride mouth rinse is the most effective protocol to maintain F⁻ release from fresh orthodontic adhesives.

Clinical significance

Most studies have investigated fluoride-uptake abilities using aged materials in which fluoride had been lost for at least 1 month. This study has found that periodic fluoride treatment altered the conventional F⁻ release pattern of fresh fluoride-releasing materials and type of fluoride-containing medium plays a more critical role in fluoride recharging of the materials than fluoride concentration. This study will help clinicians to find the most effective fluoride treatment protocol of fresh materials.     

Effect of three fluoride agents on remineralization and fluoride uptake on enamel lesion

This study is to compare the fluoride uptake of three fluoride agents and the effect of remineralization on artificial enamel lesions. Eight human third molars were all divided into four slabs. The slabs were randomly assigned to the following four groups: group A (9,040 ppm F, APF gel), group B (968 ppm F, SnF₂ home gel), group C (22,600 ppm F, fluoride varnish, FV) and a control group. After 72-hour demineralizing and 10-day pH-cycling period with the application of corresponding fluorides. The distribution of fluoride and mineral change was analyzed with EPMA and CMR respectively. There was a significant increase in the amount of F uptake after the application of the three fluoride agents compared to the control group. Group A showed an extremely greater F uptake compared to group C and B. The amount of F uptake from group C was greater than that of group B. The three tested groups showed signs of significantly greater amounts of remineralization as compared to the control group. Remineralization of group C was detected to be the greatest, followed by group A and group B, but there was no significant difference in them under statistical analysis. It can be concluded that all of the tested agents were effective in regaining mineral loss. FV may be recommended as a professional topical fluoride. It is as effective, if not more so, as traditionally used APF gel. Also 0.4% SnF₂ home gel is an efficient self-applied topical fluoride for daily use.